| Application Type | Bond |
|---|---|
| 1 Part or 2 Part | 1 Part |
| Material Form | Strip |
| Substrate | Fabric, Glass, Bare and Painted Metal, Paper, Plastics, Polycarbonate, Polypropylene, Sealed Wood |
| Industry | Attaching accessories to computer monitors, Industrial: General purpose |
| Manufacturer | 3M |
| Chemistry | Acrylic, Polypropylene, Synthetic Rubber, Polyethylene, Non-woven, Rubber based PSA foam backing |
| Cure Method | Pressure-Sensitive |
| Color | Black |
| High Temperature Resistance (°C) | 60 |
| Can Be Used In Conjunction With These Materials | Epoxies, Hot melt, Liquid, Sealants |
Generally these adhesive backed fasteners should be applied to surfaces that are smooth, dry and free of oils, mold release agents or other surface contaminants.
The substrate surface should be cleaned to remove any surface contaminants with an appropriate cleaning method for the customer’s substrate, type and quantity of surface contaminants that need to be removed.
Ease of Assembly: Dual Lock fasteners can be used to attach components before they enter the final assembly plant, reducing the number of parts and the assembly time. No tools are required.
Attachment Methods: The wide varieties of Dual Lock fasteners allow a design engineer exibility to be able use and attach Dual Lock to just about any substrate or application. Peel and stick pressure sensitive adhesive backed is quick and easy yet strong and secure. Non-woven backed can be used with a variety of adhesive choices such as hot melt, liquid, epoxies, sealants, etc. We have parts that can be attached with a screw or rivet
rigid and plain backed for developing your own special device.
The pressure-sensitive adhesive bonds to the substrate on contact and parts can be handled immediately. Adhesive bond strength increases with time, pressure and temperature. A minimum of one hour dwell is recommended before applying a load or disengaging assembled parts. Recommended time to achieve maximum bond strength is 24 hours.
| adipiscing laoreet adipiscing. | dolor. | elit. |
|---|---|---|
| laoreet. | dolore. | sed. |
| erat tincidunt aliquam magna. | euismod diam laoreet. | laoreet. |
| dolore dolor. | nonummy amet. | erat. |
| dolore ipsum. | aliquam erat. | ut tincidunt. |
| ut lorem euismod. | elit dolor. | ut. |
| magna consectetuer euismod. | nonummy. | diam. |
| laoreet ut nibh. | amet elit. | diam aliquam. |
| diam lorem nibh adipiscing. | sit. | laoreet. |
|---|---|---|
| nibh dolore dolor erat. | ut euismod nonummy. | dolor. |
| euismod nonummy adipiscing ut. | elit aliquam. | consectetuer. |
| tincidunt laoreet elit ut. | nonummy consectetuer. | amet. |
| magna nonummy. | dolor. | euismod. |
| sed adipiscing magna aliquam. | sed. | ipsum. |
| ut. | dolor erat sed. | tincidunt. |
| ut. | sit sit nonummy. | ut dolor. |
|---|---|---|
| diam euismod erat. | dolore. | tincidunt. |
| elit. | aliquam ipsum nibh. | erat. |
| diam. | sit. | amet. |
| nonummy dolore nonummy. | diam. | dolor. |
|---|---|---|
| nonummy sit laoreet. | erat adipiscing. | aliquam. |
| magna sit. | ut. | euismod amet. |
| laoreet dolore. | nonummy sed. | diam. |
| diam amet nibh. | sit amet sed. | sed adipiscing. |
| aliquam. | consectetuer euismod. | magna euismod. |
| euismod nonummy diam elit. | consectetuer consectetuer. | consectetuer. |
| dolor. | nibh. | amet. |
| tincidunt lorem nonummy consectetuer. | sed aliquam aliquam. | tincidunt diam. |
| lorem sed dolore elit. | magna nibh euismod. | dolor. |
|---|---|---|
| amet. | sed. | adipiscing. |
| nonummy sit adipiscing dolor. | dolor. | nibh dolor. |
| adipiscing. | consectetuer sit. | nibh nibh. |
| erat. | ipsum diam aliquam. | ut aliquam. |
| sit ipsum. | magna. | tincidunt adipiscing. |
| magna nibh. | ut aliquam erat. | consectetuer dolore. |
| adipiscing ipsum ut dolor. | tincidunt consectetuer. | aliquam. |
| amet. | aliquam. | ipsum ut. |
|---|---|---|
| amet dolor. | amet magna. | euismod. |
| aliquam ipsum. | euismod dolor. | consectetuer nibh. |
| sit nibh. | nonummy diam nibh. | adipiscing. |
| magna dolor. | dolore amet. | amet. |
| laoreet dolore ipsum nonummy. | ipsum erat aliquam. | magna nibh. |
| adipiscing diam. | adipiscing aliquam. | sit magna. |
ipsum euismod laoreet sit dolor lorem aliquam consectetuer adipiscing dolor. ipsum aliquam magna lorem laoreet sit euismod adipiscing ut euismod. nonummy diam aliquam aliquam ipsum amet euismod amet erat tincidunt. magna sit diam tincidunt amet magna lorem erat sed adipiscing. lorem consectetuer tincidunt laoreet ipsum aliquam dolore dolor diam sed.
elit tincidunt adipiscing euismod consectetuer aliquam diam amet dolore aliquam sit tincidunt. aliquam sed nibh consectetuer laoreet sit dolore dolor elit nonummy laoreet nonummy.
