3M CA40H Datasheet 3M CA40H

CONTACT REP
Information provided by Gluespec

  • Description for 3M CA40H

    Higher viscosity version of CA40 • Better void filling capabilities.

    *See Terms of Use Below

    Application Type Bond, Adhesive: Instant Adhesives
    1 Part or 2 Part 1-Part
    Material Form Liquid
    Substrate Aluminum- Etched, Metal, Plastic, Vinyl, EPDM Rubber, Rubber, Steel, Aluminum
    Manufacturer 3M
    Chemistry Cyanoacrylate, Ethyl
    Cure Method Moisture
    Cure Temperature (°C) 20 to 25 Room Temperature
    Viscosity (cPs) Non-sag, High, 400 to 600
    Color Clear, Colorless
    High Temperature Resistance (°C) 82
    Low Temperature Resistance (°C) -54
    Density (g/cm³) 8.7 (weight (lbs/gal))

  • Technical Data for 3M CA40H

    *See Terms of Use Below

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 1-Part
    • Material Form
      • Liquid
    • Substrate
    • Chemistry
    • Cure Method
      • Moisture / Condensation Cure - Moisture
    • Color
      • Clear / Transparent - Clear, Colorless
    Specifications
    Cure Specs
    Cure Temperature (°C) 20 to 25 Room Temperature
    Viscosity (cPs) Non-sag, High, 400 to 600 Test Method
    Fixture or Handling Strength Time (min) 0.08 to 0.67 Test Method
    Set Time (min) Slow
    Bond Strength
    General Bond Strength (psi) High
    Shear Strength (psi) 1,500, 1,500, 900, 1,000 Test Method
    Material Resistance
    High Temperature Resistance (°C) 82 Test Method
    Low Temperature Resistance (°C) -54 Test Method
    Hardness
    Flexibility Flexible
    Other Properties
    Specific Gravity 1.050 Test Method
    Density (g/cm³) 8.7 (weight (lbs/gal)) Test Method
    Business Information
    Shelf Life Details Store in original containers at or below 80°F (27°C).;These products can be expected to have at least nine months shelf life. At lower temperature, the shelf life will be longer. Lower temperatures cause increased viscosity of a temporary nature and also will cause water to condense on the container. Therefore, containers stored at low temperatures should be allowed to return to room temperature before opening so that water does not come in contact with the adhesive and cause adhesive gelation.
    Shelf Life Temperature (°F) <81
    Shelf Life (mon) >9

  • Best Practices for 3M CA40H

    *See Terms of Use Below

    1. Surface Preparation

      For optimum strength structural bonds, paint, oxide films, oils, dust, mold release agents and all other surface contaminants must be completely removed. However, the amount of surface preparation depends on the required bond strength and the environmental aging resistance desired by the user.

      See Vendor Technical Data sheet for more information

  • Comparable Materials for 3M CA40H

    *See Terms of Use Below

    Spec Engine® Results

    • PermaBond
      940(PermaBond)

      A low odour, non-fogging, nonfrosting alkoxyethyl cyanoacrylate. The reduced odour improves worker comfort. Unsightly fogging adjacent to bondlines, common with other cyanoacrylate adhesives on hot and humid days, is eliminated.

    • PermaBond
      941(PermaBond)

      A low odour, non-fogging, non-frosting alkoxyethyl cyanoacrylate, bonds most materials, 100% reactive, no solvents.

    • Compare All

    Closest Results from this Manufacturer

    • 3M
      CA5(3M)

      Higher viscosity, slower setting version ethyl of CA4 for filling gaps • Meets CID A-A-3097, Type II, Class 3

    • 3M
      CA7(3M)

      Very fast setting • Excellent adhesion to metals, plastics, and rubbers

    • 3M
      CA8(3M)

      Slower setting than CA7 • Excellent adhesion to metals, plastics and rubbers • Meets CID A-A-3097, Type II, Class 2

    • Compare All
  Download Technical Data Sheet   Save This Material   Compare View Saved Items

Popular Articles

Cyanoacrylate 202

Read Article

Cyanoacrylate 101

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Testing the effectiveness of surface treatments

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for 3M CA40H

All 3M Materials
View Now

Gluespec Poll

Who do you read or follow for engineering news and entertainment?
Fixture or Handling Strength Time Test Methods
Fixture or Handling Strength Time Fixture-Handling Strength Test Method
0.08 to 0.67 min Cured
Viscosity Test Methods
Viscosity Test Method
Non-sag
High
400 to 600 cPs Uncured
Shear Strength Test Methods
Shear Strength Type Cure Time Cure Temperature Cure Humidity Substrate Test Temperature Test Method
1,500 psi Overlap shear strength 2,880 min 20°C 60 % Steel 23°C Overlap Shear Metal to Metal Bond Strength tested @ 75°F (23°C), Tensile Shear Strength (as defined in ASTM-D-1002) - cured 48 hours at 68°F (20°C) - 60% Relative Humidity - abraded and acetone wiped - test specimen is 1/2 sq. in. bond tested @ .1 in./minute loading rate.
1,500 psi Overlap shear strength 2,880 min 20°C 60 % Aluminum-etched 23°C Overlap Shear Metal to Metal Bond Strength tested @ 75°F (23°C), Tensile Shear Strength (as defined in ASTM-D-1002) - cured 48 hours at 68°F (20°C) - 60% Relative Humidity - abraded and acetone wiped - test specimen is 1/2 sq. in. bond tested @ .1 in./minute loading rate.
900 psi Overlap shear strength 2,880 min 20°C 60 % ABS (Substrate failure) 23°C Overlap Shear Metal to Metal Bond Strength tested @ 75°F (23°C), Substrate Failure, Tensile Shear Strength (as defined in ASTM-D-1002) - cured 48 hours at 68°F (20°C) - 60% Relative Humidity - abraded and acetone wiped - test specimen is 1/2 sq. in. bond tested @ .1 in./minute loading rate.
1,000 psi Overlap shear strength 2,880 min 20°C 60 % PVC (Substrate failure) 23°C Overlap Shear Metal to Metal Bond Strength tested @ 75°F (23°C), Substrate Failure, Tensile Shear Strength (as defined in ASTM-D-1002) - cured 48 hours at 68°F (20°C) - 60% Relative Humidity - abraded and acetone wiped - test specimen is 1/2 sq. in. bond tested @ .1 in./minute loading rate.
High Temperature Resistance Test Methods
High Temperature Resistance Test Method
82°C Uncured
Low Temperature Resistance Test Methods
Low Temperature Resistance Test Method
-54°C Uncured
Density Test Methods
Density Test Method
8.7 (weight (lbs/gal)) Uncured
Specific Gravity Test Methods
Specific Gravity Test Method
1.050 Uncured