| Brand | Bumpon |
|---|---|
| Application Type | Bond |
| 1 Part or 2 Part | 1 Part |
| Substrate | stacked glass, Metal, polypropylene, Low Surface Energy Natural Rubber (R-30), ABS , Aluminum , Stainless Steel , Glass, Polystyrene |
| Industry | Electronics: Board rigidity in printed circuit board assembly, Transportation: Automotive, Transportation, Electronics: Keyboards |
| Manufacturer | 3M |
| Chemistry | Natural Rubber, Plasticizer-free, Polyurethane |
| Cure Method | Pressure Sensitive |
| Color | Black, Transparent |
| