Description for 3M PR600 Rite-Lok Cyanoacrylate
A medium viscosity cyanoacrylate with some gap-filling capability. It will bond many common substrates including plastics and rubbers.<br/>Chemical Resistance Excellent, Chemical Resistance: Excelent Solvent resistance, Most oils Application Type Bond, Adhesive: Instant Adhesives 1 Part or 2 Part 1-Part Material Form Liquid Substrate Composite, Combination with metal, Nylon, Paper, Difficult-to-bond plastic, Polypropylene, Heavily plasticized PVC, Rubber, porous substrate surfaces, polyethylene, EPDM, Low surface energy plastics, ABS, Low surface energy plastics Manufacturer 3M Chemistry Cyanoacrylate, Ethyl Hybrid Cure Method Moisture Gap Fill (in) Gap-filling Cure Time (min) 1,440 Viscosity (cPs) medium, 510 to 660, 500 to 700 Color Clear High Temperature Resistance (°C) 82 Low Temperature Resistance (°C) -54 -
Technical Data for 3M PR600 Rite-Lok Cyanoacrylate
Overview
-
Chemical Resistance
- Chemical Resistance - Excellent, Most oils
- Chemical Resistance : Relative Solvent Resistance - Excelent Solvent resistance
-
1 Part or 2 Part
- 1-Part
-
Material Form
- Liquid
-
Substrate
- Porous Substrates - porous substrate surfaces
- Low Surface Energy - Low surface energy plastics
- Metal - Combination with metal
- Plastic - Difficult-to-bond plastic, Low surface energy plastics
- Nylon
- Polypropylene
- Polyvinyl chloride (PVC) - Heavily plasticized PVC
- Polyethylene (LDPE, HDPE) - polyethylene
- ABS
- Rubber
- EPM/EPDM - EPDM
- Composites - Composite
- Paper
- Other - Like substrates, Santoprene, Viton, Common substrates, Acidic surfaces, Leather
-
Chemistry
- Cyanoacrylate (CA) - Cyanoacrylate
- Other - Ethyl Hybrid
-
Application Method
- Other - Hand applied
-
Cure Method
- Moisture / Condensation Cure - Moisture
-
Color
- Clear / Transparent - Clear
Specifications
Cure Specs
Gap Fill (in) Gap-filling Cure Time (min) 1,440 Viscosity (cPs) medium, 510 to 660, 500 to 700 Test Method Fixture or Handling Strength Time (min) 0.07 to 0.42, <0.58 Bond Strength
Shear Strength (psi) 2,900, 2,100, 2,800, 2,326, 1,200, 750, 1,750, 900, 1,050, 100 Test Method Tensile Strength (psi) 4,600 Test Method Material Resistance
High Temperature Resistance (°C) 82 Low Temperature Resistance (°C) -54 Other Properties
Specific Gravity 1.07 (g/ml) Business Information
Shelf Life Details For short term storage (<30 days), keep adhesive in a cool (60°F to 80°F [16°C to 27°C]), dry place out of direct sunlight. Keep containers tightly covered and free of moisture. Refrigeration (40°F [4°C]) gives optimum long term storage stability.;3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesives can be expected to have a shelf life of one year from the date of shipment from 3M when stored under refrigerated conditions. Shelf Life Temperature (°F) 61 to 81 Shelf Life Type From the date of shipment Shelf Life (mon) 12 -
-
Best Practices for 3M PR600 Rite-Lok Cyanoacrylate
-
Surface Preparation
For optimum strength structural bonds, paint, oxide films, oils, dust, mold release agents, and all other surface contaminants must be completely removed. However, the amount of surface preparation depends on the required bond strength and the environmental aging resistance desired by the user. Typical quick surface preparation would include wiping with a clean solvent (such as isopropyl alcohol), abrading the surface with a clean fine abrasive, and then wiping again with a clean solvent to remove loose particles.
Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow the manufacturer’s precautions and directions for use.
Ensure that parts are clean, dry, and free from oil and grease.
A instant adhesive activator may be required if there are bonding gaps or porous substrate surfaces, if substrates are low surface energy plastics (e.g., polyethylene, polypropylene) or if substrates have acidic surfaces (e.g., paper, leather).
