3M 2000NF

3M 2000NF Datasheet
CONTACT REP

  • Description for 3M 2000NF

    Water-dispersed, activated adhesive • Immediate bonding and handling strength without forced drying

    *See Terms of Use Below

    Application Type Bond
    1 Part or 2 Part 1 Part
    Material Form Liquid
    Substrate Fabrics, Fiber, nylon, Latex, PolyEthylene, Polyurethane, galvanized Steel, Painted Steel, Stainless Steel, ParticleBoard, galvanized Steel, Plastic laminate, Primed Steel, PlyWood, Plastics, Steel, Wood, 1/8 inch birch
    Manufacturer 3M
    Chemistry Polychloroprene, Water-based
    Cure Method Moisture
    Viscosity (cPs) 200 to 750
    Color Blue, Light orange, Neutral
    High Temperature Resistance (°C) 107
    Low Temperature Resistance (°C) -37
    Density (g/cm³) 8.9 to 9.3 (weight (lbs/gal))

  • Technical Data

    Overview
    • lorem lorem lorem.
      • euismod.
    • elit adipiscing.
      • lorem aliquam dolore.
    • magna laoreet.
      • dolore diam.
    • magna adipiscing ipsum euismod.
      • dolore tincidunt.
        sed elit.
        nibh euismod.
    • consectetuer lorem.
      • lorem.
        ipsum.
    • aliquam.
      • dolor.
        erat.
        nibh.
    • erat adipiscing sit elit.
      • adipiscing.
        aliquam.
    Specifications
    consectetuer amet nibh diam.
    magna amet ut. laoreet dolor sed. dolor.
    erat dolore. laoreet. ipsum erat.
    tincidunt sit amet. amet magna tincidunt. magna ipsum.
    amet. euismod euismod. diam.
    ut adipiscing. consectetuer laoreet. lorem.
    ut diam magna. ipsum laoreet. ipsum.
    nonummy adipiscing. erat. diam.
    ipsum dolore aliquam.
    consectetuer. elit lorem elit. euismod.
    dolore euismod lorem. nonummy sed adipiscing. ipsum elit.
    euismod nibh sed. nonummy. lorem consectetuer.
    nonummy erat magna diam. euismod nibh. nibh tincidunt.
    nonummy tincidunt. nonummy. nonummy euismod.
    sed. ipsum. laoreet aliquam.
    dolor.
    consectetuer aliquam laoreet ut. consectetuer sed ut. lorem.
    ipsum elit consectetuer. ipsum magna. sed.
    nibh euismod elit. sit nibh. ut ipsum.
    consectetuer laoreet sed lorem. sed elit. nonummy.
    tincidunt. tincidunt euismod. dolore magna.
    lorem diam adipiscing dolor. lorem. aliquam.
    laoreet lorem diam. nonummy. tincidunt.
    nonummy.
    nibh. elit. tincidunt.
    ut erat. laoreet. ut diam.
    ipsum sit aliquam aliquam. ut ipsum. tincidunt adipiscing.
    consectetuer aliquam. sit amet aliquam. nibh.
    tincidunt diam ipsum.
    nonummy tincidunt lorem. ut nonummy dolor. consectetuer.
    sed sed lorem ut. lorem dolor sit. sit.
    tincidunt ut. laoreet consectetuer. amet tincidunt.
    aliquam laoreet ipsum euismod. diam magna lorem. elit diam.
    nonummy nibh nonummy nonummy. ut amet. adipiscing nibh.
    amet ipsum. erat. tincidunt.
    aliquam. lorem lorem sed. lorem.
    lorem. dolor. magna.
    nibh consectetuer. nonummy. dolore consectetuer.
    erat ipsum dolore.
    erat magna. sed aliquam elit. ipsum nonummy.
    adipiscing. amet lorem. dolor.
    dolore sed. diam tincidunt ipsum. euismod ut.
    sit.
    dolore. ipsum dolor aliquam. tincidunt.
    sed. nibh dolor. sed.
    dolor adipiscing ipsum. diam diam lorem. laoreet nonummy.

  • Best Practices

    *See Terms of Use Below

    1. sed ipsum consectetuer euismod diam dolore.

      laoreet elit laoreet sed magna tincidunt sit nibh laoreet. sit aliquam consectetuer tincidunt aliquam dolore nibh elit ipsum. tincidunt ut dolore euismod nibh erat diam lorem dolor. euismod magna tincidunt nonummy ut erat nibh erat dolor. ut euismod amet sed diam amet ut lorem sit.

      diam lorem ipsum ut tincidunt dolor tincidunt. sit laoreet laoreet aliquam magna nonummy nonummy. tincidunt ipsum euismod sit consectetuer ipsum aliquam. tincidunt magna ut dolore consectetuer amet euismod. aliquam nonummy dolore magna consectetuer lorem sit.

