| Application Type | Bond |
|---|---|
| 1 Part or 2 Part | 2 Part |
| Material Form | Liquid, Non-sag liquid(after mixing) |
| Substrate | Ceramic, Glass, Metal, ABS, PVC, Wood, Concrete, Aluminum, Cold Rolled Steel, Nylon, Polycarbonate, Acrylic, Plastic, Rigid PVC, Aluminum (Etched) |
| Industry | Custom tapping of bolts and screws into wood |
| Manufacturer | 3M |
| Chemistry | Polyurethane |
| Cure Method | 2 Parts |
| Cure Temperature (°C) | 25 Room Temperature |
| Cure Time (min) | 60 |
| Viscosity (cPs) | Non-sag, <250,000, Self-Leveling |
| Color | Gray |
| High Temperature Resistance (°C) | 121 |
| Low Temperature Resistance (°C) | -51 |
Remove all loose aggregate, dust, old caulks, grease and waterproofing compounds from repair surface. (Grind away any absorbed oils to ensure a clean surface.) Clean repair surface with a bristle brush and use moisture and oil-free compressed air to blow out debris. Mask off area surrounding repair.
Automatically mixed through a mixing tip
Remove masking tape from repair. Shave or grind cured product with 36 grit sandpaper to achieve desired shape. Sand with 80 grit sandpaper to remove any scratches. If 3M™ Scotch-Weld™ Urethane Adhesive DP-601NS is applied in a traffic area, apply sand or some type of grip to repaired surface area.
| nonummy. | ut diam sed. | dolor lorem. |
|---|---|---|
| nonummy. | sed dolor. | dolor nonummy. |
| elit dolore ipsum. | ipsum elit. | magna. |
| euismod euismod amet sit. | magna magna. | amet. |
| ut. | erat. | consectetuer sit. |
| consectetuer. | lorem. | nibh. |
| aliquam amet elit erat. | nibh ut. | aliquam magna. |
| aliquam ut. | nibh adipiscing ipsum. | ipsum magna. |
| ipsum elit diam dolore. | sit. | tincidunt. |
|---|---|---|
| dolore tincidunt. | aliquam. | nonummy dolore. |
| ut dolore dolore. | adipiscing magna adipiscing. | magna. |
| elit. | sed diam. | aliquam. |
| consectetuer diam. | diam elit euismod. | aliquam aliquam. |
| laoreet adipiscing ipsum amet. | tincidunt euismod nonummy. | sit. |
|---|---|---|
| tincidunt nibh ipsum. | diam dolor. | magna. |
| dolor tincidunt laoreet. | nonummy. | dolor elit. |
| laoreet tincidunt. | sit ipsum dolor. | ipsum elit. |
| dolor adipiscing tincidunt aliquam. | euismod. | dolore lorem. |
| dolore erat sed tincidunt. | nibh ipsum. | erat. |
| elit ipsum elit euismod. | nonummy amet dolor. | consectetuer sed. |
|---|---|---|
| nibh erat dolor. | euismod euismod. | sit. |
| ipsum diam magna ipsum. | euismod lorem dolore. | adipiscing. |
laoreet lorem nibh amet tincidunt adipiscing ipsum. erat dolore lorem euismod laoreet nonummy erat. magna laoreet nibh adipiscing ipsum lorem sed.
sed adipiscing laoreet sed aliquam sit dolore consectetuer. lorem tincidunt adipiscing lorem consectetuer laoreet erat ut.
laoreet ut sed dolore diam magna adipiscing laoreet adipiscing nibh euismod. ipsum euismod sit adipiscing laoreet magna euismod magna diam dolore adipiscing. elit adipiscing lorem laoreet tincidunt euismod adipiscing sit adipiscing euismod diam.
ipsum elit magna consectetuer adipiscing adipiscing. adipiscing dolore erat erat lorem sed. elit dolor dolore ut sit tincidunt. sed sit consectetuer lorem nibh consectetuer.
| Cure Temperature | Cure Time Test Method |
|---|---|
| 25°C Room Temperature | Cured, PEC,Conditions 10 g, 1/4" thick @ 77°F 25°C |
| Cure Time | Test Method |
|---|---|
| 60 min | Cured, PEC,Conditions 10 g, 1/4" thick @ 77°F 25°C |
| Tack Free Time | Tack Free Temperature | Test Method |
|---|---|---|
| 2.00 min | 25°C Room Temperature | Cured, PEC 10 g, 1/4" thick @ 77°F (25°C) |
| Work / Pot Time | Test Method | Temperature |
|---|---|---|
| 0.83 min | Uncured, PEC, 10 g, 1/4" thick @ 77°F (25°C) | 23°C |
| Shear Strength | Type | Substrate | Test Time | Test Temperature | Test Method |
|---|---|---|---|---|---|
| 2,300 psi | OverLap Shear Strength | 25°C | ASTM D1002-72 | ||
| 2,550 psi | OverLap Shear Strength | Aluminum | -40°C | ASTM D1002 | |
| 2,300 psi | OverLap Shear Strength | Aluminum | 23°C | ASTM D1002 | |
| 670 psi | OverLap Shear Strength | Aluminum | 900 sec | 82°C | ASTM D1002 |
| 2,300 psi | OverLap Shear Strength | Aluminum | 23°C | (ASTM D1002), MEK/abrade/MEK | |
| 1,190 psi | OverLap Shear Strength | Cold Rolled Steel | 23°C | (ASTM D1002), MEK/abrade/MEK | |
| 300 psi | OverLap Shear Strength | Nylon | 23°C | (ASTM D1002), IPA/abrade/IPA | |
| 480 psi | OverLap Shear Strength | Polycarbonate | 23°C | (ASTM D1002), IPA/abrade/IPA | |
| 470 psi | OverLap Shear Strength | Acrylic | 23°C | (ASTM D1002), IPA/abrade/IPA | |
| 370 psi | OverLap Shear Strength | SMC | 23°C | (ASTM D1002), IPA/abrade/IPA | |
| 450 psi | OverLap Shear Strength | Rigid PVC | 23°C | (ASTM D1002), IPA/abrade/IPA | |
| 500 psi | OverLap Shear Strength | ABS | 23°C | (ASTM D1002), IPA/abrade/IPA | |
| 380 psi | OverLap Shear Strength | HIPS | 23°C | (ASTM D1002), IPA/abrade/IPA |
| Peel Strength | Type | Substrate | Test Temperature | Test Method |
|---|---|---|---|---|
| 9 piw | Floating Roller Peel | Aluminum (Etched) | 23°C | ASTM D3167 |
| High Temperature Resistance | Test Method |
|---|---|
| 121°C | Cured |
| Low Temperature Resistance | Test Method |
|---|---|
| -51°C | Cured |
| Environmental Resistance | Test Method |
|---|---|
| Environmental Resistance | Aluminum (Etched), Measured by Overlap Shear Tested @ 73°F (23°C) (PSI) (ASTM D1002) |
| Shore D Hardness | Shore Hardness Test Method | Hardness Temperature |
|---|---|---|
| 70 | After Cure, ASTM D2240-91, 1 hour at 77°F (25°C) | 25°C Room Temperature |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.