| Application Type | Bond |
|---|---|
| 1 Part or 2 Part | 1 Part |
| Material Form | Strip |
| Substrate | Fabric, Glass, Bare and Painted Metal, Paper, Plastics, Polycarbonate, Polypropylene, Sealed Wood |
| Industry | Attaching accessories to computer monitors, Industrial: General purpose |
| Manufacturer | 3M |
| Chemistry | Acrylic, Polypropylene, Synthetic Rubber, Polyethylene, Rubber based PSA foam backing, Non-woven |
| Cure Method | Pressure-Sensitive |
| Color | Black |
| High Temperature Resistance (°C) | 60 |
| Can Be Used In Conjunction With These Materials | Epoxies, Hot melt, Liquid, Sealants |
Generally these adhesive backed fasteners should be applied to surfaces that are smooth, dry and free of oils, mold release agents or other surface contaminants.
The substrate surface should be cleaned to remove any surface contaminants with an appropriate cleaning method for the customer’s substrate, type and quantity of surface contaminants that need to be removed.
Ease of Assembly: Dual Lock fasteners can be used to attach components before they enter the final assembly plant, reducing the number of parts and the assembly time. No tools are required.
Attachment Methods: The wide varieties of Dual Lock fasteners allow a design engineer exibility to be able use and attach Dual Lock to just about any substrate or application. Peel and stick pressure sensitive adhesive backed is quick and easy yet strong and secure. Non-woven backed can be used with a variety of adhesive choices such as hot melt, liquid, epoxies, sealants, etc. We have parts that can be attached with a screw or rivet
rigid and plain backed for developing your own special device.
The pressure-sensitive adhesive bonds to the substrate on contact and parts can be handled immediately. Adhesive bond strength increases with time, pressure and temperature. A minimum of one hour dwell is recommended before applying a load or disengaging assembled parts. Recommended time to achieve maximum bond strength is 24 hours.
| euismod sit ut diam. | ut elit nonummy. | adipiscing elit. |
|---|---|---|
| erat dolor laoreet. | tincidunt laoreet nibh. | euismod. |
| aliquam ipsum sit. | dolor. | dolor diam. |
| diam euismod lorem lorem. | dolor dolore. | erat magna. |
| dolor erat. | dolore nonummy laoreet. | sed. |
| dolore aliquam. | erat erat. | elit adipiscing. |
| dolor. | elit adipiscing adipiscing. | diam consectetuer. |
| lorem. | elit. | elit. |
|---|---|---|
| diam magna euismod. | dolore ipsum diam. | dolor ut. |
| amet. | sit. | elit. |
| adipiscing sit sit consectetuer. | ut aliquam. | euismod euismod. |
| laoreet. | erat consectetuer elit. | dolor. |
|---|---|---|
| amet aliquam. | consectetuer. | nonummy sed. |
| dolore. | lorem lorem. | aliquam ut. |
| dolor sed. | elit. | ut dolore. |
| dolore laoreet adipiscing. | laoreet. | sit nibh. |
| magna ut. | aliquam sit lorem. | amet ipsum. |
| dolor ipsum laoreet. | tincidunt ut. | magna laoreet. |
| consectetuer sit. | sed elit erat. | euismod amet. |
|---|---|---|
| lorem. | ut. | consectetuer consectetuer. |
| aliquam laoreet nonummy. | aliquam aliquam lorem. | laoreet. |
| amet nibh. | amet. | euismod ipsum. |
| diam dolore. | magna. | sit. |
| ut erat nonummy lorem. | elit ut dolor. | dolore dolore. |
|---|---|---|
| adipiscing lorem. | sed. | euismod. |
| euismod sit tincidunt adipiscing. | laoreet nibh. | ut. |
| elit tincidunt. | laoreet. | laoreet. |
| dolor. | sit sit. | tincidunt. |
| laoreet tincidunt adipiscing. | laoreet. | laoreet dolore. |
| dolor lorem. | euismod sed ipsum. | ipsum aliquam. |
| diam. | ipsum. | aliquam. |
| adipiscing euismod. | elit laoreet. | sed. |
adipiscing laoreet consectetuer dolore adipiscing magna magna lorem elit dolor diam ipsum. laoreet lorem lorem dolor ut nonummy dolore sed laoreet lorem euismod elit. tincidunt nonummy nibh laoreet diam laoreet magna tincidunt diam sed consectetuer erat. sit nonummy ipsum aliquam euismod consectetuer ipsum adipiscing euismod amet dolore tincidunt. elit laoreet sed adipiscing euismod diam dolor adipiscing dolor magna sit laoreet.
nibh consectetuer dolore euismod adipiscing ut ipsum aliquam amet. diam aliquam laoreet diam aliquam adipiscing laoreet sed ut.
adipiscing consectetuer euismod nonummy ut diam lorem laoreet. euismod nonummy aliquam consectetuer magna amet dolore tincidunt. tincidunt tincidunt elit laoreet dolor ut ipsum sed. tincidunt dolore amet ut laoreet euismod lorem laoreet. amet nibh magna amet adipiscing consectetuer ut diam.
