3M 4000UV Marine Adhesive Sealant Fast Cure Datasheet 3M 4000UV Marine Adhesive Sealant Fast Cure

CONTACT REP
Information provided by Gluespec

  • Description for 3M 4000UV Marine Adhesive Sealant Fast Cure

    A one-part adhesive sealant that cures to form a firm, rubbery waterproof seal. Its flexibility allows for the dissipation of stress caused by shock, vibration, swelling or shrinking.

    *See Terms of Use Below

    Application Type Bond, Seal, Adhesive: Instant Adhesives
    1 Part or 2 Part 1-Part
    Material Form Medium Paste
    Substrate Aluminum, Copper, Metals, Nylon, Plastics/Polymers, Wood, Stainless Steel, Fiberglass, Bronze, ABS, Fir, Teak, Teak (primed), Mahogany
    Industry Marine applications below the waterline, Rails, Two Wheel Vehicles, Commercial & Specialty Vehicles, Marine applications above the waterline
    Manufacturer 3M
    Chemistry Polyether
    Cure Method UV
    Application Temperature (°F) 40 to 100
    Cure Temperature (°C) 21
    Cure Time (min) 1,440
    Color White
    High Temperature Resistance (°C) Heat Resistance, 90
    Low Temperature Resistance (°C) -40
    Density (g/cm³) 11.7 (Approx.) (Lbs/Gallon )

  • Technical Data for 3M 4000UV Marine Adhesive Sealant Fast Cure

    *See Terms of Use Below

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 1-Part
    • Material Form
      • Paste - Medium Paste
    • Substrate
    • Industry
      • Marine - Marine applications above the waterline, Marine applications below the waterline
      • Rail - Rails
      • Two Wheel Vehicles
      • Commercial & Specialty Vehicles
      • Industrial
      • Other - Bedding and sealing applications, Fiberglass hull, Porthole frames, Deck fittings, Moldings, Thru hull and deck hardware, Portlights, Hatches, Metal Hardware
    • Chemistry
      • Other - Polyether
    • Cure Method
      • UV / Visible Light - UV
    • Color
      • White
    Specifications
    Cure Specs
    Application Temperature (°F) 40 to 100
    Cure Temperature (°C) 21
    Cure Time (min) 1,440
    Tack Free Time (min) 22 Test Method
    Bond Strength
    Peel Strength (piw) 8.8 (lbs./in.), 8.2 (lbs./in.), 5.3 (lbs./in.), 8.7 (lbs./in.), 8.0 (lbs./in.), 9.4 (lbs./in.) Test Method
    Shear Strength (psi) 226, 174, 196, 329, 424, 251, 279, 424, 251, 311, 584, 590, 509, 329, 359, 284, 135, 675, 542, 457, 381 Test Method
    Tensile Strength (psi) 253, 306, 299 Test Method
    Material Resistance
    UV Resistance superior UV resistance
    High Temperature Resistance (°C) Heat Resistance, 90
    Low Temperature Resistance (°C) -40
    Hardness
    Shore A Hardness 38 to 39
    Elongation (%) 790 Test Method
    Other Properties
    Density (g/cm³) 11.7 (Approx.) (Lbs/Gallon )
    Business Information
    Shelf Life Details Strorage: Store product at 60-80°F (16-27°C) for maximum storage life. Higher temperatures can reduce normal storage life. Lower temperatures can cause increased viscosity of a temporary nature. Rotate stock on a “first in-first out” basis.;When stored at the recommended conditions in the original, unopened container this product has a shelf life of 12 months from date of shipment.
    Shelf Life Temperature (°F) 140 to 176
    Shelf Life Type From the date of shipment.
    Shelf Life (mon) 12

  • Best Practices for 3M 4000UV Marine Adhesive Sealant Fast Cure

    *See Terms of Use Below

    1. Surface Preparation

      Surface should be clean, dry and free of contaminants. New surfaces should be solvent wiped with 3M™ General Purpose Adhesive Cleaner 08984, or equivalent. Other than new surfaces should be sanded with a fine grade abrasive to enhance bond strength.

    2. Clean-Up

      For cleaning 3M marine adhesive/sealant 4000 UV before it is cured, use a dry cloth to remove the majority, followed by a cloth damp with 3M general purpose adhesive cleaner, toluene, acetone, or other good cleaning solvent. Cured 3M marine adhesive/sealant 4000 UV can be removed mechanically with a knife, razor blade, piano wire or by sanding.

    3. Removal

      Cured 3M marine adhesive/sealant 4000 UV can be removed mechanically with a knife, razor blade, piano wire or by sanding

  • Comparable Materials for 3M 4000UV Marine Adhesive Sealant Fast Cure

    *See Terms of Use Below

    Spec Engine® Results

    • Hernon
      Ultrabond 55711(Hernon)

      A single component anaerobic and UV curable, paste-like sealing compound formulated to provide instant sealing and bonding of electrical connectors.

    • Wacker
      Elastosil A 442(Wacker)

      Wacker Elastosil A 442 is a 1-Part UV cure Silicone Rubber Paste used to Adhere Glass, Ferrous metals and Most metals

    • Compare All

    Closest Results from this Manufacturer

    • 3M
      Adhesive Sealant 540(3M)

      Polyurethane • Moisture cures rapidly to flexible seal/bond for many plastics, metal, wood, and more • 250 psi tensile strength

    • 3M
      4200(3M)

      A fast curing, one-part polyurethane that chemically reacts with moisture to deliver strong, flexible bonds to wood, gelcoat and fiberglass. It forms watertight, weather-resistant seals on joints and boat hardware above and below the waterline.

    • 3M
      Hybrid Sealant 740(3M)

      A one component, moisture curing products which form permanent elastic bonds. Differentiated from other high performance sealants as they are very low VOC, have better UV resistance.

