3M Adhesive Transfer Tape 927 Datasheet 3M Adhesive Transfer Tape 927

Information provided by Gluespec
  • Description for 3M Adhesive Transfer Tape 927

    It offers excellent adhesion to a wide variety of surfaces, including low surface energy plastics and foam. This pressure sensitive medium firm acrylic adhesive features very high initial adhesion with good holding power.

    *See Terms of Use Below

    Chemical Resistance Chemical resistance, Chemical Resistance: Mild acids, Chemical Resistance: Fluid Resistance: Water resistance, Alkalis
    Application Type Bonding
    Material Form Transfer tape
    Substrate Metal, Low surface energy plastics, Polypropylene (PP), Stainless steel, Foam, Low surface energy plastics, ABS, Plastics
    Industry Electronic markets, medical markets, Long term bonding of graphic nameplates, Automotive markets, Aerospace markets, Nameplates
    Manufacturer 3M
    Chemistry Acrylic adhesive
    Cure Method Pressure sensitive, Heat, Room temperature
    Application Temperature (°F) 70 to 100
    Total Thickness (mm) 0.050
    Double Sided Double sided
    Carrier Thickness (mm) 0.051
    Liner Thickness (mm) 0.090
    Kraft Liner Type: 60# Densified Kraft
    Oil Resistance Oil
    High Temperature Resistance (°C) 70, 121, Heat resistance, <65
    Low Temperature Resistance (°C) -40
    Key Specifications This product is defined as an article under the Toxic Substances Control Act and therefore, it is exempt from inventory listing requirements, These products have been recognized by Underwriters Laboratories, Inc. under UL 969, Marking and Labeling Systems Materials Component., Mil-Spec (United States Military Standard): P-19834B: Meets Mil-P 19834B Type 1.
    Can Be Used In Conjunction With These Materials Lamination to foam for gasket application
    Tape Backing/Carrier Aluminum foil backing
  • Technical Data for 3M Adhesive Transfer Tape 927

    Overview
    • Chemical Resistance
      • Chemical Resistance : Fluid Resistance : Water Resistance
      • Chemical Resistance - Alkalis
      • Chemical Resistance : Acid Resistance - Mild acids
    • Application Type
    • Material Form
      • Tape - Transfer tape
    • Substrate
    • Industry
      • Sign - Nameplates
      • Automotive - Automotive markets
      • Aerospace - Aerospace markets
      • Electronics - Electronic markets
      • Industrial - Industrial equipment markets
      • Printing and Graphics - Long term bonding of graphic nameplates
      • Medical - medical markets
      • Appliances - Appliance markets
      • Other - Decorative trim parts, Long term bonding of overlays to surfaces, Bonding rating plates
    • Chemistry
    • Cure Method
      • Pressure Sensitive (min) - Pressure sensitive
      • Room Temperature / Air Dry - Room temperature
      • Heat
    • Key Specifications
      • TSCA (Toxic Substances Control Act) - This product is defined as an article under the Toxic Substances Control Act and therefore, it is exempt from inventory listing requirements
      • UL (Underwriters Laboratory), ULC (Underwriters Laboratories of Canada), NFPA (National Fire Protection Association) - These products have been recognized by Underwriters Laboratories, Inc. under UL 969, Marking and Labeling Systems Materials Component.
      • Mil-Spec (United States Military Standard) : P-19834B : Type 1 - Meets Mil-P 19834B Type 1.
    • Can Be Used In Conjunction With These Materials
      • Gaskets - Lamination to foam for gasket application
    • Tape Backing/Carrier
      • Metal Foil - Aluminum foil backing
    Specifications
    Cure Specs
    Application Temperature (°F) 70 to 100
    Bond Strength
    General Bond Strength (psi) Excellent adhesion, Very high initial adhesion, Good holding power
    Peel Strength (piw) 5.7 (N/cm), 3.4 (N/cm), 4.9 (N/cm), 59 (oz/in), 3.7 (N/cm), 5.7 (N/cm) Test Method
    Tape Properties
    Total Thickness (mm) 0.050
    Double Sided Double sided
    Carrier Thickness (mm) 0.051
    Liner Thickness (mm) 0.090
    Material Resistance
    Oil Resistance Oil
    UV Resistance U.V. resistance
    High Temperature Resistance (°C) 70, 121, Heat resistance, <65 Test Method
    Low Temperature Resistance (°C) -40 Test Method
    Moisture/Humidity Resistance Humidity resistance
    Conductivity
    Dissipation Factor
    Dielectric Strength (V/mil) 340 Test Method
    Dielectric Constant 3.21 Test Method
    Hardness
    Flexibility Excellent process flexibility, Medium firm
    Other Properties
    Coefficient of Thermal Expansion (CTE) 58e-5 (m/m/°C), ASTM D696 Test Method
    Business Information
    Shelf Life Details It is suggested that products are stored at room temperature conditions of 70°F (21°C) and 50% relative humidity.; If stored properly, product retains its performance and properties for 24 months from date of manufacture.
    Shelf Life Temperature (°F) 70
    Shelf Life Type From date of manufacture
    Shelf Life (mon) 24
  • Best Practices for 3M Adhesive Transfer Tape 927

