• Description for 3M DP8010

    Acrylic bonds low surface energy polyolefins without surface preparation • Excellent environmental resistance • 1.5-2 hour handling strength • High shear and peel strength acrylic

    *See Terms of Use Below

    Chemical Resistance Very good, Chemical Resistance: Fluid Resistance: Excellent water resistance, Chemical Resistance: Fluid Resistance: Salt Water
    Application Type Bond
    1 Part or 2 Part 2-Part
    Material Form Liquid
    Substrate Aluminum, Green FRP, Copper (1/16" thick) , Glass, Metal, Lexan, Polypropylene, Rubber, CRS (non-abraded CRS), 304 Stainless Steel (1/32" thick) , Polyethylene, PTFE, Acetal, Many low surface energy plastics, Polyolefins, Primed Aluminum, Plastic, Galvanealed Steel, ThermoPlastic Polyolefin, Aluminum (1/16" thick) , Many low surface energy plastics, Cold-Rolled Steel (1/32" thick) , HDG, Oily HDG
    Industry Screws, Rivets
    Manufacturer 3M
    Chemistry Acrylic, Amine, Methacrylate
    Cure Method Base/Accelerator
    Cure Temperature (°C) 20 to 25, 23
    Cure Time (min) 480 to 1,440
    Viscosity (cPs) Non-sag, 17,000 to 22,000
    Color Yellow
    High Temperature Resistance (°C) 82
    Low Temperature Resistance (°C) -29
    Density (g/cm³) 8.4 (lbs/gal), 8.5 (lbs/gal)
  • Technical Data for 3M DP8010

    Overview
    • Chemical Resistance
      • Chemical Resistance : Fluid Resistance : Water Resistance - Excellent water resistance, Salt Water
      • Chemical Resistance - Very good
    • Application Type
    • 1 Part or 2 Part
      • 2-Part
    • Material Form
      • Liquid
    • Substrate
      • Low Surface Energy - Many low surface energy plastics
      • Polyolefin - Polyolefins, ThermoPlastic Polyolefin
      • Glass
      • Metal
      • Aluminum - Primed Aluminum, Aluminum (1/16" thick)
      • Copper - Copper (1/16" thick)
      • Steel - CRS (non-abraded CRS), Galvanealed Steel, Cold-Rolled Steel (1/32" thick) , HDG, Oily HDG
      • Plastic - Lexan, Many low surface energy plastics
      • Polypropylene
      • Polyethylene (LDPE, HDPE) - Polyethylene
      • Fluoropolymer Teflon (PTFE) - PTFE
      • Acetal
      • Rubber
      • Composites - Green FRP
      • Stainless Steel - 304 Stainless Steel (1/32" thick)
    • Industry
    • Chemistry
      • Acrylic - Methacrylate
      • Other - Amine
    • Cure Method
      • 2-Part Cure - Base/Accelerator
    • Color
      • Yellow
    Specifications
    Cure Specs
    Cure Temperature (°C) 20 to 25, 23
    Cure Time (min) 480 to 1,440
    Viscosity (cPs) Non-sag, 17,000 to 22,000
    Fixture or Handling Strength Time (min) 90 to 120 Test Method
    Work / Pot Time (min) 10 to 12 Test Method
    Mix Ratio 10:1 (by volume), 9.8:1 (by weight)
    Bond Strength
    Structural/Load-Bearing Structural
    Peel Strength (piw) 55 Test Method
    Shear Strength (psi) 750, 400, 1,100, 1,225, 1,500, 1,450, 1,250, 1,075, 2,220, 575, 550, 2,425, 775, 600, 1,550, 2,375, 2,200, 1,525, 900, 200, 825, 425, 1,225, 1,575, 1,450, 1,200, 125, 1,100, 1,000, 1,175, 975, 975, 975, 1,000, 550, 925, 50, 250 Test Method
    Material Resistance
    Environmental Resistance Environmental resistance
    High Temperature Resistance (°C) 82
    Low Temperature Resistance (°C) -29
    Moisture/Humidity Resistance Excellent
    Hardness
    Modulus (psi) 70,000 Test Method
    Other Properties
    Glass Transition Temp (Tg) (°C) 34 Test Method
    Coefficient of Thermal Expansion (CTE) 133 (ppm/°C), 171 (ppm/°C) Test Method
    % Solids (%) 100
    Density (g/cm³) 8.4 (lbs/gal), 8.5 (lbs/gal)
    Business Information
    Shelf Life Details For maximum shelf life, store duo-pak cartridges and bulk containers at 40°F (4°C) or below.;When stored at the recommended temperatures in the original unopened containers, this product has a shelf life of six months from date of shipment.
    Shelf Life Temperature (°F) <39
    Shelf Life Type From date of shipment
    Shelf Life (mon) 6
    Not Good For
    Don't Use With Silicone Surfaces, Surfaces Containing Mold Release, Polyimide, Nylons
  • Best Practices for 3M DP8010

