| Application Type | Bond |
|---|---|
| 1 Part or 2 Part | 2 Part |
| Material Form | Liquid |
| Substrate | Aluminum, PlexiGlass, Metal, Nylon, ABS, Rigid PVC, Cold rolled Steel, Rubber, Wood, FRP, Abraded Aluminum, Lexan, Polycarbonate, Primed Steel, Etched Aluminum, Plastic, Steel, Solvent Wiped Aluminum, Polystyrene, Abraded Steel , Plastics, Solvent Wiped Steel, Primed steel |
| Manufacturer | 3M |
| Chemistry | Isocyanate, Polyol, Polyurethane, Urethane |
| Cure Method | Base/Accelerator |
| Cure Temperature (°C) | 20 to 25, 24 |
| Cure Time (min) | 1,440, Fast |
| Viscosity (cPs) | 30,000 |
| Color | Brown |
| Chemical Resistance | Salt spray, Water |
| High Temperature Resistance (°C) | 82 |
| Low Temperature Resistance (°C) | -40 |
Surfaces to be bonded must be dry and free from rust, oil, grease and wax. Surfaces can be cleaned with an abrasive such as 3MTM Coated Abrasives (240 grit) followed by wiping with a solvent such as Scotch-GripTM Solvent No. 3.*
*Note: When using solvents, extinguish all ignition sources and follow the manufacturer’s precautions and directions for use when handling such materials.
| amet tincidunt nonummy euismod. | tincidunt. | consectetuer. |
|---|---|---|
| sit. | sit. | diam aliquam. |
| lorem elit ipsum ut. | sed. | elit adipiscing. |
| erat adipiscing nibh. | dolore magna dolore. | dolore ipsum. |
| adipiscing tincidunt magna diam. | tincidunt ut nonummy. | magna dolore. |
| euismod magna. | nonummy. | elit. |
| lorem dolore sed. | amet euismod. | tincidunt adipiscing. |
| laoreet ut nonummy adipiscing. | sed. | ipsum magna. |
|---|---|---|
| ipsum magna dolore. | aliquam laoreet. | consectetuer dolor. |
| magna aliquam tincidunt consectetuer. | amet ipsum elit. | tincidunt. |
| laoreet. | euismod dolore elit. | consectetuer sed. |
| sit lorem sit aliquam. | ipsum aliquam euismod. | consectetuer sed. |
| amet adipiscing consectetuer. | dolor. | diam. |
| elit nibh. | magna. | euismod. |
|---|---|---|
| euismod magna. | lorem magna. | dolor euismod. |
| dolor euismod aliquam dolore. | erat. | consectetuer. |
| ipsum. | adipiscing. | euismod ipsum. |
|---|---|---|
| euismod adipiscing. | tincidunt amet tincidunt. | ut consectetuer. |
| ut dolore sit laoreet. | amet nonummy euismod. | tincidunt. |
| nibh diam. | sed. | dolore magna. |
|---|---|---|
| lorem sed elit. | consectetuer. | erat sed. |
| consectetuer. | magna amet erat. | dolor. |
| consectetuer. | dolor. | adipiscing. |
| aliquam. | tincidunt. | consectetuer sit. |
| diam ipsum. | magna nonummy. | laoreet. |
| adipiscing lorem amet aliquam. | amet laoreet ipsum. | tincidunt tincidunt. |
|---|---|---|
| laoreet elit nonummy. | tincidunt elit. | amet dolore. |
| dolor lorem dolore. | nibh. | tincidunt. |
| ipsum. | laoreet nonummy consectetuer. | amet dolor. |
| nonummy consectetuer aliquam. | euismod adipiscing. | dolore consectetuer. |
| nibh dolore nonummy. | sit. | dolor. |
| aliquam laoreet. | diam nonummy. | ut. |
|---|---|---|
| dolor euismod consectetuer diam. | dolor nonummy. | erat. |
| consectetuer sed tincidunt. | dolor nonummy magna. | ipsum. |
| nonummy euismod. | laoreet erat tincidunt. | ut. |
| sit aliquam. | adipiscing. | nonummy. |
magna elit diam adipiscing aliquam nonummy sed lorem sit tincidunt. tincidunt sed sit euismod dolore lorem sit nibh sit lorem. aliquam erat dolor euismod sit aliquam dolor magna aliquam nonummy.
