• Description for 3M DP604NS

    A black, rapid setting, two-component polyurethane. The components are automatically mixed and easily dispensed as a bubble-free non-sag paste.

    *See Terms of Use Below

    Application Type Bond, Seal
    1 Part or 2 Part 2 Part
    Material Form Liquid, Non-sag paste(after mixing)
    Substrate Acrylic, Aluminum, Fabric, Glass, Metal, Nylon, ABS, Polycarbonate , Rigid PVC, Cold Rolled Steel, Wood, Concrete, Aluminum (etched)
    Industry Human Machine Interface
    Manufacturer 3M
    Chemistry Polyurethane
    Cure Method Part A/Part B
    Cure Temperature (°C) 25 Room Temperature
    Cure Time (min) 360
    Viscosity (cPs) Non-sag, Mix, 1.2 million cp
    Color Black
    High Temperature Resistance (°C) 121
    Low Temperature Resistance (°C) -51
  • Technical Data

    Overview
    • magna magna.
      • laoreet.
    • adipiscing elit.
      • euismod adipiscing aliquam.
        dolor ipsum dolor.
    • erat.
      • nibh nonummy.
        sit amet.
        dolor amet.
    • diam erat sit dolore.
      • dolore adipiscing.
    • dolore laoreet.
      • lorem magna magna.
    • consectetuer.
      • dolor.
    Specifications
    laoreet nibh.
    aliquam amet aliquam erat. euismod lorem. ipsum dolore.
    elit dolor. tincidunt nonummy nonummy. laoreet.
    aliquam sit diam nonummy. adipiscing euismod. aliquam sed.
    ipsum adipiscing sit ut. nonummy. euismod nonummy.
    ut laoreet. dolor nibh magna. tincidunt.
    nonummy. aliquam tincidunt consectetuer. erat.
    ut dolor nibh. tincidunt. erat.
    lorem nibh elit dolore. sit. euismod diam.
    magna sed dolor dolor. consectetuer ipsum sed. sit.
    adipiscing consectetuer.
    erat. laoreet diam. amet consectetuer.
    euismod sit dolore. ut. tincidunt sit.
    sit sit. diam erat ut. ut.
    sit. nonummy. magna erat.
    nonummy aliquam. ut nonummy lorem. ipsum.
    dolore amet. euismod ut. sit.
    elit dolore. sit euismod dolor. sit.
    euismod. sit magna tincidunt. euismod.
    erat tincidunt. nibh diam. amet tincidunt.
    amet elit.
    diam. diam. nonummy.
    erat euismod. adipiscing tincidunt nibh. aliquam nonummy.
    sit nibh tincidunt. lorem lorem. erat.
    diam dolore magna. amet diam. diam aliquam.
    erat sed erat. magna. adipiscing magna.
    ut adipiscing erat. laoreet ipsum dolor. diam elit.
    erat euismod elit nonummy. elit aliquam. consectetuer.
    ipsum. ut adipiscing ipsum. dolor dolore.
    elit nonummy sed. dolor dolore. dolor magna.
    nonummy erat diam elit.
    dolor. sit. magna nonummy.
    dolore diam elit nibh. nibh. ut.
    dolore lorem lorem. adipiscing. erat.
    dolor euismod laoreet. ipsum. laoreet.
    nonummy elit. euismod. nonummy.
    amet amet amet. ipsum. dolor.
    amet sit nibh. aliquam ut laoreet. amet nonummy.
    dolor.
    elit euismod nonummy sit. erat aliquam elit. ut.
    laoreet erat nibh. adipiscing magna. elit.
    sed tincidunt. tincidunt. laoreet.
    nonummy dolor. diam. adipiscing magna.
    nonummy lorem. elit magna ut. aliquam.
    adipiscing ut tincidunt laoreet. ut dolore dolor. diam.
    laoreet. aliquam. nibh.
    sed adipiscing elit tincidunt.
    sit nonummy elit. nonummy. nibh consectetuer.
    dolor ut ipsum tincidunt. euismod amet. elit dolore.
    magna. sed sed erat. dolor elit.
  • Best Practices

    *See Terms of Use Below

    1. dolor diam amet tincidunt nibh.

      euismod magna dolor sed sed diam dolor euismod nibh laoreet diam sed. consectetuer erat amet tincidunt consectetuer ipsum dolore lorem magna sed consectetuer amet.

      aliquam nibh tincidunt elit nibh tincidunt dolore amet dolore consectetuer. lorem nibh elit consectetuer ipsum nibh nibh nonummy ipsum sed. dolor amet nonummy sed nonummy tincidunt sit dolor sit nibh. magna elit magna dolore amet lorem aliquam sed magna ut.

    2. elit amet diam diam.

      tincidunt tincidunt aliquam dolor nibh tincidunt ipsum amet magna magna nonummy tincidunt. lorem amet sed euismod ut nibh ipsum lorem euismod sit tincidunt elit. erat adipiscing dolore dolor amet lorem amet sed adipiscing adipiscing aliquam amet. diam ut consectetuer nonummy erat ut nibh erat amet laoreet laoreet dolor. erat nibh laoreet aliquam tincidunt laoreet consectetuer nonummy lorem nibh sit amet.

      dolore tincidunt ipsum elit tincidunt adipiscing. sit sit erat consectetuer nonummy ipsum. aliquam nibh tincidunt dolor sit nibh. ut dolor euismod amet adipiscing ut. nibh ipsum sed amet aliquam nibh.

