3M 1099L Datasheet 3M 1099L

CONTACT REP
Information provided by Gluespec

  • Description for 3M 1099L

    A low viscosity grade for spray application. Fast drying, provides strong, flexible bonds.

    *See Terms of Use Below

    Chemical Resistance Weathering, Chemical Resistance: Solvent, Chemical Resistance: Fluid Resistance: Excellent water resistance, Chemical Resistance: Resists Plasticizer, Fuels, Oil
    Application Type Bond
    1 Part or 2 Part 1-Part
    Material Form Liquid
    Substrate Aluminum, Fabric, Plastic, Vinyls, Foams
    Manufacturer 3M
    Chemistry Acetone, Methyl ethyl ketone (MEK), Nitrile Rubber
    Cure Method Solvent, Heat
    Application Temperature (°F) 64
    Cure Temperature (°C) 93, 116, 138, 160, 182, 204
    Cure Time (min) Fast, 120, 40, 12, 8, 5.00, 2.00
    Viscosity (cPs) Low, 200 to 325
    Color Light Tan
    High Temperature Resistance (°C) 121, 82
    Low Temperature Resistance (°C) -55, 24
    Density (g/cm³) 7.0 to 7.4 (weight (lbs/gal))

  • Technical Data for 3M 1099L

    *See Terms of Use Below

    Overview
    • Chemical Resistance
      • Chemical Resistance : Fluid Resistance : Water Resistance - Excellent water resistance
      • Chemical Resistance - Fuels, Oil, Weathering
      • Chemical Resistance : Relative Solvent Resistance - Solvent
      • Chemical Resistance : Plasticizer Resistance - Resists Plasticizer
    • Application Type
    • 1 Part or 2 Part
      • 1-Part
    • Material Form
      • Liquid
    • Substrate
    • Chemistry
      • Other - Acetone, Methyl ethyl ketone (MEK), Nitrile Rubber
    • Application Method
      • Dispenser - Lamination equipment
      • Spray - Sprayable
    • Cure Method
      • Solvent
      • Heat
    • Color
      • Brown - Light Tan
    Specifications
    Cure Specs
    Application Temperature (°F) 64
    Cure Temperature (°C) 93, 116, 138, 160, 182, 204
    Cure Time (min) Fast, 120, 40, 12, 8, 5.00, 2.00
    Viscosity (cPs) Low, 200 to 325 Test Method
    Bond Strength
    Peel Strength (piw) 16.5 (lbs./in. width), 26 (lbs./in. width), 23.5 (lbs./in. width), 27.5 (lbs./in. width), 31 (lbs./in. width), 30 (lbs./in. width), 17.5 (lbs./in. width), 7 (lbs./in. width), 3.5 (lbs./in. width) Test Method
    Shear Strength (psi) 2,989, 3,409, 1,306, 897, 643, 607, 467 Test Method
    Material Resistance
    High Temperature Resistance (°C) 121, 82
    Low Temperature Resistance (°C) -55, 24
    Conductivity
    Dissipation Factor 99.00000
    Hardness
    Flexibility Flexible
    Other Properties
    Flash Point (°F) -0.4 Test Method
    % Solids (%) 22 to 26 Test Method
    Density (g/cm³) 7.0 to 7.4 (weight (lbs/gal))
    Business Information
    Shelf Life Details Store product at 60-80°F (16-27°C) for maximum storage life. Higher temperatures can reduce normal storage life. Lower temperatures can cause increased viscosity of a temporary nature. Rotate stock on a “first in-first out” basis.;When stored at the recommended conditions in the original, unopened container this product has a shelf life of 15 months from date of shipment.
    Shelf Life Temperature (°F) 61 to 81
    Shelf Life (mon) 15
    Not Good For
    Don't Use With Polyolefin plastic

  • Best Practices for 3M 1099L

    *See Terms of Use Below

    1. Surface Preparation

      Remove all dust, dirt, oil, grease, wax, loose paint, etc. Wiping with methyl ethyl ketone (MEK)* or 3M™ Citrus Base Cleaner* will aid in preparing the surface for bonding.

      *Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow manufacturer’s precautions and directions for use.

    2. Application

      For best results, the temperature of the adhesive and surfaces should be at least 65°F (18°C).

      Stir well before using.