ut elit ipsum tincidunt nibh nonummy sed dolore. adipiscing elit dolore nonummy ipsum nibh erat consectetuer. ut sit diam amet sed laoreet aliquam consectetuer. magna sit lorem elit nibh ipsum tincidunt magna. dolore dolor diam consectetuer laoreet adipiscing euismod lorem.
adipiscing adipiscing euismod magna aliquam sed dolore. dolore sed nonummy lorem consectetuer amet tincidunt. erat tincidunt aliquam dolor ut nonummy elit. nibh sed diam amet sit adipiscing erat.
amet aliquam magna elit nonummy amet amet nonummy dolore aliquam diam. sit nonummy tincidunt aliquam adipiscing aliquam adipiscing elit dolor sit sed.
dolore adipiscing elit adipiscing sed diam tincidunt euismod aliquam nibh magna. elit aliquam dolore consectetuer dolore elit euismod elit aliquam nibh dolore. dolore ipsum nibh tincidunt dolor nibh ut ut ipsum sed magna.
aliquam elit erat consectetuer elit erat ut amet ut. elit amet erat nonummy adipiscing ut laoreet adipiscing dolor. magna sit nonummy diam nonummy amet aliquam ut dolore. laoreet ut sed diam lorem adipiscing consectetuer dolor sit.
magna lorem tincidunt magna dolor euismod adipiscing euismod adipiscing. lorem diam magna laoreet elit tincidunt dolor aliquam diam. adipiscing magna amet tincidunt consectetuer sit nonummy ipsum diam.
| Viscosity | Temperature |
|---|---|
| 30,000 cPs | 24°C |
| Work / Pot Time | Test Method | Temperature |
|---|---|---|
| 5.00 to 15 min | 100 grams mixed at 75°F 24°C: 5-15 min. | 24°C |
| 7 min |
| Shear Strength | Type | Substrate | Test Time | Test Temperature | Test Method |
|---|---|---|---|---|---|
| 2,500 psi | Overlap shear strength | Etched Aluminum | -40°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 2,000 psi | Overlap shear strength | Abraded and Solvent Wiped Aluminum | -40°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 1,000 psi | Overlap shear strength | Solvent Wiped Aluminum | -40°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 2,000 psi | Overlap shear strength | Abraded and Solvent Wiped Steel | -40°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 1,000 psi | Overlap shear strength | Solvent Wiped Steel | -40°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 2,000 psi | Overlap shear strength | Etched Aluminum | 24°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 2,000 psi | Overlap shear strength | Abraded and Solvent Wiped Aluminum | 24°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 1,000 psi | Overlap shear strength | Solvent Wiped Aluminum | 24°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 1,200 psi | Overlap shear strength | Abraded and Solvent Wiped Steel | 24°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 700 psi | Overlap shear strength | Solvent Wiped Steel | 24°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 300 psi | Overlap shear strength | Etched Aluminum | 82°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 300 psi | Overlap shear strength | Abraded and Solvent Wiped Aluminum | 82°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 100 psi | Overlap shear strength | Solvent Wiped Aluminum | 82°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 100 psi | Overlap shear strength | Abraded and Solvent Wiped Steel | 82°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 20 psi | Overlap shear strength | Solvent Wiped Steel | 82°C | All aluminum data were developed on .063-inch thick 2024 T-3 clad aluminum and all steel data on .035-inch cold rolled steel. Test specimens were 1/2-inch overlap, 1-inch wide with .005-inch thick bondlines pulled at a testing rate of .1-inch/min. | |
| 240 psi | Overlap shear strength | Nylon | -40°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 1,240 psi | Overlap shear strength | Lexan | -40°C | Denotes substrate failure., All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 620 psi | Overlap shear strength | Plexiglass | -40°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 1,660 psi | Overlap shear strength | FRP | -40°C | Denotes substrate failure, All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 370 psi | Overlap shear strength | Rigid PVC | -40°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 440 psi | Overlap shear strength | ABS | -40°C | Denotes substrate failure, All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 330 psi | Overlap shear strength | Polystyrene | -40°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 580 psi | Overlap shear strength | Nylon | 24°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 1,840 psi | Overlap shear strength | Lexan | 24°C | Denotes substrate failure., All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 1,300 psi | Overlap shear strength | Plexiglass | 24°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 1,150 psi | Overlap shear strength | FRP | 24°C | Denotes substrate failure., All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 960 psi | Overlap shear strength | Rigid PVC | 24°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 810 psi | Overlap shear strength | ABS | 24°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 530 psi | Overlap shear strength | Polystyrene | 