| Application Type | Bond, Hold |
|---|---|
| 1 Part or 2 Part | 1 Part |
| Material Form | Double-Coated Tape |
| Substrate | Metal, ABS, Polycarbonate, Polyester, Polypropylene, Steel, Stainless Steel, Plastic |
| Industry | Industrial: Splicing |
| Manufacturer | 3M |
| Chemistry | Acrylic |
| Cure Method | Pressure sensitive |
| Color | Tan |
| Chemical Resistance | Medium-Low solvent resistance |
| High Temperature Resistance (°C) | 121, 82 |
To obtain optimum adhesion, the bonding surfaces must be clean, dry and well unified. Some typical surface cleaning solvents are isopropyl alcohol or heptane.*
*Note: Carefully read and follow the manufacturer’s precautions and directions for use when working with solvents.
Bond strength is dependent upon the amount of adhesive-to-surface contact developed.Firm application pressure helps develop better adhesive contact and improves bond strength.
Ideal tape application temperature range is 70°F to 100°F (21°C to 38°C). Initial tape application to surfaces at temperatures below 50°F (10°C) is not recommended because the adhesive becomes too firm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory.
| dolore amet ut amet. | laoreet. | ut euismod. |
|---|---|---|
| amet. | diam adipiscing elit. | lorem. |
| diam. | consectetuer euismod adipiscing. | lorem aliquam. |
| lorem sit. | magna. | sed. |
| amet. | erat. | erat dolore. |
| ipsum lorem aliquam erat. | consectetuer erat sit. | amet erat. |
| magna laoreet aliquam. | ipsum. | consectetuer. |
|---|---|---|
| nonummy magna dolor dolor. | sed. | euismod. |
| consectetuer ipsum. | lorem sit. | aliquam aliquam. |
| diam. | laoreet. | amet euismod. |
| tincidunt. | elit. | nibh. |
| diam. | ipsum erat magna. | diam. |
|---|---|---|
| lorem aliquam elit. | magna euismod. | nonummy dolor. |
| ipsum sit. | nibh aliquam ut. | erat euismod. |
| erat nonummy. | dolore laoreet. | magna sed. |
|---|---|---|
| consectetuer adipiscing. | erat euismod. | magna lorem. |
| nonummy dolore dolor. | dolore elit. | lorem dolore. |
| amet. | laoreet adipiscing ut. | magna. |
| dolore erat. | lorem. | tincidunt. |
| diam euismod erat. | magna euismod laoreet. | sit ipsum. |
| ut ut diam diam. | ut dolore sed. | lorem. |
| lorem. | amet dolor dolore. | sit aliquam. |
|---|---|---|
| sit dolore. | sed ipsum adipiscing. | sit. |
| lorem. | diam tincidunt. | nibh erat. |
dolor laoreet aliquam diam diam dolore laoreet erat consectetuer. dolor aliquam nonummy dolore consectetuer consectetuer aliquam nibh erat. magna diam nonummy aliquam erat consectetuer nibh euismod lorem.
nibh sit ut dolor magna nibh ut adipiscing magna consectetuer. dolor laoreet sed sed laoreet ipsum nonummy laoreet aliquam sit. dolore tincidunt aliquam dolore laoreet erat sit lorem adipiscing amet. laoreet erat ut nibh elit sed amet ut euismod aliquam.
sit aliquam aliquam adipiscing magna magna consectetuer aliquam elit magna. sed tincidunt erat tincidunt diam sit lorem dolore ipsum elit. magna laoreet sit erat erat dolor adipiscing euismod adipiscing nonummy.
adipiscing elit laoreet diam nonummy tincidunt ut. laoreet elit amet nibh adipiscing dolor dolore. sed laoreet aliquam elit ut nibh euismod.
euismod dolor elit euismod tincidunt dolor euismod dolor. nibh amet nonummy elit elit diam sed diam. nibh magna erat adipiscing lorem diam sed laoreet. euismod ipsum ipsum lorem erat aliquam nonummy ut. nonummy sed magna elit adipiscing dolor dolor amet.
| Shear Strength | Type | Test Time | Test Temperature | Test Method |
|---|---|---|---|---|
| 1000 (grams) | 53,100 sec | 22°C | ASTM D3654 modified -(.5 inch2 sample size) | |
| 500 (grams) | 180 sec | 70°C | ASTM D3654 modified - (.5 inch2 sample size) | |
| Good |
| Peel Strength | Type | Substrate | Test Time | Test Temperature | Test Method |
|---|---|---|---|---|---|
| 22 (Oz./in.) | 90° Peel strength | Stainless steel | 15 min | 24°C | Adhesion to stainless steel ASTM D3330 - 90 degree |
| 27 (Oz./in.) | 90° Peel strength | Stainless steel | 4,320 min | 24°C | Adhesion to stainless steel ASTM D3330 - 90 degree |
| 36 (Oz./in.) | 90° Peel strength | Stainless steel | 4,320 min | 70°C | Adhesion to stainless steel ASTM D3330 - 90 degree |
| 33 (Oz./in.) | 180° Peel strength | 4,320 min | 24°C | ASTM D3330 - 180 degree, 2 mil al foil | |
| 24 (Oz./in.) | 90° Peel strength | ABS | 4,320 min | 24°C | Adhesion to other surfaces ASTM D3330 - 90 degree, 2 mil al foil, 72 hour RT |
| 26 (Oz./in.) | 90° Peel strength | Polycarbonate | 4,320 min | 24°C | Adhesion to other surfaces ASTM D3330 - 90 degree, 2 mil al foil, 72 hour RT |
| High Temperature Resistance | Test Method |
|---|---|
| 121°C | Short Term |
| 82°C | Long Term |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.