      Porous Surface(s): Brush, flow or spray a thin, even coat of adhesive to one or both surfaces. Coating both surfaces is preferred since it gives greater strength and permits longer open time before bonding. Very absorbent materials may require more than one coat. Bond while adhesive is still wet or aggressively tacky. Join surfaces with firm pressure.

      Non-Porous Surface(s): Brush, flow or spray a thin, even coat of adhesive to both surfaces. Allow adhesive to dry until tacky. Join surfaces with firm pressure.

    3. Curing

      Drying time depends on temperature humidity, air movement, and porosity of the materials bonded. Greater immediate strength may be obtained by heat or solvent reactivation.

      3M™ Scotch-Weld™ Nitrile High Performance Plastic Adhesive 1099 and 1099-L may be heat cured to obtain superior properties. Cure assembled parts at time and temperature listed using 100 psi pressure on the bond line.

    4. Clean-Up

      Excess adhesive may be removed with methyl ethyl ketone (MEK)* or acetone,* preferably while adhesive is still wet.

      *Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow manufacturer’s precautions and directions for use.

  • Comparable Materials for 3M 1099L

    *See Terms of Use Below

    Spec Engine® Results

  Download Technical Data Sheet   Save This Material   Compare View Saved Items

Popular Articles

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Lightweighting drives automotive adhesives demand

Read Article

Testing the effectiveness of surface treatments

Read Article

6 objects held together by adhesives you probably can't live without

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for 3M 1099L

All 3M Materials
View Now

Gluespec Poll

Which answer best describes a project you are currently working on?
Viscosity Test Methods
Viscosity Test Method Temperature
Low
200 to 325 cPs Brookfield RVF @ 80°F 27°C #2 sp @ 20 rpm 27°C
Peel Strength Test Methods
Peel Strength Type Cure Time Cure Temperature Substrate Test Temperature
16.5 (lbs./in. width) 180° Peel strength 1,440 min 24°C Canvas-Steel 24°C
26 (lbs./in. width) 180° Peel strength 4,320 min 24°C Canvas-Steel 24°C
23.5 (lbs./in. width) 180° Peel strength 7,200 min 24°C Canvas-Steel 24°C
27.5 (lbs./in. width) 180° Peel strength 10,080 min 24°C Canvas-Steel 24°C
31 (lbs./in. width) 180° Peel strength 20,160 min 24°C Canvas-Steel 24°C
30 (lbs./in. width) 180° Peel strength 30,240 min 24°C Canvas-Steel 24°C
17.5 (lbs./in. width) 180° Peel strength 30,240 min 24°C Canvas-Steel -34°C
7 (lbs./in. width) 180° Peel strength 30,240 min 24°C Canvas-Steel 66°C
3.5 (lbs./in. width) 180° Peel strength 30,240 min 24°C Canvas-Steel 82°C
Shear Strength Test Methods
Shear Strength Type Substrate Test Temperature Test Method
2,989 psi Overlap shear strength Alum./Alum. -55°C Bonds heat cured @ 300°F (177°C) for 30 minutes with 100 psi pressure on the bondline.
3,409 psi Overlap shear strength Alum./Alum. -34°C Bonds heat cured @ 300°F (177°C) for 30 minutes with 100 psi pressure on the bondline.
1,306 psi Overlap shear strength Alum./Alum. 24°C Bonds heat cured @ 300°F (177°C) for 30 minutes with 100 psi pressure on the bondline.
897 psi Overlap shear strength Alum./Alum. 65°C Bonds heat cured @ 300°F (177°C) for 30 minutes with 100 psi pressure on the bondline.
643 psi Overlap shear strength Alum./Alum. 82°C Bonds heat cured @ 300°F (177°C) for 30 minutes with 100 psi pressure on the bondline.
607 psi Overlap shear strength Alum./Alum. 93°C Bonds heat cured @ 300°F (177°C) for 30 minutes with 100 psi pressure on the bondline.
467 psi Overlap shear strength Alum./Alum. 121°C Bonds heat cured @ 300°F (177°C) for 30 minutes with 100 psi pressure on the bondline.
Flash Point Test Methods
Flash Point Test Method
-18.0°C Closed up
% Solids Test Methods
% Solids Test Method
22 to 26 % By weight