3M Double Coated Removable Foam Tape 4658F Datasheet 3M Double Coated Removable Foam Tape 4658F

Information provided by Gluespec
  • Description for 3M Double Coated Removable Foam Tape 4658F

    It is is a clear, double coated acrylic foam tape that removes cleanly from many surfaces, firm acrylic adhesive, high ultimate bond strength, good temperature resistance, solvent resistance and static shear holding power.

    *See Terms of Use Below

    Chemical Resistance Chemical Resistance: Good solvent resistance, Chemical Resistance: Hydrocarbon solvents
    Application Type Bond, Hold
    Material Form Tape: Foam Tape
    Substrate Fabric, Highly polished wood, Stainless Steel, Blown vinyl, Foam, Cloth, Wood veneers
    Industry Electronic, Holding Electronic Accessories, Nameplates, Display Case, Signs, Dispensers, Point of Purchase and other Displays
    Manufacturer 3M
    Chemistry Acrylic
    Cure Method Pressure Sensitive
    Application Temperature (°F) 70 to 100
    Color Clear
    Total Thickness (mm) 0.787
    Double Sided Double Coated
    High Temperature Resistance (°C) 100, 79, Good temperature resistance
    Density (g/cm³) 0.960
  • Technical Data for 3M Double Coated Removable Foam Tape 4658F

    Overview
    • Chemical Resistance
      • Chemical Resistance : Relative Solvent Resistance - Good solvent resistance, Hydrocarbon solvents
    • Application Type
    • Material Form
      • Tape : Foam Tape
    • Substrate
      • Foam
      • Vinyl - Blown vinyl
      • Wood - Highly polished wood, Wood veneers
      • Fabric - Cloth
      • Stainless Steel
      • Other - Many surfaces, Wallpaper, Painted plaster board
    • Industry
      • Displays - Display Case, Point of Purchase and other Displays
      • Sign - Signs
      • Electronics - Electronic, Dispensers, Holding Electronic Accessories
      • Printing and Graphics - Nameplates
      • Other - Smoke Alarms, Picture Frame Tabs, Air Fresheners, Exhibitions
    • Chemistry
    • Cure Method
      • Pressure Sensitive (min) - Pressure Sensitive
    • Color
      • Clear / Transparent - Clear
    Specifications
    Cure Specs
    Application Temperature (°F) 70 to 100
    Bond Strength
    General Bond Strength (psi) High Ultimate
    Peel Strength (piw) 26.3 N/cm, 240 oz/in Test Method
    Shear Strength (psi) Static shear Holding, 1000 (g), 750 (g), 500 (g) Test Method
    Tape Properties
    Total Thickness (mm) 0.787
    Double Sided Double Coated
    Tape Backing Polyester
    Material Resistance
    UV Resistance Excellent
    High Temperature Resistance (°C) 100, 79, Good temperature resistance Test Method
    Other Properties
    Density (g/cm³) 0.960
    Business Information
    Shelf Life Details Product retains its performance and properties for 24 months from date of manufacture when stored in original cartons at 70°F (21°C) and 50% relative humidity.
    Shelf Life Temperature (°F) 70
    Shelf Life Type From date of manufacture
    Shelf Life (mon) 24
  • Best Practices for 3M Double Coated Removable Foam Tape 4658F

    *See Terms of Use Below

    1. Surface Preparation

      To obtain optimum adhesion, the bonding surfaces must be clean, dry and well unified.

      Typical surface cleaning solvents are isopropyl alcohol (rubbing alcohol) and water or heptane.

      Note: Carefully read and follow manufacturer’s precautions and directions for use when using solvents.

    2. Application

      Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm application pressure helps develop better adhesive contact and improve bond strength.

      Ideal tape application temperature is 70°F to 100°F (21°C to 38°C). Initial tape application to surfaces at temperatures below 50°F (10°C) is not recommended because the adhesive may become too firm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory.

    3. Removal

      For rigid surfaces, lever or pry apart the substrates to break the bond.

      For flexible surfaces, peel back slowly to ensure clean removal.

      To remove tape from substrate, pull back corner and peel off quickly

      Removable

  • Comparable Materials for 3M Double Coated Removable Foam Tape 4658F

    *See Terms of Use Below

    Spec Engine® Results

Popular Articles

Testing the effectiveness of surface treatments

Read Article

What Projects Require Custom Adhesive Formulations and Why?

Read Article

Plastic Bonding with Adhesives - Considerations Q&A

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for 3M Double Coated Removable Foam Tape 4658F

Gluespec Poll

Who do you read or follow for engineering news and entertainment?
Peel Strength Test Methods
Peel Strength Type Substrate Test Time Test Temperature Test Method
26.3 N/cm 90° Peel strength Stainless steel 4,320 min 23°C 12 in/min (300 mm/min) ASTM D3330 72 hour dwell on Stainless Steel at 23°C (72°F) and 50% RH Backing: 2 mil Polyester
240 oz/in 90° Peel Adhesion Stainless Steel 4,320 min 23°C ASTM D3330 ,12 in/min (300 mm/min), 50%RH,2 mil PET
Shear Strength Test Methods
Shear Strength Type Test Time Test Temperature Test Method
Static shear Holding
1000 (g) Static shear strength 600,000 sec 22°C Room Temperature ASTM D3654, 1/2 in x 1 in sample size
750 (g) Static shear strength 600,000 sec 49°C ASTM D3654, 1/2 in x 1 in sample size
500 (g) Static shear strength 600,000 sec 70°C ASTM D3654, 1/2 in x 1 in sample size
High Temperature Resistance Test Methods
High Temperature Resistance Test Method
100°C Short Term Temperature Resistance
79°C Long Term Temperature Resistance
Good temperature resistance