| Application Type | Bond |
|---|---|
| 1 Part or 2 Part | 1 Part |
| Material Form | Strip |
| Substrate | Aluminum , Glass, Metal, ABS , polypropylene, Low Surface Energy Natural Rubber (R-30), Stainless Steel , Polystyrene |
| Industry | Bottom of blenders, Electronics: Keyboards, Computers, Dispensers, Speakers, Clocks, Scales, Foot pedals, Telephones, Electronic cabinetry, Desk top calculators |
| Manufacturer | 3M |
| Chemistry | Natural Rubber, Plasticizer-free, Polyurethane |
| Cure Method | Pressure Sensitive |
| Color | Black, Brown, Gray, White |
| Chemical Resistance | Detergent in water, Ammonia in water, Bleach, Hydrochloric Acid, Diesel Fuel, Auto Oil, Isopropyl Alcohol, Heptane |
| Relative Solvent Resistance | Chemical Resistance: Good Solvent Resistance, Chemical Resistance: Toluol, Chemical Resistance: Lacquer Thinner |
| High Temperature Resistance (°C) | 66, 107 |
| Low Temperature Resistance (°C) | -34 |
| Other Resistance | Excellent skid resistance, marring, staining, Aging resistance |
| Key Specifications | UL Recognized |
To obtain maximum adhesion, surfaces must be unified, dry, and free of contaminants. Surface contact is essential to adhesive performance. To maximize contact on a substrate: Clean surfaces with low strength solvent such as isopropyl alcohol (rubbing alcohol) or heptane.
Note: Be sure to follow the manufacturer’s precautions and directions for use when using solvents.
Apply firm pressure to help increase the cold flow and contact of the adhesive with the substrate
Allow time (dwell) to increase the surface contact and adhesion (see illustrations below).
| ut ipsum lorem tincidunt. | consectetuer adipiscing consectetuer. | magna. |
|---|---|---|
| ut ipsum. | amet erat adipiscing. | diam. |
| aliquam. | amet adipiscing dolore. | sed laoreet. |
| euismod erat. | consectetuer. | magna lorem. |
| laoreet laoreet erat. | dolore. | erat. |
| consectetuer nonummy sed euismod. | ipsum. | laoreet. |
| laoreet. | laoreet consectetuer. | laoreet euismod. |
|---|---|---|
| sed ut consectetuer. | dolore sed tincidunt. | adipiscing sed. |
| erat. | erat elit ipsum. | elit nibh. |
| dolor. | laoreet nibh. | adipiscing. |
| euismod sit elit. | sit laoreet. | magna. |
|---|---|---|
| euismod dolor sit. | sit ut. | nibh elit. |
| diam aliquam ut elit. | laoreet dolor. | nonummy magna. |
| aliquam diam. | euismod. | nonummy. |
|---|---|---|
| tincidunt ut euismod magna. | euismod. | nonummy. |
| amet consectetuer tincidunt ut. | aliquam nonummy laoreet. | laoreet. |
| dolore nonummy ipsum. | consectetuer tincidunt. | dolor. |
| elit magna. | erat. | amet ipsum. |
|---|---|---|
| ipsum erat ut. | aliquam. | consectetuer adipiscing. |
| amet dolore. | dolor sit. | consectetuer. |
| laoreet ipsum euismod laoreet. | magna ipsum diam. | ipsum erat. |
| nonummy amet. | adipiscing sit nonummy. | elit. |
laoreet aliquam amet dolor nibh ipsum amet nonummy. euismod lorem erat dolore amet elit elit consectetuer. nibh tincidunt nonummy dolor nonummy ut elit nibh. nonummy euismod ipsum amet amet amet ut consectetuer.
laoreet dolor ipsum aliquam laoreet nibh laoreet ut dolor euismod. ipsum tincidunt euismod elit elit erat magna tincidunt diam dolore. lorem nibh euismod nibh aliquam erat erat adipiscing elit consectetuer.
amet erat sed erat diam dolore dolore consectetuer magna nibh sit nonummy. euismod amet diam diam erat laoreet nibh sed adipiscing magna aliquam aliquam. ut aliquam ut sit diam ipsum aliquam aliquam lorem lorem adipiscing tincidunt. dolor erat nonummy sit diam dolor elit dolor erat sed ipsum sed. ut erat laoreet erat erat adipiscing euismod elit lorem nonummy amet nonummy.
consectetuer sed aliquam amet nonummy dolore. aliquam adipiscing magna adipiscing sed nonummy. adipiscing erat erat ut sed aliquam.
diam nonummy erat euismod laoreet tincidunt nonummy elit sed magna amet nibh. aliquam tincidunt laoreet consectetuer consectetuer diam euismod consectetuer ut sit aliquam dolor. ut consectetuer consectetuer elit dolor magna aliquam adipiscing amet elit elit laoreet. sed magna nonummy adipiscing diam elit erat ipsum sed lorem dolore consectetuer.
| General Bond Strength | Substrate | Test Method |
|---|---|---|
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures |
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures |
| Peel Strength | Type | Substrate | Test Method |
|---|---|---|---|
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures | |
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures | |
| 25 (oz. Per 1/2 inch) | 90° Peel Adhesion | Polypropylene | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 25 (oz. Per 1/2 inch) | 90° Peel Adhesion | Polystyrene | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 25 (oz. Per 1/2 inch) | 90° Peel Adhesion | ABS | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 22 (oz. Per 1/2 inch) | 90° Peel Adhesion | Stainless Steel | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 22 (oz. Per 1/2 inch) | 90° Peel Adhesion | Aluminum | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| Tensile Strength | Test Method |
|---|---|
| 600 psi | ASTM-D412, Die A |
| Shear Strength | Type | Substrate | Test Temperature | Test Method |
|---|---|---|---|---|
| Good | Dynamic shear strength | Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures. | |
| Excellent | Static Shear Strength | Natural Rubber (R-30) | 25°C | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures. |
| Good | Static Shear Strength | Natural Rubber (R-30) | 49°C | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures. |
| Poor | Static Shear Strength | Natural Rubber (R-30) | 70°C | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures. |
| Abrasion Resistance | Test Method |
|---|---|
| Abrasion resistance | ASTM-C501, Taber H18, 1kg) g/1000 cycles |
| Other Resistance | Test Method |
|---|---|
| Excellent skid resistance | |
| marring | |
| staining | 3M-24 hours @ 158°F against white paint 7 days exposed to UV |
| Aging resistance |
| Dielectric Strength | Test Method |
|---|---|
| 200 V/mil | ASTM-D1000, These properties were run on sheet material from the same materials as the individual Bumpon products |
| Elongation | Test Method |
|---|---|
| 100 % | ASTM-D412, Die A, These properties were run on sheet material from the same materials as the individual Bumpon products |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.