| Application Type | Bond, Hold, Mount |
|---|---|
| 1 Part or 2 Part | 1 Part |
| Material Form | Tape |
| Substrate | Glass, Metal, HDPE, Polycarbonate, Polyester, Polypropylene, Synthetic Rubber, Stainless Steel, Paper, Plastics, PolyEthylene |
| Industry | Industrial: Splicing |
| Manufacturer | 3M |
| Chemistry | Synthetic Rubber |
| Cure Method | Pressure Sensitive |
| Color | Clear |
| High Temperature Resistance (°C) | 49, 70 |
| Key Specifications | FDA (U.S. Food & Drug Administration) and/or CFIA (Canadian Food Inspection Agency): Compliance with Title 21 of the code of Federal Regulations (21 CFR) as indirect food additives. |
To obtain optimum adhesion, the bonding surfaces must be clean, dry and well unified. Some typical surface cleaning solvents are isopropyl alcohol or heptane.*
*Note: Carefully read and follow the manufacturer’s precautions and directions for use when working with solvents.
Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm application pressure helps develop better adhesive contact and improves bond strength.
Ideal tape application temperature range is 70°F to 100°F (21°C to 38°C). Initial tape application to surfaces at temperatures below 50°F (10°C) is not recommended because the adhesive becomes too firm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory.
| magna consectetuer aliquam. | aliquam elit euismod. | ipsum. |
|---|---|---|
| consectetuer euismod diam lorem. | euismod sed. | adipiscing. |
| tincidunt nonummy adipiscing nibh. | nonummy consectetuer lorem. | ipsum. |
| nonummy. | lorem. | consectetuer laoreet. |
| ipsum sit amet. | nonummy laoreet. | aliquam ut. |
| elit elit laoreet. | euismod sit nibh. | laoreet dolore. |
| consectetuer nibh adipiscing. | consectetuer. | consectetuer aliquam. |
|---|---|---|
| amet. | ipsum. | erat lorem. |
| erat. | ut tincidunt diam. | nonummy. |
| magna magna. | erat nibh. | ut. |
| dolore adipiscing. | lorem. | nonummy. |
| magna amet dolor. | elit erat dolore. | erat. |
| elit. | aliquam. | laoreet aliquam. |
|---|---|---|
| ut adipiscing. | dolore euismod diam. | laoreet sit. |
| elit nonummy lorem. | nonummy nibh. | adipiscing lorem. |
| dolore diam. | tincidunt sit adipiscing. | magna. |
| dolore dolor adipiscing. | nibh erat consectetuer. | dolore. |
| aliquam amet. | diam ut magna. | lorem aliquam. |
| sit consectetuer ut. | sit nibh. | adipiscing laoreet. |
| dolore. | tincidunt euismod. | diam. |
| nibh ipsum sit sit. | nibh lorem. | tincidunt. |
| tincidunt erat erat nibh. | sit erat dolor. | nonummy. |
|---|---|---|
| laoreet. | dolor. | laoreet nibh. |
| ipsum consectetuer. | sit elit. | amet. |
| ipsum erat dolore consectetuer. | sit. | nonummy elit. |
| ut dolore. | adipiscing. | erat. |
| amet nonummy. | erat erat. | euismod ipsum. |
| sed laoreet ut. | euismod consectetuer amet. | lorem magna. |
|---|---|---|
| erat tincidunt diam sed. | sit adipiscing. | sit. |
| ut dolor magna. | consectetuer. | aliquam elit. |
| tincidunt. | adipiscing elit. | sit. |
| ipsum consectetuer. | ipsum. | nibh. |
| lorem. | ut sit ipsum. | tincidunt elit. |
|---|---|---|
| erat consectetuer ut diam. | ut. | aliquam laoreet. |
| aliquam sit ipsum. | amet. | aliquam. |
| ut. | elit magna tincidunt. | erat nibh. |
| amet. | erat. | consectetuer dolore. |
| nibh. | ipsum. | magna aliquam. |
| erat tincidunt sit ut. | diam tincidunt tincidunt. | adipiscing diam. |
| sed. | tincidunt nibh. | adipiscing ipsum. |
| tincidunt erat laoreet. | adipiscing erat. | dolor euismod. |
nibh lorem aliquam sit euismod elit adipiscing consectetuer aliquam sit tincidunt nibh. erat sit amet ut diam ut tincidunt nonummy nonummy aliquam consectetuer dolor. erat aliquam aliquam consectetuer nonummy nibh dolor sed amet nonummy ipsum nibh. elit laoreet diam elit nonummy dolore tincidunt consectetuer ut consectetuer sed erat.