24°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 40 psi | Overlap shear strength | Nylon | 82°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 125 psi | Overlap shear strength | Lexan | 82°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 70 psi | Overlap shear strength | Plexiglass | 82°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 180 psi | Overlap shear strength | FRP | 82°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 110 psi | Overlap shear strength | Rigid PVC | 82°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 300 psi | Overlap shear strength | ABS | 82°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 110 psi | Overlap shear strength | Polystyrene | 82°C | All data were developed on 1/8-inch thick, 1/2-inch overlap, 1-inch wide specimens with .005-inch thick bondlines that had been abraded and alcohol wiped prior to bonding. | |
| 5 psi | Overlap shear strength | plastic to primed steel | 1,800 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 20 psi | Overlap shear strength | plastic to primed steel | 3,600 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 90 psi | Overlap shear strength | plastic to primed steel | 7,200 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 400 psi | Overlap shear strength | plastic to primed steel | 10,800 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 490 psi | Overlap shear strength | plastic to primed steel | 14,400 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 560 psi | Overlap shear strength | plastic to primed steel | 18,000 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 680 psi | Overlap shear strength | plastic to primed steel | 21,600 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 790 psi | Overlap shear strength | plastic to primed steel | 25,200 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 1,200 psi | Overlap shear strength | plastic to primed steel | 57,600 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 1,550 psi | Overlap shear strength | plastic to primed steel | 86,400 sec | 25°C | Specimens: 1/2-inch overlap fiber reinforced plastic to primed steel, 0.032-inch bondline. Specimens were pulled at 2 inches/min. |
| 0 psi | Overlap shear strength | plastic to primed steel | 600 sec | 38°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 240 psi | Overlap shear strength | plastic to primed steel | 1,800 sec | 38°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 500 psi | Overlap shear strength | plastic to primed steel | 2,700 sec | 38°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 650 psi | Overlap shear strength | plastic to primed steel | 3,600 sec | 38°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 140 psi | Overlap shear strength | plastic to primed steel | 600 sec | 49°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 480 psi | Overlap shear strength | plastic to primed steel | 1,200 sec | 49°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 750 psi | Overlap shear strength | plastic to primed steel | 30 sec | 49°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 120 psi | Overlap shear strength | plastic to primed steel | 5.00 sec | 66°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 400 psi | Overlap shear strength | plastic to primed steel | 10 sec | 66°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 760 psi | Overlap shear strength | plastic to primed steel | 15 sec | 66°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 400 psi | Overlap shear strength | plastic to primed steel | 5.00 sec | 82°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 660 psi | Overlap shear strength | plastic to primed steel | 10 sec | 82°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 900 psi | Overlap shear strength | plastic to primed steel | 15 sec | 82°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 340 psi | Overlap shear strength | plastic to primed steel | 2.00 sec | 93°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 660 psi | Overlap shear strength | plastic to primed steel | 5.00 sec | 93°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 900 psi | Overlap shear strength | plastic to primed steel | 10 sec | 93°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 440 psi | Overlap shear strength | plastic to primed steel | 2.00 sec | 107°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 760 psi | Overlap shear strength | plastic to primed steel | 5.00 sec | 107°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| 900 psi | Overlap shear strength | plastic to primed steel | 10 sec | 107°C | Specimens: 1/2-inch overlap shear, fiber reinforced plastic to primed steel .032-inch bondline. Specimens were placed in an oven at designated temperature for the specified time. Bonds were then cooled for 1 minute and pulled at a rate of 2-inch/min. |
| Tensile Strength | Cure Time | Cure Temperature | Test Temperature | Test Method |
|---|---|---|---|---|
| 3,000 psi | 60 min | 121°C | 20 to 25°C RT | ASTM-D-738 at 2 inches/min. |
| 3,000 psi | 30 min | 141°C | 20 to 25°C RT | ASTM-D-738 at 2 inches/min. |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.