Loxeal 31- 10
Chemical Resistance Chemical Resistance: Fluid Resistance: Well resistant to water, Well resistant to gasoline, Chemical resistance Application Type Bond 1 Part or 2 Part 2-Part Material Form Liquid Substrate Rigid PVC, ABS, Polyester, Some plastics, Wood, Concrete, Glass, Ferrite, Metals, Marble, Steel, Ceramic Manufacturer Loxeal Cure Method 2-Part Cure, Room temperature Application Temperature (°F) <59 Gap Fill (in) 0.004 to 0.079 Cure Temperature (°C) 25 Cure Time (min) 720 to 1,440 Color Transparent, Amber, After mixing Oil Resistance Well resistant to oils High Temperature Resistance (°C) 80 Low Temperature Resistance (°C) -40
Technical Data for Loxeal 31- 10
- Chemical Resistance : Fluid Resistance : Water Resistance - Well resistant to water
- Chemical Resistance - Well resistant to gasoline
- Adhesive - Bond
1 Part or 2 Part
- Other - Structural adhesive, Multipurpose
- Room Temperature / Air Dry - Room temperature
- 2-Part Cure
- Amber - Amber, After mixing
- Clear / Transparent - Transparent
Application Temperature (°F) <59 Gap Fill (in) 0.004 to 0.079 Cure Temperature (°C) 25 Test Method Cure Time (min) 720 to 1,440 Test Method Work / Pot Time (min) 90 to 150 Test Method Mix Ratio 1:1 (by volume)
Peel Strength (piw) 10 - 25 (N/25mm) Test Method Shear Strength (psi) Test Method
Oil Resistance Well resistant to oils Environmental Resistance Environmental resistance High Temperature Resistance (°C) 80 Low Temperature Resistance (°C) -40
Shelf Life Details 1 year in original unopened packaging at +5°/+25°C Shelf Life Temperature (°F) 41 to 77 Shelf Life (mon) 12
Not Good For
Don't Use With Rubber, Soft materials, Polyethylene, Polypropylene, PTFE
Best Practices for Loxeal 31- 10
For best results we recommend to scratch the surfaces with a tool and then to degrease and clean with Loxeal Cleaner 10 or Acetone and let dry for a few seconds.
Apply product at temperature higher than +15°C.
Assembly: Parts to be bonded shall be assembled immediately after product application and kept close until full polymerization without providing any mechanical stress.
The resin and the hardener need to be mechanically mixed before use in the ratio of weight and/or volume in compliance with technical specifications until a homogeneous colour is reached. Products are available in dual cartridges with proper static mixers (separately provided) allowing a direct and correct product application on the substrates to bond, completely discarding the first 3/5 cm of the extruded product. Avoid excess of product blend because heating produced by chemical reaction may cause risk and loss of product.
Excess of product can be removed with Acetone or any other solvent based cleaner compatible with the substrates to bond. Application tools and dosing systems shall be cleaned before the product is hardened.
Cured product can be removed only mechanically.
Comparable Materials for Loxeal 31- 10
Spec Engine® Results
Closest Results from this Manufacturer
Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of MaterialsRead Article
Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:Read Article
Work / Pot Time Test Methods
|Work / Pot Time||Test Method||Temperature|
|90 to 150 min||Usable/Pot life, Curing, Time detected using 2 g of Part A +Part B mix||25°C|
Cure Time Test Methods
|Cure Time||Test Method|
|720 to 1,440 min||Functional cure time|
Cure Temperature Test Methods
|Cure Temperature||Cure Time Test Method|
|25°C||Functional cure time|
Shear Strength Test Methods
|Shear Strength||Cure Temperature||Substrate||Test Method|
Peel Strength Test Methods
|Peel Strength||Cure Temperature||Test Method|
|10 - 25 (N/25mm)||25°C||ISO 4578, Curing|