    *See Terms of Use Below

    1. Surface Preparation

      3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010 and DP-8010NS can bond polypropylene, polyethylene and other thermoplastic polyolefins without special surface preparation. However, all substrates should be clean, dry and free of loose paint, oxide films, oils, dust, mold release agents and other surface contaminants. The amount of surface preparation directly depends on the bond strength and environmental resistance desired by the user.

      See vendor technical data sheet for more information.

  • Comparable Materials for 3M DP8010

    *See Terms of Use Below

    Spec Engine® Results

Popular Articles

Testing the effectiveness of surface treatments

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

What Projects Require Custom Adhesive Formulations and Why?

Read Article

Plastic Bonding with Adhesives - Considerations Q&A

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Gluespec Poll

Who do you read or follow for engineering news and entertainment?
Fixture or Handling Strength Time Test Methods
Fixture or Handling Strength Time Fixture-Handling Strength Time Temperature
90 to 120 min 23°C
Work / Pot Time Test Methods
Work / Pot Time Temperature
10 to 12 min 23°C
Peel Strength Test Methods
Peel Strength Type Substrate Test Temperature Test Method
55 piw T-Peel Strength HDPE 23°C Substrate Failure/Break/Yield, Peel tests on 0.02" thick HDPE, 0.017" bondline thickness, 8" x 1" in T-peel mode at a rate of 2.0"/min.
Shear Strength Test Methods
Shear Strength Type Cure Time Cure Temperature Substrate Chemical Test Time Test Temperature Test Method
750 psi Overlap shear strength >2,880 min 23°C UHMWPE Control - no chemical exposure 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
400 psi Overlap shear strength >2,880 min 23°C LDPE 100% RH 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,100 psi Overlap shear strength >2,880 min 23°C HDPE Water Soak 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,225 psi Overlap shear strength >2,880 min 23°C PE NaOH (10% by weight) 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,500 psi Overlap shear strength >2,880 min 23°C PP HCI (16% by volume) 1,209,600 sec 23°C Cohesive failure, Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,450 psi Overlap shear strength >2,880 min 23°C ABS Isoproyl Alcohol 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,250 psi Overlap shear strength >2,880 min 23°C Lexan Antifreeze Coolan 1,209,600 sec 23°C Cohesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
1,075 psi Overlap shear strength >2,880 min 23°C Plexiglass (PMMA) Gasoline 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,220 psi Overlap shear strength >2,880 min 23°C PVC Diesel Fuel 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
575 psi Overlap shear strength >2,880 min 23°C HIPS Toluene 1,209,600 sec 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
550 psi Overlap shear strength >2,880 min 23°C PTFE Acetone 1,209,600 sec 23°C Adhesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
2,425 psi Overlap shear strength >2,880 min 23°C Green FRP 23°C Mixed (Mode of AF and CF), Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C).
775 psi Overlap shear strength >2,880 min 23°C Polystyrene 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
600 psi Overlap shear strength >2,880 min 23°C Glass (3/16" thick) 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,550 psi Overlap shear strength >2,880 min 23°C Gel Coat (3/16" thick) 23°C Substrate Failure/Break/Yield, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
2,375 psi Overlap shear strength >2,880 min 23°C Copper (1/16" thick) 23°C Mixed (Mode of AF and CF), Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