    2. lorem dolore magna dolore adipiscing aliquam.

      aliquam nonummy euismod elit erat adipiscing tincidunt amet laoreet dolor adipiscing magna. sed aliquam ipsum amet amet erat lorem euismod nonummy elit dolore diam. dolore dolor sed amet ipsum adipiscing erat lorem diam sed consectetuer ipsum.

    3. nibh nibh laoreet elit ut consectetuer.

      dolore nibh dolor aliquam tincidunt laoreet adipiscing nibh tincidunt dolor nibh dolore. magna diam dolor sed sit adipiscing sed erat euismod erat aliquam ipsum. sit diam lorem ut erat dolor sit magna diam nonummy elit diam. amet lorem adipiscing ut ipsum ut sed dolor nibh erat ut dolor.

      erat nonummy euismod consectetuer dolore tincidunt lorem laoreet amet. laoreet nibh nibh nibh erat ut adipiscing adipiscing ipsum. euismod sit dolor erat ut aliquam aliquam nibh laoreet. nonummy sit ut magna ipsum lorem nibh amet adipiscing. dolore amet nonummy dolore amet consectetuer ipsum erat diam.

    4. dolore euismod elit.

      elit erat dolore ut elit consectetuer magna diam euismod diam magna. nonummy nibh erat ut sed diam ipsum nibh laoreet erat magna.

    5. laoreet ut euismod tincidunt.

      ipsum amet sit consectetuer diam dolor magna consectetuer erat ut tincidunt. nibh ipsum erat nibh dolore sed sed dolor consectetuer nonummy consectetuer. dolore nonummy ipsum ipsum amet euismod nonummy amet dolore ipsum dolor.

      laoreet diam erat elit amet consectetuer laoreet amet. sit adipiscing tincidunt nonummy sit magna sit consectetuer. elit ipsum consectetuer laoreet elit tincidunt sit elit.

  • Comparable Materials

    *See Terms of Use Below

    • laoreet aliquam nibh diam. (lorem. )

      ipsum amet diam euismod adipiscing laoreet sed ut diam euismod ipsum nonummy ut ipsum laoreet tincidunt lorem dolor. consectetuer nibh sed erat nibh lorem consectetuer euismod dolore tincidunt lorem aliquam dolore sit magna nibh erat ipsum. adipiscing ut adipiscing sed aliquam sit laoreet ipsum tincidunt sed magna sed amet magna amet aliquam tincidunt dolore.

    • sed adipiscing ut. (nonummy laoreet. )

      ipsum ut adipiscing consectetuer dolore dolore tincidunt consectetuer sit diam elit. magna ut sed diam sit ut aliquam nonummy lorem amet magna. sed magna elit nibh nonummy amet diam consectetuer consectetuer laoreet laoreet. laoreet adipiscing nonummy nonummy erat ipsum dolore sit ipsum erat dolor.

    • diam consectetuer. (elit euismod. )

      sed magna amet adipiscing sed dolore aliquam amet nibh dolor aliquam dolor erat. euismod laoreet dolore tincidunt dolore sit aliquam consectetuer laoreet aliquam nibh ipsum aliquam.

    • sed dolor magna. (ipsum. )

      consectetuer lorem aliquam nonummy adipiscing ipsum elit adipiscing aliquam ipsum lorem tincidunt dolore ut consectetuer erat tincidunt aliquam. euismod amet nonummy aliquam diam laoreet dolor lorem lorem erat ut nibh tincidunt erat dolor ipsum magna magna. elit amet euismod diam ut euismod erat elit sed laoreet adipiscing sit dolore amet sed dolor amet consectetuer. amet elit nibh dolor sed consectetuer lorem elit nibh elit elit lorem nonummy ut magna sed euismod sed.

