3M SA24 Rite-Lok Structural Adhesive
Application Type Bond 1 Part or 2 Part 2-Part Material Form Liquid Substrate Ferrite, Composite materials, Glass, Metals, Wood items, Wood, More absorbent (more porous) surface, Mirror Industry Bonded substrates include electronic components, Speaker magnets, Firearm components Manufacturer 3M Chemistry Acrylic, Urethane Methacrylate, Urethane Methacrylate, Urethane Methacrylate Cure Method 2-Part Cure Cure Time (min) 1,440 Viscosity (cPs) 10,000 to 25,000 Color Amber
Technical Data for 3M SA24 Rite-Lok Structural Adhesive
- Adhesive - Bond
1 Part or 2 Part
- Ceramic - Ferrite
- Porous Substrates - More absorbent (more porous) surface
- Glass - Mirror
- Metal - Metals
- Wood - Wood items
- Composites - Composite materials
- Electronics - Bonded substrates include electronic components, Firearm components
- Speakers - Speaker magnets
- Magnet - Speaker magnets
- Other - Flat bond lines
- Acrylated Urethane - Urethane Methacrylate
- Acrylic - Urethane Methacrylate
- Polyurethane - Urethane Methacrylate
- 2-Part Cure
- Red - Amber
Cure Time (min) 1,440 Viscosity (cPs) 10,000 to 25,000 Fixture or Handling Strength Time (min) 1.00, 1.00 to 5.00
Structural/Load-Bearing Structural General Bond Strength (psi) Excellent Shear Strength (psi) 2,500 Test Method
Impact Resistance impact resistant
Specific Gravity 1.130
Shelf Life Details Storage: Store product in a cool, dry area out of direct sunlight.;Twelve months when stored at 60° to 80°F 16° to 27°C) in the original unopened container. Shelf Life Temperature (°F) 140 to 176 Shelf Life (mon) 12
Best Practices for 3M SA24 Rite-Lok Structural Adhesive
For optimum strength surfaces should be clean and free of all surface contaminants including paint, oxide films, oils, dust, mold release agents, etc. However, the amount of surface preparation depends on the required bond strength and the environmental resistance desired by the user. Typical quick surface preparation would include wiping with a clean solvent (such as isopropyl alcohol), abrading the surface with a clean fine abrasive, and then wiping again with a clean solvent to remove loose particles.
Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow the manufacturer's precautions and directions for use.
For best results, ensure that parts are clean, dry, and free from oil and grease. However, bonds can still be achieved on 'as received' or slightly oily parts.
Rite Lok™ structural Acrylic Activator AC380D should be applied to the less absorbent (less porous) substrate. If necessary, it may be applied to both bonding surfaces.
Rite lok™ structural Acrylic Adhesive should be applied to the more absorbent (more porous) surface in beads or spread as a thin layer using a flat edge.
The two parts should then be brought together and clamped or held in position to achieve best results.
Due to its anaerobic nature, any Rite-Lok™ Structural Acrylic Adhesive squeezed outside of the joint will remain soft.
Full bond strength will typically be achieved within a 24 hour cure time.
Comparable Materials for 3M SA24 Rite-Lok Structural Adhesive
Spec Engine® Results
Closest Results from this Manufacturer
Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of MaterialsRead Article
Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:Read Article
1 VIEW FREE
View 3M - SA24 Rite-Lok Structural Adhesive now.