3M 70 Scotch-Weld HoldFast Cylinder Spray Adhesive Datasheet 3M 70 Scotch-Weld HoldFast Cylinder Spray Adhesive

Information provided by Gluespec
  • Description for 3M 70 Scotch-Weld HoldFast Cylinder Spray Adhesive

    Industrial grade, versatile bulk spray adhesives formulated for specific substrates and market needs (soft foams – polystyrene foams).

    *See Terms of Use Below

    Application Type Bond
    1 Part or 2 Part 1 Part
    Material Form Liquid, Synthetic elastomer
    Substrate Acrylic, Aluminum, Fabrics, Soft foams, Polystyrene foams, Polystyrene foams, Wood, Galvanized, Polyethylene, Glass, Metal, Heavy papers, Most plastics, Polypropylene, Rubber, Concrete, FRP (Fiber Reinforced Plastic), Birch, ABS
    Industry Motor homes, Marine
    Manufacturer 3M
    Chemistry Synthetic elastomer
    Cure Method Solvent
    Cure Time (min) Fast, 0.50 to 1.00
    Color Clear, Translucent
    High Temperature Resistance (°C) High temperature resistance
    Density (g/cm³) 5.7 (lbs/gal)

Popular Articles

Lightweighting drives automotive adhesives demand

Read Article

Testing the effectiveness of surface treatments

Read Article

6 objects held together by adhesives you probably can't live without

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for 3M 70 Scotch-Weld HoldFast Cylinder Spray Adhesive

Gluespec Poll

What level of expertise do you have in specialty chemicals like adhesives, sealants, conformal coatings, etc.?
Shear Strength Test Methods
Shear Strength Type Substrate Test Temperature Test Method
64 psi Overlap Shear Strength ABS to ABS (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
123 psi Overlap Shear Strength ABS to ABS (1 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
152 psi Overlap Shear Strength Acrylic to Acrylic (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
79 psi Overlap Shear Strength Aluminum to Aluminum (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
193 psi Overlap Shear Strength Birch to Birch (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
92 psi Overlap Shear Strength Birch to Birch (1 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
78 psi Overlap Shear Strength Galvanized to Galvanized (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
87 psi Overlap Shear Strength Galvanized to Galvanized (1 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
35 psi Overlap Shear Strength Polyethylene to Polyethylene (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
75 psi Overlap Shear Strength Polypropylene to Polypropylene (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
96 psi Overlap Shear Strength FRP (Fiber Reinforced Plastic) to FRP (2 surface adhesive bond) 24°C 1 square inch bonds tested at 2 inches per minute separation rate at 75°F (24°)
Tensile Strength Test Methods
Tensile Strength Cure Time Test Temperature Test Method
30 (grams) 10 min -12°C 4 square inch bonds tested with 30 grams hanging in tensile. Temperature is held for 10 minutes and ramped at 10°F increments, until complete failure.
% Solids Test Methods
% Solids Test Method
High
21 % Solids Content - (by wt.)