3M 2214 Hi-Temp New Formula Gray Datasheet 3M 2214 Hi-Temp New Formula Gray

CONTACT REP
Information provided by Gluespec

  • Description for 3M 2214 Hi-Temp New Formula Gray

    Version of 2214 with excellent performance under high temperature and high humidity • Resists hot ethylene glycol

    *See Terms of Use Below

    Chemical Resistance Ethyl Gasoline, Chemical Resistance: Fluid Resistance: Tap Water, Excellent, Hot ethylene glycol
    Application Type Bond
    1 Part or 2 Part 1-Part
    Material Form Paste
    Substrate Aluminum, Fiber Glass, Metal, Plastic, Polyester, Rubber, Cold rolled Steel, Phenolics, Etched Aluminum, Glass, Steel
    Manufacturer 3M
    Chemistry Epoxy, Epoxy: Modified Epoxy
    Cure Method Heat
    Cure Temperature (°C) 121, 149
    Cure Time (min) 60, 15
    Viscosity (cPs) >1,000,000
    Color Gray Brown, Gray
    Arc Resistance (sec) Arc
    Aging Resistance Aging resistance
    High Temperature Resistance (°C) 177, High
    Low Temperature Resistance (°C) -55
    Volume Resistivity (O) 9.4e14 (ohms/cm)
    Density (g/cm³) 13.8 (weight (lbs/gal))

  • Technical Data for 3M 2214 Hi-Temp New Formula Gray

    *See Terms of Use Below

    Overview
    • Chemical Resistance
      • Chemical Resistance : Fluid Resistance : Water Resistance - Tap Water
      • Chemical Resistance - Ethyl Gasoline, Excellent, Hot ethylene glycol
    • Application Type
    • 1 Part or 2 Part
      • 1-Part
    • Material Form
      • Paste
    • Substrate
    • Chemistry
    • Cure Method
      • Heat
    • Color
      • Brown - Gray Brown
      • Gray
    Specifications
    Cure Specs
    Cure Temperature (°C) 121, 149
    Cure Time (min) 60, 15
    Viscosity (cPs) >1,000,000 Test Method
    Thixotropic Thixotropic
    Bond Strength
    Structural/Load-Bearing Structural
    Peel Strength (piw) 2, 5 Test Method
    Shear Strength (psi) 2,800, 2,800, 2,800, 2,500, 2,000, 1,200, 2,000, 2,500, 2,000, 2,000, 2,000, 700 Test Method
    Material Resistance
    Arc Resistance (sec) Arc
    Aging Resistance Aging resistance
    Environmental Resistance Environmental resistance
    High Temperature Resistance (°C) 177, High
    Low Temperature Resistance (°C) -55
    Moisture/Humidity Resistance Moisture/humidity resistance
    Conductivity
    Filler Aluminum
    Dielectric Strength (V/mil) 77 Test Method
    Thermal Conductivity (W/m°K) 0.42
    Surface Resistivity (O) 1.1e17 (ohms/sq.) Test Method
    Volume Resistivity (O) 9.4e14 (ohms/cm) Test Method
    Hardness
    Shore D Hardness 85 Test Method
    Elongation (%) 1 Test Method
    Other Properties
    Coefficient of Thermal Expansion (CTE) 44e-6 (in./ in/°C) Test Method
    % Solids (%) 100
    Density (g/cm³) 13.8 (weight (lbs/gal))
    Business Information
    Shelf Life Details Store products at 39°F (4°C) or below for maximum storage life. Higher temperatures reduce normal storage life. Rotate stock on a “first-in-first-out” basis. CAUTION: Products are heat sensitive. Storage above 130°F (54°C) may cause an exothermic reaction resulting in evolution of excessive heat, noxious fumes, and possibly fire.;All of these products have a shelf life of 8 months when stored in their unopened containers @ 39°F (4°C) or below.
    Shelf Life Temperature (°F) <39
    Shelf Life (mon) 8

  • Best Practices for 3M 2214 Hi-Temp New Formula Gray

    *See Terms of Use Below

    1. Surface Preparation

      For high strength structural bonds, paint, oxide films, oils, dust, mold release agents and all other surface contaminants must be completely removed. However, the amount of surface preparation directly depends on the substrates, the required bond strength, environmental aging resistance, and requirements determined by the user in light of the user’s particular purpose and method of application.

      See vendor technical data sheet for more information.