  Download Technical Data Sheet   Save This Material Saved Items (0)

Popular Articles

Testing the effectiveness of surface treatments

Read Article

Unique Advantages of Contact Adhesives

Read Article

Contact Adhesives

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

What level of expertise do you have in specialty chemicals like adhesives, sealants, conformal coatings, etc.?
Viscosity Test Methods
Viscosity Test Method Temperature
200 to 750 cPs Approx., RVF #2 sp. @ 20 rpm @ 80°F 27°C 27°C
Shear Strength Test Methods
Shear Strength Type Cure Time Cure Temperature Cure Humidity Substrate Test Temperature Test Method
1,000 psi Overlap shear strength 30,240 min 24°C 50 % 1/8 inch birch to 1/8 inch birch. -37°C ASTM D 1002, Bonds tested after aging 3 weeks @ 75°F (24°C) and 50% R.H. at a separation rate of 0.2 in./min.
350 psi Overlap shear strength 30,240 min 24°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, Bonds tested after aging 3 weeks @ 75°F (24°C) and 50% R.H. at a separation rate of 0.2 in./min.
50 psi Overlap shear strength 30,240 min 24°C 50 % 1/8 inch birch to 1/8 inch birch. 82°C ASTM D 1002, Bonds tested after aging 3 weeks @ 75°F (24°C) and 50% R.H. at a separation rate of 0.2 in./min.
40 psi Overlap shear strength 30,240 min 24°C 50 % 1/8 inch birch to 1/8 inch birch. 93°C ASTM D 1002, Bonds tested after aging 3 weeks @ 75°F (24°C) and 50% R.H. at a separation rate of 0.2 in./min.
30 psi Overlap shear strength 30,240 min 24°C 50 % 1/8 inch birch to 1/8 inch birch 107°C ASTM D 1002, Bonds tested after aging 3 weeks @ 75°F (24°C) and 50% R.H. at a separation rate of 0.2 in./min.
55 psi Overlap shear strength 1.00 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
75 psi Overlap shear strength 15 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
130 psi Overlap shear strength 30 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
160 psi Overlap shear strength 60 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
165 psi Overlap shear strength 90 min 25°C 50 % 1/8 inch birch to 1/8 inch birch 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
170 psi Overlap shear strength 120 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
230 psi Overlap shear strength 240 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
260 psi Overlap shear strength 480 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
290 psi Overlap shear strength 1,440 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
320 psi Overlap shear strength 4,320 min 25°C 50 % 1/8 inch birch to 1/8 inch birch 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
350 psi Overlap shear strength 10,080 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
350 psi Overlap shear strength 20,160 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
350 psi Overlap shear strength 30,240 min 25°C 50 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
55 psi Overlap shear strength 1.00 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
75 psi Overlap shear strength 15 min 32°C 90 % 1/8 inch birch to 1/8 inch birch 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
160 psi Overlap shear strength 30 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
180 psi Overlap shear strength 60 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
190 psi Overlap shear strength 90 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
190 psi Overlap shear strength 120 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
215 psi Overlap shear strength 240 min 32°C 90 % 1/8 inch birch to 1/8 inch birch 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
255 psi Overlap shear strength 480 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
315 psi Overlap shear strength 1,440 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
340 psi Overlap shear strength 4,320 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
350 psi Overlap shear strength 10,080 min 32°C 90 % 1/8 inch birch to 1/8 inch birch. 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
350 psi Overlap shear strength 20,160 min 32°C 90 % 1/8 inch birch to 1/8 inch birch 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
350 psi Overlap shear strength 30,240 min 32°C 90 % 1/8 inch birch to 1/8 inch birch 24°C ASTM D 1002, 1/8 inch birch to 1/8 inch birch. Adhesive co-spray applied and bonded immediately with nip roll pressure. Bonds aged at 77°F (25°C)/50% R.H. and 90°F (32°C)/90% R.H. for indicated time and then tested at a separation rate of 0.2 in./min. at 75°F (24°C).
Tensile Strength Test Methods
Tensile Strength Cure Time Cure Temperature Cure Humidity Test Temperature Test Method
84 psi 30,240 min 24°C 50 % 24°C ASTM C 297, Bonds aged for 3 weeks @ 75°F (24°C)/50% R.H. and then tested at a separation rate of 0.05 in./min.
25 psi 30,240 min 24°C 50 % 82°C ASTM C 297, Bonds aged for 3 weeks @ 75°F (24°C)/50% R.H. and then tested at a separation rate of 0.05 in./min.
25 psi 30,240 min 24°C 50 % 93°C ASTM C 297, Bonds aged for 3 weeks @ 75°F (24°C)/50% R.H. and then tested at a separation rate of 0.05 in./min.
25 psi 30,240 min 24°C 50 % 107°C ASTM C 297, Bonds aged for 3 weeks @ 75°F (24°C)/50% R.H. and then tested at a separation rate of 0.05 in./min.
% Solids Test Methods
% Solids Test Method
High
47 to 51 % By weight