3M Scotch-Weld Super Fast Instant Adhesive SF100
Chemical Resistance Excellent, Chemical Resistance: Excelent Solvent resistance, Most oils Application Type Bond, Adhesive: Instant Adhesives 1 Part or 2 Part 1-Part Material Form Liquid Substrate paper, difficult-to-bond plastics, polypropylene, rubbers, woods, porous substrate surfaces, Silicone Elastomer, polyethylene, Low surface energy plastics, cardboard, Low surface energy plastics Manufacturer 3M Chemistry Cyanoacrylate, Ethyl Hybrid Cure Method Moisture Cure Time (min) super fast, 1,440 Viscosity (cPs) Low, 71 to 95 Color Clear High Temperature Resistance (°C) 82 Low Temperature Resistance (°C) -54 Key Specifications CID (United States Government Commercial Item Description): A-A-3097: Type II, Class 2
Technical Data for 3M Scotch-Weld Super Fast Instant Adhesive SF100
- Chemical Resistance - Excellent, Most oils
- Chemical Resistance : Relative Solvent Resistance - Excelent Solvent resistance
1 Part or 2 Part
- Porous Substrates - porous substrate surfaces
- Low Surface Energy - Low surface energy plastics
- Plastic - difficult-to-bond plastics, Low surface energy plastics
- Silicone - Silicone Elastomer
- Polyethylene (LDPE, HDPE) - polyethylene
- Rubber - rubbers
- Wood - woods
- Paper - cardboard
- Other - acidic and/or contaminated surfaces, leathers, oily surfaces
- Other - high speed production applications
- Cyanoacrylate (CA) - Cyanoacrylate
- Other - Ethyl Hybrid
- Other - Hand applied
- Moisture / Condensation Cure - Moisture
- Clear / Transparent - Clear
- CID (United States Government Commercial Item Description) : A-A-3097 : Type II, Class 2
Cure Time (min) super fast, 1,440 Viscosity (cPs) Low, 71 to 95 Test Method Fixture or Handling Strength Time (min) 0.05 to 0.08
Shear Strength (psi) 2,900, 2,109, 2,266, 1,689, 914, 755, 1,096, 321, 728, 105 Test Method Tensile Strength (psi) 3,700 Test Method
High Temperature Resistance (°C) 82 Low Temperature Resistance (°C) -54
Specific Gravity 1.06 (g/ml)
Shelf Life Details For short term storage (<30 days), keep adhesive in a cool (60°F to 80°F [16°C to 27°C]), dry place out of direct sunlight. Keep containers tightly covered and free of moisture. Refrigeration (40°F [4°C]) gives optimum long term storage stability.;3M™ Scotch-Weld™ Super Fast Instant Adhesives can be expected to have a shelf life of 12 months from the date of shipment from 3M when stored under refrigerated conditions. Shelf Life Temperature (°F) 60 to 80, 40 Shelf Life Type From the date of Shipment Shelf Life (mon) 12
Best Practices for 3M Scotch-Weld Super Fast Instant Adhesive SF100
For optimum strength structural bonds, paint, oxide films, oils, dust, mold release agents, and all other surface contaminants must be completely removed. However, the amount of surface preparation depends on the required bond strength and the environmental aging resistance desired by the user. Typical quick surface preparation would include wiping with a clean solvent (such as isopropyl alcohol), abrading the surface with a clean fine abrasive, and then wiping again with a clean solvent to remove loose particles. Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow the manufacturer’s precautions and directions for use.
Ensure that parts are clean, dry, and free from oil and grease.
A instant adhesive activator may be required if there are bonding gaps or porous substrate surfaces, if substrates are low surface energy plastics (e.g., polyethylene, polypropylene) or if substrates have acidic surfaces (e.g., paper, leather).
Bond speed is typically very fast so ensure that parts are properly aligned before dispensing.
Product is normally hand applied from the bottle. Apply sparingly to one surface and press parts firmly together until handling strength is achieved. As a general rule, as little cyanoacrylate as possible should be used. Over application will result in slower cure speed and lower bond strength.
Full bond strength will typically be achieved within a 24 hour cure time.
Low humidity or low temperature conditions will slow down the cure rate.
After curing, 3M™ Scotch-Weld™ Super Fast Instant Adhesive bonds are suitable for use up to about 180°F (82°C). At 180°F (82°C) the bonds will be approximately 70% of the strength at room temperature and at 212°F (100°C) about 50% of full strength.
Cyanoacrylate bond resistance to most oils and solvents is excellent. Long term humidity, moisture, or water immersion may affect the strength of a cured cyanoacrylate bond depending on the substrates and the bond gap. Testing is recommended to evaluate the effect.
Comparable Materials for 3M Scotch-Weld Super Fast Instant Adhesive SF100
Spec Engine® Results
Closest Results from this Manufacturer
Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of MaterialsRead Article
Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:Read Article
Viscosity Test Methods
|71 to 95 cPs||ISO 3104/3105.|
Tensile Strength Test Methods
|Tensile Strength||Test Method|
|3,700 psi||ASTM D2095 (grit-blasted steel).|
Shear Strength Test Methods
|Shear Strength||Type||Substrate||Test Method|
|2,900 psi||Overlap shear Strength||ASTM D1002 (grit-blasted steel).|
|2,109 psi||Overlap Shear Strength||Steel||ASTM D-1002|
|2,266 psi||Overlap Shear Strength||Stainless Steel||ASTM D-1002|
|1,689 psi||Overlap Shear Strength||Aluminum||ASTM D-1002|
|914 psi||Overlap Shear Strength||ABS||ASTM D-1002|
|755 psi||Overlap Shear Strength||Polycarbonate||ASTM D-1002|
|1,096 psi||Overlap Shear Strength||PVC||ASTM D-1002|
|321 psi||Overlap Shear Strength||Nylon||ASTM D-1002|
|728 psi||Overlap Shear Strength||Polypropylene||ASTM D-1002|
|105 psi||Overlap Shear Strength||Silicone Elastomer||ASTM D-1002|
1 VIEW FREE
View 3M - Scotch-Weld Super Fast Instant Adhesive SF100 now.