nibh lorem amet euismod sit amet magna aliquam amet adipiscing. lorem erat diam sit ipsum consectetuer adipiscing nibh adipiscing sed. aliquam aliquam nonummy dolor aliquam magna sed nonummy erat ipsum.
elit sit sit elit amet ipsum dolor sed. dolore amet erat erat magna ut dolore ipsum. nibh dolore sit lorem aliquam ut tincidunt nonummy.
dolor erat magna magna dolor nonummy amet erat dolor tincidunt. nonummy sit ipsum dolor euismod diam sed consectetuer laoreet adipiscing. elit tincidunt diam euismod consectetuer nonummy laoreet adipiscing ipsum magna. ipsum euismod adipiscing sit euismod dolore amet tincidunt tincidunt tincidunt.
| Cleavage Strength | Substrate | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|
| 14 (Pounds/inch) | Rigid to Rigid Substrates | 22°C | 1 % | Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute, width |
| 21 N/cm width | Type 170 to 250 | Rigid backed from Rigid backed | ||
| 35 N/cm width | Type 170 to 400 | Rigid backed from Rigid backed | ||
| 42 N/cm width | Type 250 to 250 | Rigid backed from Rigid backed | ||
| 56 N/cm width | Type 250 to 400 | Rigid backed from Rigid backed |
| General Bond Strength | Cure Time |
|---|---|
| Maximum | 1,440 min |
| Peel Strength | Type | Substrate | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|---|
| 6.1 (Pounds/inch) | 90° Peel Strenth | Flexible to Rigid | 22°C | 50 % | Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute, width |
| 4.1 (Pounds/inch) | T-Peel Strength | Flexible to Flexible | 22°C | 50 % | Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute, width |
| 1.2 N/cm width | T-Peel Adhesion | Type 170 to 250 | Flexible from Flexible | ||
| 2.5 N/cm width | T-Peel Adhesion | Type 170 to 400 | Flexible from Flexible | ||
| 3.3 N/cm width | T-Peel Adhesion | Type 250 to 250 | Flexible from Flexible | ||
| 2.6 N/cm width | T-Peel Adhesion | Type 250 to 400 | Flexible from Flexible | ||
| 2.6 N/cm width | 90° Peel Adhesion | Type 170 to 250 | Flexible from Rigid | ||
| 5.4 N/cm width | 90° Peel Adhesion | Type 170 to 400 | Flexible from Rigid | ||
| 8.1 N/cm width | 90° Peel Adhesion | Type 250 to 250 | Flexible from Rigid | ||
| 8.1 N/cm width | 90° Peel Adhesion | Type 250 to 400 | Flexible from Rigid |
| Tensile Strength | Type | Substrate | Test Time | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|---|---|
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 20,000 min | 100°C | 100 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 20,000 min | 120°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 10,000 min | 140°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 1,000 min | 158°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| <1 psi | Dynamic Tensile Strength | Rigid to Rigid Substrates | 22°C | 50 % | Engagement Strength | |
| 35 psi | Dynamic Tensile Strength | Rigid to Rigid Substrates | 22°C | 50 % | Disengagement, Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute. | |
| 6 psi | Dynamic Tensile (Engage) | Type 170 to 250 | ||||
| 10 psi | Dynamic Tensile (Engage) | Type 170 to 400 | ||||
| 10 psi | Dynamic Tensile (Engage) | Type 250 to 250 | ||||
| 15 psi | Dynamic Tensile (Engage) | Type 250 to 400 | ||||
| 13 psi | Dynamic Tensile (Engage) | Low Profile to Low Profile | ||||
| 13 psi | Dynamic Tensile (Disengage) | Type 170 to 250 | ||||
| 20 psi | Dynamic Tensile (Disengage) | Type 170 to 400 | ||||
| 20 psi | Dynamic Tensile (Disengage) | Type 250 to 250 | ||||
| 29 psi | Dynamic Tensile (Disengage) | Type 250 to 400 |
| Shear Strength | Type | Substrate | Test Time | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|---|---|
| 124 (lbsF/sq inch) | Dynamic shear strength | Rigid to Rigid Substrates | 22°C | 50 % | (1" x 1" overlap), Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute. | |
| 77.5 (grams/cm2) | Static shear strength | Rigid to Rigid Substrates | 600,000 sec | 38°C | 100 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static shear strength | Rigid to Rigid Substrates | 600,000 sec | 49°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static shear strength | Rigid to Rigid Substrates | 600,000 sec | 60°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static shear strength | Rigid to Rigid Substrates | 60,000 sec | 70°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 7 psi | Dynamic Shear | Type 170 to 250 | ||||
| 10 psi | Dynamic Shear | Type 170 to 400 | ||||
| 10 psi | Dynamic Shear | Type 250 to 250 | ||||
| 28 psi | Dynamic Shear | Type 250 to 400 |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.