Application Type Bond, Hold 1 Part or 2 Part 1 Part Material Form Tape Substrate Metal, ABS, HDPE, Polycarbonate, Polyester, Polypropylene, Stainless Steel, Plastics Manufacturer 3M Chemistry Acrylic Cure Method Pressure-Sensitive Color Natural High Temperature Resistance (°C) 177, 93 Density (g/cm³) 1.012 (g/cc)
Technical Data for 3M 9500PC
Application Temperature (°F) 70 to 100
Peel Strength (piw) 71 (Oz./in.), 93 (Oz./in.), 121 (Oz./in.), 140 (Oz./in.), 74 (Oz./in.), 60 (Oz./in.), 44 (Oz./in.), 77 (Oz./in.), 33 (Oz./in.) Test Method Shear Strength (psi) 1000 (grams), 500 (grams) Test Method
UV Resistance Excellent High Temperature Resistance (°C) 177, 93 Test Method Moisture/Humidity Resistance Moisture/humidity resistance
Density (g/cm³) 1.012 (g/cc)
Shelf Life Details Store in original cartons at 70°F (21°C) and 50% relative humidity.;If stored under proper conditions, product retains its performance and properties for two years from date of manufacture. Shelf Life Temperature (°F) 70 Shelf Life Type from date of manufacture Shelf Life (mon) 24
Best Practices for 3M 9500PC
To obtain optimum adhesion, the bonding surfaces must be clean, dry and well unified. Some typical surface cleaning solvents are isopropyl alcohol or heptane.*
*Carefully read and follow the manufacturer’s precautions and directions for use when working with solvents.
Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm application pressure helps develop better adhesive contact and improves bond strength.
Ideal tape application temperature range is 70°F to 100°F (21°C to 38°C). Initial tape application to surfaces at temperatures below 50°F (10°C) is not recommended because the adhesive becomes too firm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory.
Comparable Materials for 3M 9500PC
Spec Engine® Results
Questions about this material?
Get personal assistance with your specific application needs.
Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of MaterialsRead Article
Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:Read Article
Shear Strength Test Methods
|Shear Strength||Test Time||Test Temperature||Test Method|
|1000 (grams)||600,000 sec||22°C||ASTM D3654 modified - (.5 inch2 sample size)|
|500 (grams)||600,000 sec||70°C||ASTM D3654 modified - (.5 inch2 sample size)|
Peel Strength Test Methods
|Peel Strength||Type||Substrate||Test Time||Test Temperature||Test Method|
|71 (Oz./in.)||90° Peel strength||Stainless steel||15 min||25°C||ASTM D3330 - 90 degree|
|93 (Oz./in.)||90° Peel strength||Stainless steel||4,320 min||25°C||ASTM D3330 - 90 degree|
|121 (Oz./in.)||90° Peel strength||Stainless steel||4,320 min||70°C||ASTM D3330 - 90 degree|
|140 (Oz./in.)||180° Peel strength||4,320 min||25°C||ASTM D3330 - 180 degree, 2 mil al foil|
|74 (Oz./in.)||90° Peel strength||ABS||4,320 min||25°C||ASTM D3330 - 90 degree, 2 mil al foil|
|60 (Oz./in.)||90° Peel strength||Polycarbonate(PC)||4,320 min||25°C||ASTM D3330 - 90 degree, 2 mil al foil|
|44 (Oz./in.)||90° Peel strength||Polypropylene (PP)||4,320 min||25°C||ASTM D3330 - 90 degree, 2 mil al foil|
|77 (Oz./in.)||90° Peel strength||Polyester (PET)||4,320 min||25°C||ASTM D3330 - 90 degree, 2 mil al foil|
|33 (Oz./in.)||90° Peel strength||High Density Polyethylene (HDPE)||4,320 min||25°C||ASTM D3330 - 90 degree, 2 mil al foil|
High Temperature Resistance Test Methods
|High Temperature Resistance||Test Method|
|177°C||Relative High Temperature Operating Ranges: Short Term (minutes, hours)|
|93°C||Relative High Temperature Operating Ranges: Long Term (days, weeks)|