2,200 psi Overlap shear strength >2,880 min 23°C Aluminum (1/16" thick) 23°C Cohesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,525 psi Overlap shear strength >2,880 min 23°C Cold-Rolled Steel (1/32" thick) 23°C Adhesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
900 psi Overlap shear strength >2,880 min 23°C 304 Stainless Steel (1/32" thick) 23°C Adhesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
200 psi Overlap shear strength >2,880 min 23°C Acetal 23°C Adhesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
825 psi Overlap shear strength >2,880 min 23°C CRS/HDPE (Non-abraded CRS) 23°C Adhesive Failure to CRS, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
425 psi Overlap shear strength >2,880 min 23°C Aluminum/HDPE (non-abraded aluminum) 23°C Adhesive Failure to Al, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,225 psi Overlap shear strength >2,880 min 23°C ED-500 E-coated CRS/HDPE 23°C Adhesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,575 psi Overlap shear strength >2,880 min 23°C EC 3924 Primed CRS (non-abraded CRS) 23°C Cohesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,450 psi Overlap shear strength >2,880 min 23°C EC 3924 Primed Al/HDPE (non-abraded Al) 23°C Cohesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,200 psi Overlap shear strength >2,880 min 23°C DCT 5002X Top Coat CRS/HDPE (non-abraded CRS) 23°C Top Coat Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
125 psi Overlap shear strength >2,880 min 23°C RK8010A Top Coat CRS/HDPE (non-abraded CRS) 23°C Adhesive Failure, Overlap shear test for adhesion determined in accordance to ASTM D1002. Sampe dimenions were 1" x 4" x 1/8" (unless other thicknesses indicated) with an overlap area of 1" x 1/2". Plastics and glass substrates were cleansed with isopropyl alcohol (IPA) wipes, metal substrates were abraded with 150-grit sandpaper and cleansed with methyl ethyl ketone (MEK) wipes. All bonds were allowed to cure for a minimum of 48 hours at 73°F (23°C) before tested. Data were collected using a Sintech 5GL Mechanical Tester with the 2000-lb or 5000-lb load cells. Test rate was 2"/min. for plastic bonds, and 0.1"/min. for metal and glass bonds at 73°F (23°C)
1,100 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
1,000 psi Overlap Shear 71°C Environmental & Chemical Exposure Test on HDPE, Mixed (Mode of AF and CF)
1,175 psi Overlap Shear 71°C Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
975 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
975 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
975 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
1,000 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
550 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
925 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Substrate Failure/Break/Yield
50 psi Overlap Shear Room Temperature Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
250 psi Room Temperature Environmental & Chemical Exposure Test on HDPE, Cohesive Failure
Modulus Test Methods
Modulus Test Method
70,000 psi Modulus @ 1% Strain
Coefficient of Thermal Expansion (CTE) Test Methods
Coefficient of Thermal Expansion (CTE) CTE Temperature (°C) CTE Test Method
133 (ppm/°C) -40 to 120°C Tg and CTE determined by TMA -40°F to 249°F (-40°C to 120°C) at 10°F (5°C)/min. (after 2 heat cycles).
171 (ppm/°C) -40 to 120°C Tg and CTE determined by TMA -40°F to 249°F (-40°C to 120°C) at 10°F (5°C)/min. (after 2 heat cycles).
Glass Transition Temp (Tg) Test Methods
Glass Transition Temp (Tg) Glass Transition Temperature (Tg) Test Method
34°C Tg and CTE determined by TMA -40°F to 249°F (-40°C to 120°C) at 10°F (5°C)/min. (after 2 heat cycles).