Description for 3M PR600B Rite-Lok Cyanoacrylate
Designed to give exceptional performance on difficult-to-bond plastic and rubber substrates.Chemical Resistance Excellent, Chemical Resistance: Excelent Solvent resistance, Most oils Application Type Bond, Adhesive: Instant Adhesives 1 Part or 2 Part 1-Part Material Form Liquid Substrate composite, in combination with metal, Nylon, Paper, difficult-to-bond plastic, polypropylene, heavily plasticized PVC, rubber, porous substrate surfaces, polyethylene, EPDM, Low surface energy plastics, ABS, Low surface energy plastics Manufacturer 3M Chemistry Cyanoacrylate, Ethyl Hybrid Cure Method Moisture Cure Time (min) 1,440 Viscosity (cPs) 510 to 660 Color Black High Temperature Resistance (°C) 82 Low Temperature Resistance (°C) -54 -
Technical Data for 3M PR600B Rite-Lok Cyanoacrylate
Overview
-
Chemical Resistance
- Chemical Resistance - Excellent, Most oils
- Chemical Resistance : Relative Solvent Resistance - Excelent Solvent resistance
-
1 Part or 2 Part
- 1-Part
-
Material Form
- Liquid
-
Substrate
- Porous Substrates - porous substrate surfaces
- Low Surface Energy - Low surface energy plastics
- Metal - in combination with metal
- Plastic - difficult-to-bond plastic, Low surface energy plastics
- Nylon
- Polypropylene
- Polyvinyl chloride (PVC) - heavily plasticized PVC
- Polyethylene (LDPE, HDPE) - polyethylene
- ABS
- Rubber
- EPM/EPDM - EPDM
- Composites - composite
- Paper
- Other - like substrates, Santoprene, Viton, common substrates, acidic surfaces, leather
-
Chemistry
- Cyanoacrylate (CA) - Cyanoacrylate
- Other - Ethyl Hybrid
-
Application Method
- Other - Hand applied
-
Cure Method
- Moisture / Condensation Cure - Moisture
-
Color
- Black
Specifications
Cure Specs
Cure Time (min) 1,440 Viscosity (cPs) 510 to 660 Test Method Fixture or Handling Strength Time (min) 0.07 to 0.42 Material Resistance
High Temperature Resistance (°C) 82 Low Temperature Resistance (°C) -54 Other Properties
Specific Gravity 1.070 Business Information
Shelf Life Details Storage: For short term storage (<30 days), keep adhesive in a cool (60°F to 80°F [16°C to 27°C]), dry place out of direct sunlight. Keep containers tightly covered and free of moisture. Refrigeration (40°F [4°C]) gives optimum long term storage stability.;3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesives can be expected to have a shelf life of one year from the date of shipment from 3M when stored under refrigerated conditions. Shelf Life Temperature (°F) 140 to 176, 40 Shelf Life Type From the date of shipment Shelf Life (mon) 12 -
-
Best Practices for 3M PR600B Rite-Lok Cyanoacrylate
-
Surface Preparation
For optimum strength structural bonds, paint, oxide films, oils, dust, mold release agents, and all other surface contaminants must be completely removed. However, the amount of surface preparation depends on the required bond strength and the environmental aging resistance desired by the user. Typical quick surface preparation would include wiping with a clean solvent (such as isopropyl alcohol), abrading the surface with a clean fine abrasive, and then wiping again with a clean solvent to remove loose particles.
Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow the manufacturer’s precautions and directions for use.
Ensure that parts are clean, dry, and free from oil and grease.
A Instant Adhesive Activator may be required if there are bonding gaps or porous substrate surfaces, if substrates are low surface energy plastics (e.g., polyethylene, polypropylene) or if substrates have acidic surfaces (e.g., paper, leather).
-
Application
Bond speed is typically very fast so ensure that parts are properly aligned before dispensing.
Product is normally hand applied from the bottle. Apply sparingly to one surface and press parts firmly together until handling strength is achieved. As a general rule, as little cyanoacrylate as possible should be used. Over application will result in slower cure speed and lower bond strength.
-
Curing
Full bond strength will typically be achieved within a 24 hour cure time.
Low humidity or low temperature conditions will slow down the cure rate
After curing, 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive bonds are suitable for use up to about 180°F (82°C). At 180°F (82°C) the bonds will be approximately 70% of the strength at room temperature and at 212°F (100°C) about 50% of full strength.
Cyanoacrylate bond resistance to most oils and solvents is excellent. Long term humidity, moisture, or water immersion may affect the strength of a cured cyanoacrylate bond depending on the substrates and the bond gap. Testing is recommended to evaluate the effect
-
-
Comparable Materials for 3M PR600B Rite-Lok Cyanoacrylate
Spec Engine® Results
Closest Results from this Manufacturer
Popular Articles
Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation
Read ArticleCyanoacrylate 202
Read ArticleCyanoacrylate 101
Read ArticleTesting the effectiveness of surface treatments
Read ArticleSponsored Articles
Unique Advantages of Contact Adhesives
Read ArticleUsing LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials
Read ArticleSylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:
Read ArticleCase Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive
Read ArticleFeatured Ads