3M DP8005 Translucent Datasheet 3M DP8005 Translucent

Information provided by Gluespec
  • Description for 3M DP8005 Translucent

    Acrylic bonds low surface energy polyolefins without surface preparation • Excellent environmental resistance • 2-3 hour handling strength

    *See Terms of Use Below

    Chemical Resistance Very good, Chemical Resistance: Fluid Resistance: Excellent water resistance, Chemical Resistance: Fluid Resistance: Salt Water
    Application Type Bond
    1 Part or 2 Part 2-Part
    Material Form Liquid
    Substrate Acrylic (PMMA), Aluminum, Glass, Fiber Reinforced plastic, Polycarbonate, Polypropylene, Wood, PolyEthylene, HDPE, ThermoPlastic Elastomers
    Industry Commercial & Specialty Vehicles
    Manufacturer 3M
    Chemistry Acrylic, Amine, Solvent-Free, Methacrylate
    Cure Method Base/Accelerator
    Cure Temperature (°C) 20 to 25, 23
    Cure Time (min) 480 to 1,440
    Color Yellow
    High Temperature Resistance (°C) 82
    Low Temperature Resistance (°C) -29
    Density (g/cm³) 8 to 8.4 (lbs/gal), 8.75 to 9.15 (lbs/gal)
  • Technical Data for 3M DP8005 Translucent

    Overview
    • Chemical Resistance
      • Chemical Resistance : Fluid Resistance : Water Resistance - Excellent water resistance, Salt Water
      • Chemical Resistance - Very good
    • Application Type
    • 1 Part or 2 Part
      • 2-Part
    • Material Form
      • Liquid
    • Substrate
    • Industry
      • Commercial & Specialty Vehicles
    • Chemistry
    • Cure Method
      • 2-Part Cure - Base/Accelerator
    • Color
      • Yellow
    Specifications
    Cure Specs
    Cure Temperature (°C) 20 to 25, 23
    Cure Time (min) 480 to 1,440
    Fixture or Handling Strength Time (min) 120 to 180 Test Method
    Work / Pot Time (min) 2.50 to 3.00 Test Method
    Mix Ratio 10:1 (by volume), 9.16:1 (by weight)
    Bond Strength
    Structural/Load-Bearing Structural
    Peel Strength (piw) 17 (pli) Test Method
    Shear Strength (psi) 1,100, 1,075, 1,100, 750, 400, 1,525, 850, 950, 2,050, 550, 2,475, 250, 775, 650, 1,500, 2,275, 2,275, 2,500, 2,300, 975, 950, 950, 2,150, 750, 1,100, 700, 500, 300, 975, 2,475, 1,875, 1,150, 750, 1,100, 950, 975, 1,100, 925, 1,075, 1,100, 950, 1,000, 325, 1,050, 25, 100 Test Method
    Material Resistance
    Environmental Resistance Excellent environmental resistance
    High Temperature Resistance (°C) 82
    Low Temperature Resistance (°C) -29
    Moisture/Humidity Resistance Excellent
    Hardness
    Shore D Hardness 55 Test Method
    Modulus (psi) 85,669 Test Method
    Other Properties
    Glass Transition Temp (Tg) (°C) 33 Test Method
    Coefficient of Thermal Expansion (CTE) 125 (ppm/°C), 170 (ppm/°C) Test Method
    % Solids (%) 100
    Density (g/cm³) 8 to 8.4 (lbs/gal), 8.75 to 9.15 (lbs/gal)
    Business Information
    Shelf Life Details For maximum shelf life, store duo-pak cartridges and bulk containers at 40°F (4°C) or below.;When stored at the recommended temperatures in the original unopened containers, this product has a shelf life of twelve months from date of shipment.
    Shelf Life Temperature (°F) <39
    Shelf Life Type from date of shipment
    Shelf Life (mon) 12
    Not Good For
    Don't Use With PTFE, Silicone Surfaces, Surfaces Containing Mold-Release Agents, Polyimide, Nylons
  • Best Practices for 3M DP8005 Translucent

    *See Terms of Use Below

    1. Surface Preparation

      3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 can bond polypropylene, polyethylene and other thermoplastic polyolefins without special surface preparation. However, all substrates should be clean, dry and free of paint, oxide films, oils, dust, mold release agents and other surface contaminants. The amount of surface preparation directly depends on the bond strength and environmental resistance desired by the user.

      See Vendor technical data sheet for more information.

    2. Clean-Up

      Solvent wipe surface using acetone or isopropyl alcohol.*

      *Note: When using solvents, be sure to extinguish all ignition sources and follow the manufacturer’s precautions and directions for use.

  • Comparable Materials for 3M DP8005 Translucent

    *See Terms of Use Below

    Spec Engine® Results

Popular Articles

What Projects Require Custom Adhesive Formulations and Why?