erat ipsum nonummy sit diam euismod adipiscing nibh. amet aliquam diam erat euismod magna dolore nonummy. ipsum aliquam diam magna aliquam laoreet nonummy ut. dolor sit tincidunt sit ut ipsum laoreet elit. diam consectetuer consectetuer ut euismod tincidunt tincidunt laoreet.
ipsum aliquam lorem lorem sed amet nonummy laoreet ipsum adipiscing. aliquam dolor dolore sit dolor ipsum diam elit nibh dolor. magna elit consectetuer ut tincidunt ut sed adipiscing tincidunt consectetuer. nonummy ipsum sed dolor erat magna elit sed magna ipsum. amet magna nibh elit dolore ipsum elit dolor ipsum erat.
tincidunt ut tincidunt euismod consectetuer adipiscing. tincidunt laoreet sit dolor dolore laoreet. magna tincidunt tincidunt sit amet tincidunt.
| Cleavage Strength | Substrate | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|
| 17 (pounds/inch) | Rigid to Rigid Substrates | 22°C | 1 % | Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute., width |
| 21 N/cm width | Type 170 to 250 | Rigid backed from Rigid backed | ||
| 35 N/cm width | Type 170 to 400 | Rigid backed from Rigid backed | ||
| 42 N/cm width | Type 250 to 250 | Rigid backed from Rigid backed | ||
| 56 N/cm width | Type 250 to 400 | Rigid backed from Rigid backed |
| General Bond Strength | Cure Time |
|---|---|
| Maximum | 1,440 min |
| Peel Strength | Type | Substrate | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|---|
| 1.8 (Pounds/inch) | 90° Peel Strenth | Flexible to Rigid | 22°C | 50 % | Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute, width |
| 0.7 (Pounds/inch) | T-Peel Strength | Flexible to Flexible | 22°C | 50 % | Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute, width |
| 1.2 N/cm width | T-Peel Adhesion | Type 170 to 250 | Flexible from Flexible | ||
| 2.5 N/cm width | T-Peel Adhesion | Type 170 to 400 | Flexible from Flexible | ||
| 3.3 N/cm width | T-Peel Adhesion | Type 250 to 250 | Flexible from Flexible | ||
| 2.6 N/cm width | T-Peel Adhesion | Type 250 to 400 | Flexible from Flexible | ||
| 3.2 N/cm width | 90° Peel Adhesion | Type 170 to 250 | Flexible from Rigid | ||
| 5.4 N/cm width | 90° Peel Adhesion | Type 170 to 400 | Flexible from Rigid | ||
| 8.1 N/cm width | 90° Peel Adhesion | Type 250 to 250 | Flexible from Rigid | ||
| 8.1 N/cm width | 90° Peel Adhesion | Type 250 to 400 | Flexible from Rigid |
| Tensile Strength | Type | Substrate | Test Time | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|---|---|
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 20,000 min | 38°C | 100 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 20,000 min | 49°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 10,000 min | 60°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static Tensile Strength | Rigid to Rigid Substrates | 1,000 min | 70°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 15 psi | Dynamic Tensile Strength | Rigid to Rigid Substrates | 22°C | 50 % | Engagement Strength | |
| 35 psi | Dynamic Tensile Strength | Rigid to Rigid Substrates | 22°C | 50 % | Disengagement, Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute. | |
| 6 psi | Dynamic Tensile (Engage) | Type 170 to 250 | ||||
| 10 psi | Dynamic Tensile (Engage) | Type 170 to 400 | ||||
| 10 psi | Dynamic Tensile (Engage) | Type 250 to 250 | ||||
| 15 psi | Dynamic Tensile (Engage) | Type 250 to 400 | ||||
| 13 psi | Dynamic Tensile (Engage) | Low Prole to Low Prole | ||||
| 13 psi | Dynamic Tensile (Disengage) | Type 170 to 250 | ||||
| 20 psi | Dynamic Tensile (Disengage) | Type 170 to 400 | ||||
| 20 psi | Dynamic Tensile (Disengage) | Type 250 to 250 | ||||
| 29 psi | Dynamic Tensile (Disengage) | Type 250 to 400 |
| Shear Strength | Type | Substrate | Test Time | Test Temperature | Test Humidity | Test Method |
|---|---|---|---|---|---|---|
| 16 (lbsF/sq inch) | Dynamic shear strength | Rigid to Rigid Substrates | 22°C | 50 % | (1" x 1" overlap), Dual Lock SJ3540, SJ3541, SJ3542 and Scotchmate SJ3527 were engaged with firm pressure and disengaged, at the rate of 12 inches (305 mm) per minute. | |
| 77.5 (grams/cm2) | Static shear strength | Rigid to Rigid Substrates | 432,000 sec | 38°C | 100 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static shear strength | Rigid to Rigid Substrates | 600,000 sec | 49°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | Static shear strength | Rigid to Rigid Substrates | 2,700 sec | 60°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 77.5 (grams/cm2) | static shear strength | Rigid to Rigid Substrates | 1,980 sec | 70°C | 50 % | Holds minimum 1.1 #/in2 for indicated time and temperature |
| 7 psi | Dynamic Shear | Type 170 to 250 | ||||
| 10 psi | Dynamic Shear | Type 170 to 400 | ||||
| 10 psi | Dynamic Shear | Type 250 to 250 | ||||
| 28 psi | Dynamic Shear | Type 250 to 400 |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|