3M HT40 Rite-Lok Hi Temperature Instant Adhesive
Chemical Resistance Most oils, Chemical Resistance: Solvent resistance Application Type Bond, Adhesive: Instant Adhesives 1 Part or 2 Part 1-Part Material Form Liquid Substrate Porous substrate surfaces, Polyethylene, Paper, Low surface energy plastics, Polypropylene Industry Electronics, Electric motors, Transformers, Automotive Manufacturer 3M Chemistry Cyanoacrylate, Ethyl Hybrid Cure Method Moisture Viscosity (cPs) Low, 30 to 50 Color Clear High Temperature Resistance (°C) High temperature resistant, 106, 121, Thermal cycling resistance Low Temperature Resistance (°C) -54
Technical Data for 3M HT40 Rite-Lok Hi Temperature Instant Adhesive
- Chemical Resistance - Most oils
- Chemical Resistance : Relative Solvent Resistance - Solvent resistance
1 Part or 2 Part
- Cyanoacrylate (CA) - Cyanoacrylate
- Other - Ethyl Hybrid
- Other - Hand applied
- Moisture / Condensation Cure - Moisture
- Clear / Transparent - Clear
Viscosity (cPs) Low, 30 to 50 Test Method Fixture or Handling Strength Time (min) 0.08 to 0.33
High Temperature Resistance (°C) High temperature resistant, 106, 121, Thermal cycling resistance Low Temperature Resistance (°C) -54 Vibration Resistance/Shock Resistance Shock resistance
Specific Gravity 1.050
Shelf Life Details Storage conditions:For short term storage (<30 days), keep adhesive in a cool (60°F to 80°F [16°C to 27°C]), dry place out of direct sunlight. Keep containers tightly covered and free of moisture. Refrigeration (40°F [4°C]) gives optimum long term storage stability.;Rite-Lok™General Purpose Instant Adhesives can be expected to have a shelf life of one year from the date of shipment from 3M when stored under refrigerated conditions. Shelf Life Temperature (°F) 140 to 176, 40 Shelf Life Type From the date of shipment Shelf Life (mon) 12
Best Practices for 3M HT40 Rite-Lok Hi Temperature Instant Adhesive
For optimum strength structural bonds, paint, oxide films, oils, dust, mold release agents, and all other surface contaminants must be completely removed. However, the amount of surface preparation depends on the required bond strength and the environmental aging resistance desired by the user. Typical quick surface preparation would include wiping with a clean solvent (such as isopropyl alcohol), abrading the surface with a clean fine abrasive, and then wiping again with a clean solvent to remove loose particles.
Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow the manufacturer’s precautions and directions for use.
Ensure that parts are clean, dry, and free from oil and grease.
A Rite-Lok™ Instant Adhesive Activator may be required if there are bonding gaps or porous substrate surfaces, if substrates are low surface energy plastics (e.g., polyethylene, polypropylene) or if substrates have acidic surfaces (e.g., paper, leather).
Bond speed is typically very fast so ensure that parts are properly aligned before dispensing.
Product is normally hand applied from the bottle. Apply sparingly to one surface and press parts firmly together until handling strength is achieved. As a general rule, as little cyanoacrylate as possible should be used. Over application will result in slower cure speed and lower bond strength.
Full bond strength will typically be achieved within a 24 hour cure time.
Low humidity or low temperature conditions will slow down the cure rate.
After curing, Rite-Lok™ General Purpose Instant Adhesive bonds are suitable for use up to about 180°F (82°C). At 180°F (82°C) the bonds will be approximately70% of the strength at room temperature and at 212°F (100°C) about 50% of full strength.
Cyanoacrylate bond resistance to most oils and solvents is excellent. Long term humidity, moisture, or water immersion may affect the strength of a cured cyanoacrylate bond depending on the substrates and the bond gap. Testing is recommended to evaluate the effect.