    2. Application

      Warm products to room temperature before opening containers to restore proper application consistency and to prevent moisture condensation on adhesive surface. Containers may be stored at room temperature for 1-2 days to thaw. Do not warm at temperatures above 80°F (27°C).

      For maximum bond strength, apply product evenly to both surfaces to be joined.

      Join the adhesive coated surfaces and heat cure using the following bondline temperature and time for the specific product being used.

      Keep parts from moving during cure as contact pressure is necessary.

    3. Clean-Up

      Cleanup can be accomplished with solvent such as 3M™ Scotch-Grip™ Solvent No. 3 or Methyl Ethyl Ketone.*

      *Note: Prior to use of these solvents, extinguish or eliminate any ignition sources and read and follow supplier’s environmental, health, and safety recommendations listed on the MSDS and product label.

  • Comparable Materials for 3M 2214 Hi-Temp New Formula Gray

    *See Terms of Use Below

    Spec Engine® Results

  Download Technical Data Sheet   Save This Material   Compare View Saved Items

Popular Articles

Electrically Conductive Adhesives

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Epoxy Adhesives for Medical Devices

Read Article

Testing the effectiveness of surface treatments

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for 3M 2214 Hi-Temp New Formula Gray

All 3M Materials
View Now
Heat Cure Epoxy Adhesives
View Now
Epoxy Adhesives
View Now