    *See Terms of Use Below

    1. Surface Preparation

      For maximum bond strength (during installation of the final part) the surface should be thoroughly cleaned and dried. Typical cleaning solvents are heptane (for oily surfaces) or isopropyl alcohol for plastics. Use reagent grade solvents since common household materials like rubbing alcohol frequently contain oils to minimize the drying effect on skin These oils can interfere with the performance of a pressure-sensitive adhesive.

    2. Application

      The ideal adhesive application temperature range is 70°F (21°C) to 100°F (38°C).

      Once properly applied, at the recommended application temperature, low temperature holding is generally satisfactory (please refer to the Typical Physical Properties and Performance Characteristics section).

    3. Curing

      It is necessary to provide pressure during lamination (1.5-20 PLI recommended) and during final part installation (10-15 PLI) to allow to adhesive the come into direct contact with the substrate. Using a hard edged plastic tool, which is the full width of the laminated part, helps to provide the necessary pressure at the point of lamination. Heat can increase bond strength when bonding to metal parts (generally this same increase is observed at room temperature over longer times, weeks). For plastic parts, the bond strength is not enhanced with the addition of heat.

  • Comparable Materials for 3M Adhesive Transfer Tape 927

    *See Terms of Use Below

    Spec Engine® Results

Popular Articles

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Plastic Bonding with Adhesives - Considerations Q&A

Read Article

Testing the effectiveness of surface treatments

Read Article

What Projects Require Custom Adhesive Formulations and Why?

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for 3M Adhesive Transfer Tape 927

Gluespec Poll

Who do you read or follow for engineering news and entertainment?
Peel Strength Test Methods
Peel Strength Cure Time Cure Temperature Substrate Test Method
5.7 (N/cm) 15 min 23°C Stainless steel 90° Peel adhesion, ASTM D3330, Dwell, Environmental Condition: 50%RH, Backing: 2 mil Aluminum foil, Notes: 12 in/min (300 mm/min)
3.4 (N/cm) 15 min 23°C ABS 90° Peel adhesion, ASTM D3330, Dwell, Environmental Condition: 50%RH, Backing: 2 mil Aluminum foil, Notes: 12 in/min (300 mm/min)
4.9 (N/cm) 15 min 23°C Polypropylene (PP) 90° Peel adhesion, ASTM D3330, Dwell, Environmental Condition: 50%RH, Backing: 2 mil Aluminum foil, Notes: 12 in/min (300 mm/min)
59 (oz/in) 4,320 min 23°C Stainless steel 90° Peel adhesion, ASTM D3330, Dwell, Environmental Condition: 50%RH, Backing: 2 mil Aluminum foil, Notes: 12 in/min (300 mm/min)
3.7 (N/cm) 4,320 min 23°C ABS 90° Peel adhesion, ASTM D3330, Dwell, Environmental Condition: 50%RH, Backing: 2 mil Aluminum foil, Notes: 12 in/min (300 mm/min)
5.7 (N/cm) 4,320 min 23°C Polypropylene (PP) 90° Peel adhesion, ASTM D3330, Dwell, Environmental Condition: 50%RH, Backing: 2 mil Aluminum foil, Notes: 12 in/min (300 mm/min)
High Temperature Resistance Test Methods
High Temperature Resistance Test Method
70°C Long term temperature resistance
121°C Short term temperature resistance
Heat resistance
<65°C For intermittent longer periods (days, weeks)
Low Temperature Resistance Test Methods
Low Temperature Resistance Test Method
-40°C Lower temperature service limit
Dielectric Constant Test Methods
Dielectric Constant Temperature Test Method
3.21 23°C ASTM D150, 1KHz
Dielectric Strength Test Methods
Dielectric Strength Test Method
340 V/mil ASTM D149
Coefficient of Thermal Expansion (CTE) Test Methods
Coefficient of Thermal Expansion (CTE) CTE Test Method
58e-5 (m/m/°C) ASTM D696
ASTM D696 20e-5 (m/m/°C)