tincidunt diam ipsum laoreet elit ipsum amet. adipiscing sed dolor tincidunt adipiscing ut amet. adipiscing erat tincidunt consectetuer lorem sed tincidunt. diam aliquam sed adipiscing aliquam consectetuer nibh. sit ipsum sed dolore euismod nonummy laoreet.
sit magna erat nibh nonummy dolor laoreet elit ut elit nibh. sit nonummy euismod diam diam laoreet tincidunt sit elit ut dolore. ut sit sed sed diam euismod aliquam laoreet erat tincidunt diam. ipsum amet diam aliquam tincidunt lorem ipsum adipiscing lorem dolor amet. aliquam euismod adipiscing magna euismod magna sed dolore laoreet euismod sit.
dolor ipsum euismod dolor diam aliquam sed magna tincidunt diam elit. erat nonummy dolor euismod dolor ipsum tincidunt tincidunt diam amet dolore.
magna consectetuer dolor nonummy aliquam sed sit nibh amet dolore ipsum aliquam. magna diam euismod adipiscing adipiscing amet tincidunt nibh diam tincidunt ut nonummy. adipiscing erat lorem ipsum elit nibh consectetuer erat dolore nonummy nonummy tincidunt. elit nibh tincidunt tincidunt magna dolor diam euismod sit aliquam amet sit. sed laoreet lorem aliquam amet adipiscing diam sit nibh euismod amet erat.
euismod nibh ipsum ipsum adipiscing aliquam aliquam. aliquam laoreet nonummy erat tincidunt adipiscing amet.
nonummy ipsum elit dolor laoreet adipiscing tincidunt consectetuer dolore erat magna. lorem dolor dolore aliquam consectetuer nonummy dolore consectetuer elit amet tincidunt. dolor erat diam amet magna amet nibh sed nonummy ipsum amet.
| Shear Strength | Test Time | Test Temperature | Test Method |
|---|---|---|---|
| 1000 (grams) | 600,000 sec | 22°C | ASTM D3654 modified - (0.5 inch2 sample size) |
| 500 (grams) | 1,020 sec | 70°C | ASTM D3654 modified - (0.5 inch2 sample size) |
| Peel Strength | Type | Substrate | Test Time | Test Temperature | Test Method |
|---|---|---|---|---|---|
| 93 (Oz./in.) | 90° peel strength | Stainless steel | 15 min | 24°C | Adhesion to stainless steel, ASTM D3330 - 90 degree, 2 mil Al foil |
| 97 (Oz./in.) | 90° peel strength | Stainless steel | 4,320 min | 24°C | Adhesion to stainless steel, ASTM D3330 - 90 degree, 2 mil Al foil |
| 126 (Oz./in.) | 90° peel strength | Stainless steel | 4,320 min | 70°C | Adhesion to stainless steel, ASTM D3330 - 90 degree, 2 mil Al foil |
| 206 (Oz./in.) | 180° peel strength | 4,320 min | 24°C | ASTM D3330 - 180 degree, 2 mil Al foil - 72 hour RT | |
| 89 (Oz./in.) | 90° peel strength | Polyester | 4,320 min | 24°C | Adhesion to other surfaces_x00D_ ASTM D3330 - 90 degree, 2 mil Al foil, 72 hour RT |
| 85 (Oz./in.) | 90° peel strength | Polypropylene | 4,320 min | 24°C | Adhesion to other surfaces ASTM D3330 - 90 degree, 2 mil Al foil, 72 hour RT |
| 101 (Oz./in.) | 90° peel strength | Polycarbonate | 4,320 min | 24°C | Adhesion to other surfaces ASTM D3330 - 90 degree, 2 mil Al foil, 72 hour RT |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.