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Testing the effectiveness of surface treatments

Read Article

Plastic Bonding with Adhesives - Considerations Q&A

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Gluespec Poll

What level of expertise do you have in specialty chemicals like adhesives, sealants, conformal coatings, etc.?
Fixture or Handling Strength Time Test Methods
Fixture or Handling Strength Time Fixture-Handling Strength Test Method Fixture-Handling Strength Time Temperature
120 to 180 min Minimum of 50 psi shear at 73°F/23°(C) 23°C
Work / Pot Time Test Methods
Work / Pot Time Temperature
2.50 to 3.00 min 23°C
Peel Strength Test Methods
Peel Strength Type Substrate Test Temperature Test Method
17 (pli) T-Peel strength HDPE 23°C Substrate Failure, Peel tests on 0.02" thick HDPE, 0.017" bondline thickness, 8" x 1" in T-peel mode at a rate of 2.0"/min.
Shear Strength Test Methods
Shear Strength Type Cure Time Cure Temperature Substrate Chemical Test Time Test Temperature Test Method
1,100 psi Overlap shear strength >2,880 min 23°C HDPE Control - no chemical exposure 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,075 psi Overlap shear strength >2,880 min 23°C PE 100% RH 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,100 psi Overlap shear strength >2,880 min 23°C PP Water Soak 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
750 psi Overlap shear strength >2,880 min 23°C UHMWPE Salt Water Soak (5% by wt.) 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
400 psi Overlap shear strength >2,880 min 23°C LDPE 100% RH Salt Water Soak (5% by wt.) 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,525 psi Overlap shear strength >2,880 min 23°C ABS NaOH (10% by wt.) 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
850 psi Overlap shear strength >2,880 min 23°C Polycarbonate HCl (16% by vol.) 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
950 psi Overlap shear strength >2,880 min 23°C Plexiglass (PMMA) Isopropyl Alcohol 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,050 psi Overlap shear strength >2,880 min 23°C PVC Antifreeze Coolant 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
550 psi Overlap shear strength >2,880 min 23°C HIPS Gasoline 1,209,600 sec 23°C Substrate failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,475 psi Overlap shear strength >2,880 min 23°C Green FRP Diesel Fuel 1,209,600 sec 23°C Cohesive failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
250 psi Overlap shear strength >2,880 min 23°C PTFE Toluene 1,209,600 sec 23°C Adhesive failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
775 psi Overlap shear strength >2,880 min 23°C Polystyrene Acetone 1,209,600 sec 23°C Substrate Failure/Bread/Yields, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
650 psi Overlap shear strength >2,880 min 23°C Glass (3/16" thick) 23°C Substrate Failure/Bread/Yields, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,500 psi Overlap shear strength >2,880 min 23°C Gel Coat (3/16" thick) 23°C Substrate Failure/Bread/Yields, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,275 psi Overlap shear strength >2,880 min 23°C Copper (1/16" thick) 23°C Cohesive failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,275 psi Overlap shear strength >2,880 min 23°C Aluminum (1/16" thick) 23°C Cohesive failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,500 psi Overlap shear strength >2,880 min 23°C Cold-Rolled Steel (1/32" thick) 23°C Adhesive failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,300 psi Overlap shear strength >2,880 min 23°C 304 Stainless Steel (1/32" thick) 23°C Cohesive failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
975 psi Overlap shear strength >2,880 min 23°C HDPE/HDG 23°C Substrate failure/Break/Yield (HDPE), Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
950 psi Overlap shear strength >2,880 min 23°C HDPE/Galvanealed 23°C Substrate failure/Break/Yield (HDPE), Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
950 psi Overlap shear strength >2,880 min 23°C HDPE/CRS (non-abraded CRS) 23°C Substrate failure/Break/Yield (HDPE), Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,150 psi Overlap shear strength >2,880 min 23°C Oily HDG 23°C Cohesive failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
750 psi Overlap shear strength HDPE -29°C Cohesive failure, Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,100 psi Overlap shear strength HDPE 23°C Substrate failure/Break/Yield, Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
700 psi Overlap shear strength HDPE 49°C Cohesive failure, Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
500 psi Overlap shear strength HDPE 66°C Cohesive failure, Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
300 psi Overlap shear strength HDPE 82°C Cohesive failure, Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
975 psi Overlap shear strength Green-FRP -29°C Adhesive failure, Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
2,475 psi Overlap shear strength Green-FRP 23°C Adhesive failure, Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,875 psi Overlap shear strength Green-FRP 49°C Mixed (Mode of AF and CF), Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,150 psi Overlap shear strength Green-FRP 66°C Mixed (Mode of AF and CF), Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
750 psi Overlap shear strength Green-FRP 82°C Mixed (Mode of AF and CF), Overlap Shear Test Method: Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,100 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
950 psi Overlap shear 71°C Environmental & Chemical Exposure Test on HDPE, Mixed (Mode of AF and CF)
975 psi Overlap shear 71°C Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
1,100 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
925 psi Overlap shear 71°C Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
1,075 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
1,100 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
950 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
1,000 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
325 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
1,050 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
25 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
100 psi Overlap shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
Modulus Test Methods
Modulus Test Method
85,669 psi Modulus at 1% Strain
Shore D Hardness Test Methods
Shore D Hardness Shore Hardness Test Method
55 ASTM D-2240
Coefficient of Thermal Expansion (CTE) Test Methods
Coefficient of Thermal Expansion (CTE) CTE Temperature (°C) CTE Test Method
125 (ppm/°C) -40 to 120°C Tg and CTE determined by TMA -40°F to 249°F (-40°C to 120°C) at 10°F (5°C)/min. (after 2 heat cycles).
170 (ppm/°C) -40 to 120°C Tg and CTE determined by TMA -40°F to 249°F (-40°C to 120°C) at 10°F (5°C)/min. (after 2 heat cycles).
Glass Transition Temp (Tg) Test Methods
Glass Transition Temp (Tg) Glass Transition Temperature (Tg) Test Method
33°C Tg and CTE determined by TMA -40°F to 249°F (-40°C to 120°C) at 10°F (5°C)/min. (after 2 heat cycles).