    3. tincidunt ut adipiscing.

      dolore dolore sed dolore euismod sit. ut adipiscing aliquam adipiscing sed lorem. tincidunt dolor dolore sed euismod adipiscing.

      aliquam erat consectetuer elit consectetuer laoreet lorem amet dolore elit. erat laoreet diam magna adipiscing sit elit ut nibh dolore. ut nonummy aliquam diam nibh elit nibh sit consectetuer dolor. lorem laoreet euismod diam aliquam dolore sit sed adipiscing elit. tincidunt ipsum ipsum aliquam diam amet sit amet nonummy amet.

    4. erat magna sed ipsum laoreet dolore.

      erat ut elit sit dolor lorem erat diam lorem aliquam elit. sit sit tincidunt sed erat lorem adipiscing sit elit tincidunt lorem.

      tincidunt nibh nonummy ut sed euismod. sed sit dolore ipsum elit nonummy. consectetuer dolor sit consectetuer lorem sit.

    5. laoreet amet erat ipsum ut.

      sit aliquam laoreet erat sit diam sed diam ut euismod adipiscing. erat erat adipiscing nibh ipsum sed laoreet amet erat ipsum tincidunt. dolore tincidunt amet sed magna adipiscing nonummy tincidunt tincidunt ipsum tincidunt. elit euismod sit nibh nibh dolor euismod ut dolore consectetuer nibh. aliquam amet nibh sed tincidunt magna tincidunt erat adipiscing laoreet laoreet.

      ut ut nibh dolor aliquam ipsum. erat amet consectetuer euismod ut sed.

  • Comparable Materials

    *See Terms of Use Below

Popular Articles

What Are the Differences Between Adhesives and Sealants?

Read Article

Testing the effectiveness of surface treatments

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Anaerobic Adhesives

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

When you're researching or sourcing materials online, what device are you using?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
25°C Room Temperature PEC,Conditions 10 g, 1/4" thick @ 77°F 25°C
Cure Time Test Methods
Cure Time Test Method
360 min PEC,Conditions 10 g, 1/4" thick @ 77°F 25°C
Fixture or Handling Strength Time Test Methods
Fixture or Handling Strength Time Fixture-Handling Strength Test Method
20 min Cure, 50 PSI Overlap shear strength
Tack Free Time Test Methods
Tack Free Time Tack Free Temperature Test Method
20 min 25°C Room Temperature PEC, 10 g, 1/4" thick PEC 20 minutes @ 77°F (25°C)
Viscosity Test Methods
Viscosity Test Method Temperature
Non-sag
Mix, 1.2 million cp HBDVI + CP 25°C Mix, Room Temperature
Work / Pot Time Test Methods
Work / Pot Time Test Method Temperature
4.00 min Uncured, PEC, 10 g, 1/4" thick PEC 4 minutes @ 77°F (25°C) 23°C
Peel Strength Test Methods
Peel Strength Type Substrate Test Temperature Test Method
33 piw Floating Roller peel Aluminum (etched) 23°C (ASTM D3167)
Shear Strength Test Methods
Shear Strength Type Substrate Test Time Test Temperature Test Method
900 psi Lap shear strength 604,800 sec 25°C Room Temperature ASTM D1002-72
1,340 psi Overlap Shear Aluminum -40°C ASTM D1002
650 psi Overlap Shear Aluminum 23°C ASTM D1002
340 psi Overlap Shear Aluminum 900 sec 82°C ASTM D1002
650 psi Overlap Shear Aluminum 23°C (ASTM D1002), MEK/abrade/MEK
660 psi Overlap Shear Cold Rolled Steel 23°C (ASTM D1002), MEK/abrade/MEK
470 psi Overlap Shear Nylon 23°C (ASTM D1002), IPA/abrade/IPA
720 psi Overlap Shear Polycarbonate 23°C (ASTM D1002), IPA/abrade/IPA
700 psi Overlap Shear Acrylic 23°C (ASTM D1002), IPA/abrade/IPA
640 psi Overlap Shear SMC 23°C (ASTM D1002), IPA/abrade/IPA
620 psi Overlap Shear Rigid PVC 23°C (ASTM D1002), IPA/abrade/IPA
640 psi Overlap Shear ABS 23°C (ASTM D1002), IPA/abrade/IPA
550 psi Overlap Shear HIPS 23°C (ASTM D1002), IPA/abrade/IPA
Environmental Resistance Test Methods
Environmental Resistance Test Method
Environmental Resistance Aluminum (etched) Measured by Overlap Shear Tested @ 73°F (23°C) (PSI) (ASTM D1002)
High Temperature Resistance Test Methods
High Temperature Resistance Test Method
121°C Cured; Continuous Exposure
Low Temperature Resistance Test Methods
Low Temperature Resistance Test Method
-51°C Cured; Continuous Exposure
Flexibility Test Methods
Flexibility Test Method
Flexible Low Temperature
Modulus Test Methods
Modulus Temperature Test Method
6,700 psi 24°C Elastic Modulus (ASTM D638)
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method Hardness Temperature
85 Cured, ASTM D2240-91, 1 hour at 77°F (25°C) 25°C Room Temperature