    • Compare All
  Download Technical Data Sheet   Save This Material   Compare View Saved Items

Popular Articles

Testing the effectiveness of surface treatments

Read Article

Anaerobic Adhesives

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

What Are the Differences Between Adhesives and Sealants?

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for 3M 4000UV Marine Adhesive Sealant Fast Cure

All 3M Materials
View Now
Marine Adhesive Sealants
View Now
Fiberglass Bonding
View Now
Marine Adhesive Sealants
View Now

Gluespec Poll

Who do you read or follow for engineering news and entertainment?
Tack Free Time Test Methods
Tack Free Time Tack Free Temperature
22 min 21°C
Peel Strength Test Methods
Peel Strength Type Substrate Test Temperature Test Humidity Test Method
8.8 (lbs./in.) 180° Peel Strength Gelcoat 21°C 50 % One inch (2.54 cm) wide specimen on canvas. Tested at 70°F (21°C), 50% relative humidity, Cohesive failure, width
8.2 (lbs./in.) 180° Peel Strength Fiberglass 21°C 50 % One inch (2.54 cm) wide specimen on canvas. Tested at 70°F (21°C), 50% relative humidity, Cohesive failure, width
5.3 (lbs./in.) 180° Peel Strength Aluminum 21°C 50 % One inch (2.54 cm) wide specimen on canvas. Tested at 70°F (21°C), 50% relative humidity, Cohesive failure, width
8.7 (lbs./in.) 180° Peel Strength Teak 21°C 50 % One inch (2.54 cm) wide specimen on canvas. Tested at 70°F (21°C), 50% relative humidity, Cohesive failure, width
8.0 (lbs./in.) 180° Peel Strength Teak (primed) 21°C 50 % One inch (2.54 cm) wide specimen on canvas. Tested at 70°F (21°C), 50% relative humidity, Cohesive failure, width
9.4 (lbs./in.) 180° Peel Strength Mahogany 21°C 50 % One inch (2.54 cm) wide specimen on canvas. Tested at 70°F (21°C), 50% relative humidity, Cohesive failure, width
Tensile Strength Test Methods
Tensile Strength Test Temperature Test Method
253 psi 21°C A 1/8 inch (0.3175 cm) dumbbell specimen with a 1/8 inch (0.3175 cm) square cross section was tested at 2.0 inches/minute (5.08 cm/minute)
306 psi ASTM references: D412 and G-26 Type B, BH
299 psi ASTM references: D412 and G-26 Type B, BH
Shear Strength Test Methods
Shear Strength Type Substrate Test Temperature Test Humidity Test Method
226 psi Overlap Shear Strength Woods: Fir 21°C 50 % One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 40/60 Coh/Adh) failure
174 psi Overlap Shear Strength Woods: Teak 21°C 50 % One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 40/60 Coh/Adh) failure
196 psi Overlap Shear Strength Woods: Teak (primed) 21°C 50 % One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 40/60 Coh/Adh) failure
329 psi Overlap Shear Strength Metals: Aluminum 21°C 50 % One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Adhesive
424 psi Overlap Shear Strength Plastics/Polymers: Gelcoat 21°C 50 % One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
251 psi Overlap Shear Strength Plastics/Polymers: Fiberglass 21°C 50 % One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
279 psi Overlap Shear Strength Plastics/Polymers: ABS 21°C 50 % One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 40/60 Coh/Adh) failure
424 psi Overlap Shear Strength Plastics/Polymers: Gelcoat 21°C 50 % Initial Strength, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 95/5 (Coh/Adh)failure
251 psi Overlap Shear Strength Plastics/Polymers: Fibergalss 21°C 50 % Initial Strength, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
311 psi Overlap Shear Strength Plastics/ Polmers: Nylon 21°C 50 % Initial Strength, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 50/50 (Coh/Adh) failure
584 psi Overlap Shear Strength Metals: Stainless Steel 21°C 50 % Initial Strength, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 95/5 (Coh/Adh) failure
590 psi Overlap Shear Strength Metals: Bronze 21°C 50 % Initial Strength, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 90/10 (Coh/Adh) failure
509 psi Overlap Shear Strength Metals: Copper 21°C 50 % Initial Strength, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
329 psi Overlap Shear Strength Metals: Alumunum 21°C 50 % Initial Strength, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 5/95 (Coh/Adh) failure
359 psi Overlap Shear Strength Plastics/Polymers: Gelcoat 21°C 50 % Salt Water Immersion 500 hours, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
284 psi Overlap Shear Strength Plastics/Polymers: Fiberglass 21°C 50 % Salt Water Immersion 500 hours, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
135 psi Overlap Shear Strength Plastics/ Polmers: Nylon 21°C 50 % Salt Water Immersion 500 hours, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 25/75 (Coh/Adh) failure
675 psi Overlap Shear Strength Metals: Stainless Steel 21°C 50 % Salt Water Immersion 500 hours, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
542 psi Overlap Shear Strength Metals: Bronze 21°C 50 % Salt Water Immersion 500 hours, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, Cohesive failure
457 psi Overlap Shear Strength Metals: Copper 21°C 50 % Salt Water Immersion 500 hours, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 75/25 (Coh/Adh) failure
381 psi Overlap Shear Strength Metals: Aluminum 21°C 50 % Salt Water Immersion 500 hours, One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness). Tested at 70°F (21°C), 50% relative humidity, 55/45 (Coh/Adh) failure.
Elongation Test Methods
Elongation Test Method
790 % A 1/8 inch (0.3175 cm) dumbbell specimen with a 1/8 inch (0.3175 cm) square cross section was tested at 2.0 inches/minute (5.08 cm/minute).