-
Application
Bond speed is typically very fast so ensure that parts are properly aligned before dispensing.
Product is normally hand applied from the bottle. Apply sparingly to one surface and press parts firmly together until handling strength is achieved. As a general rule, as little cyanoacrylate as possible should be used. Over application will result in slower cure speed and lower bond strength.
-
Curing
Full bond strength will typically be achieved within a 24 hour cure time.
Low humidity or low temperature conditions will slow down the cure rate
After curing, 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive bonds are suitable for use up to about 180°F (82°C). At 180°F (82°C) the bonds will be approximately 70% of the strength at room temperature and at 212°F (100°C) about 50% of full strength.
Cyanoacrylate bond resistance to most oils and solvents is excellent. Long term humidity, moisture, or water immersion may affect the strength of a cured cyanoacrylate bond depending on the substrates and the bond gap. Testing is recommended to evaluate the effect
-
-
Comparable Materials for 3M PR600 Rite-Lok Cyanoacrylate
Spec Engine® Results
-
799(PermaBond)• Single component • Ethyl cyanoacrylate • High viscosity • Fast cure •Surface insensitive • Extremely fast setting • Rapidly bond • No solvents • Colourless.
-
268(PermaBond)
Faster set times and improved gap-filling capability compared to conventional Cyanoacrylate.
-
Loctite 425(Henkel)Designed as a fast curing, low strength adhesive for locking metal and plastics fasteners. The product is designed for pre- or post-application.
- Compare All
Closest Results from this Manufacturer
-
Scotch-Weld Super Fast Instant Adhesive SF100(3M)Rely less on surface moisture for cure speed than standard cyanoacrylates. They are designed to join together difficult-to-bond plastics and rubbers, acidic and/or contaminated surfaces such as woods, leathers, cardboard, and oily surfaces.
-
PR40 Rite-Lok Cyanoacrylate(3M)
A low viscosity cyanoacrylate adhesive which bonds close-itting plastic or rubber parts quickly and with high strength.
-
MC100 Rite-Lok Cyanoacrylate(3M)
Designed to give optimum performance and high strength bonds on metals.
- Compare All
-
Popular Articles
Cyanoacrylate 202
Read Article
Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation
Read Article
Cyanoacrylate 101
Read Article
Testing the effectiveness of surface treatments
Read ArticleSponsored Articles
Unique Advantages of Contact Adhesives
Read Article
Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials
Read Article
Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:
Read Article
Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive
Read ArticleFeatured Ads
Viscosity Test Methods
| Viscosity | Test Method |
|---|---|
| medium | |
| 510 to 660 cPs | Brookfield LVF, Spindle 3 @ 30 rpm. |
| 500 to 700 cPs | Cone-Plate viscosity, CP75 at 100/s shear rate. |
Tensile Strength Test Methods
| Tensile Strength | Test Method |
|---|---|
| 4,600 psi | ASTM D2095 |
Shear Strength Test Methods
| Shear Strength | Type | Substrate | Test Method |
|---|---|---|---|
| 2,900 psi | Overlap Shear Strength | ASTM D1002 (grit-blasted steel). | |
| 2,100 psi | Overlap Shear Strength | Steel | ASTM D-1002; Grit blasted |
| 2,800 psi | Overlap Shear Strength | Stainless Steel | ASTM D-1002; Grit blasted |
| 2,326 psi | Overlap Shear Strength | Aluminum | ASTM D-1002; Grit blasted |
| 1,200 psi | Overlap Shear Strength | ABS | ASTM D-1002; Substrate failure |
| 750 psi | Overlap Shear Strength | Polycarbonate | ASTM D-1002; Substrate failure |
| 1,750 psi | Overlap Shear Strength | PVC | ASTM D-1002; Substrate failure |
| 900 psi | Overlap Shear Strength | Nylon | ASTM D-1002 |
| 1,050 psi | Overlap Shear Strength | Polypropylene | ASTM D-1002; Substrate failure; Primed with AC77 |
| 100 psi | Overlap Shear Strength | Silicone Elastomer | ASTM D-1002; Substrate failure; Primed with AC79 |