Gluespec Poll

Which answer best describes a project you are currently working on?
Viscosity Test Methods
Viscosity Test Method
>1,000,000 cPs Brookfield
Peel Strength Test Methods
Peel Strength Type Substrate Test Temperature Test Method
2 piw T-peel strength Aluminum 24°C T-Peel bonds were measured on 1" wide specimens cut from two FPL etched 8" x 8" x .032" 2024 T3 clad aluminum panels bonded together. The separation note of the testing jaws was 20"/minute. Tests similar to ASTM D-1876. (All data in lbs./in. of width.)
5 piw T-peel strength Steel 24°C T-Peel bonds were measured on two 1" wide x 8" long specimens bonded together. These bonds were made on MEK wiped .035" steel. After bonding they were then pulled apart in 180° Peel at a jaw separation rate of 20"/in. rate. Tests similar to ASTM D-1876. (All data in lbs./in. of width.)
Shear Strength Test Methods
Shear Strength Type Cure Time Cure Temperature Substrate Test Temperature Test Method
2,800 psi Overlap shear strength 60 min 121°C Aluminum -53°C The data was developed using a cure cycle of 40 minutes @ 250°F (121°C) under 25 psi pressure except Scotch-Weld adhesive 2214 Hi-Temp New Formula which was 60 minutes at 250°F (121°C)., Overlap shear strength was measured on FPL etched 1" wide by 1/2" overlap specimens. The bonds were made from 2 panels of 4" x 7" x .063", 2024 T3 clad aluminum bonded together and cut into 1" wide specimens. The separation rate of the testing jaws was .1"/minute. Tests similar to ASTM D-1002.
2,800 psi Overlap shear strength 60 min 121°C Aluminum 24°C The data was developed using a cure cycle of 40 minutes @ 250°F (121°C) under 25 psi pressure except Scotch-Weld adhesive 2214 Hi-Temp New Formula which was 60 minutes at 250°F (121°C)., Overlap shear strength was measured on FPL etched 1" wide by 1/2" overlap specimens. The bonds were made from 2 panels of 4" x 7" x .063", 2024 T3 clad aluminum bonded together and cut into 1" wide specimens. The separation rate of the testing jaws was .1"/minute. Tests similar to ASTM D-1002.
2,800 psi Overlap shear strength 60 min 121°C Aluminum 82°C The data was developed using a cure cycle of 40 minutes @ 250°F (121°C) under 25 psi pressure except Scotch-Weld adhesive 2214 Hi-Temp New Formula which was 60 minutes at 250°F (121°C)., Overlap shear strength was measured on FPL etched 1" wide by 1/2" overlap specimens. The bonds were made from 2 panels of 4" x 7" x .063", 2024 T3 clad aluminum bonded together and cut into 1" wide specimens. The separation rate of the testing jaws was .1"/minute. Tests similar to ASTM D-1002.
2,500 psi Overlap shear strength 60 min 121°C Aluminum 121°C The data was developed using a cure cycle of 40 minutes @ 250°F (121°C) under 25 psi pressure except Scotch-Weld adhesive 2214 Hi-Temp New Formula which was 60 minutes at 250°F (121°C)., Overlap shear strength was measured on FPL etched 1" wide by 1/2" overlap specimens. The bonds were made from 2 panels of 4" x 7" x .063", 2024 T3 clad aluminum bonded together and cut into 1" wide specimens. The separation rate of the testing jaws was .1"/minute. Tests similar to ASTM D-1002.
2,000 psi Overlap shear strength 60 min 121°C Aluminum 149°C The data was developed using a cure cycle of 40 minutes @ 250°F (121°C) under 25 psi pressure except Scotch-Weld adhesive 2214 Hi-Temp New Formula which was 60 minutes at 250°F (121°C)., Overlap shear strength was measured on FPL etched 1" wide by 1/2" overlap specimens. The bonds were made from 2 panels of 4" x 7" x .063", 2024 T3 clad aluminum bonded together and cut into 1" wide specimens. The separation rate of the testing jaws was .1"/minute. Tests similar to ASTM D-1002.
1,200 psi Overlap shear strength 60 min 121°C Aluminum 177°C The data was developed using a cure cycle of 40 minutes @ 250°F (121°C) under 25 psi pressure except Scotch-Weld adhesive 2214 Hi-Temp New Formula which was 60 minutes at 250°F (121°C)., Overlap shear strength was measured on FPL etched 1" wide by 1/2" overlap specimens. The bonds were made from 2 panels of 4" x 7" x .063", 2024 T3 clad aluminum bonded together and cut into 1" wide specimens. The separation rate of the testing jaws was .1"/minute. Tests similar to ASTM D-1002.
2,000 psi Overlap shear strength Steel -53°C Overlap shear strength was measured on 1" wide by 1/2" overlap specimens. These bonds were made on 1" x 4" x .035" thick cold rolled steel which was MEK solvent wiped prior to bonding. The separation rate of the testing jaws was .1"/min. Tests similar to ASTM D-1002.
2,500 psi Overlap shear strength Steel 24°C Overlap shear strength was measured on 1" wide by 1/2" overlap specimens. These bonds were made on 1" x 4" x .035" thick cold rolled steel which was MEK solvent wiped prior to bonding. The separation rate of the testing jaws was .1"/min. Tests similar to ASTM D-1002.
2,000 psi Overlap shear strength Steel 82°C Overlap shear strength was measured on 1" wide by 1/2" overlap specimens. These bonds were made on 1" x 4" x .035" thick cold rolled steel which was MEK solvent wiped prior to bonding. The separation rate of the testing jaws was .1"/min. Tests similar to ASTM D-1002.
2,000 psi Overlap shear strength Steel 121°C Overlap shear strength was measured on 1" wide by 1/2" overlap specimens. These bonds were made on 1" x 4" x .035" thick cold rolled steel which was MEK solvent wiped prior to bonding. The separation rate of the testing jaws was .1"/min. Tests similar to ASTM D-1002.
2,000 psi Overlap shear strength Steel 149°C Overlap shear strength was measured on 1" wide by 1/2" overlap specimens. These bonds were made on 1" x 4" x .035" thick cold rolled steel which was MEK solvent wiped prior to bonding. The separation rate of the testing jaws was .1"/min. Tests similar to ASTM D-1002.
700 psi Overlap shear strength Steel 177°C Overlap shear strength was measured on 1" wide by 1/2" overlap specimens. These bonds were made on 1" x 4" x .035" thick cold rolled steel which was MEK solvent wiped prior to bonding. The separation rate of the testing jaws was .1"/min. Tests similar to ASTM D-1002.
Dielectric Strength Test Methods
Dielectric Strength Test Method
77 V/mil ASTM-D-149
Surface Resistivity Test Methods
Surface Resistivity Temperature Test Method
1.1e17 (ohms/sq.) 23°C ASTM-D-257, 500 Volts-DC
Volume Resistivity Test Methods
Volume Resistivity Temp (°C) Test Method
9.4e14 (ohms/cm) 23°C ASTM-D-257, 500 Volts-DC
Elongation Test Methods
Elongation Test Method
1 % Approx.
Shore D Hardness Test Methods
Shore D Hardness Shore Hardness Test Method
85 Approx.
Coefficient of Thermal Expansion (CTE) Test Methods
Coefficient of Thermal Expansion (CTE) CTE Temperature (°C)
44e-6 (in./ in/°C) -60 to 80°C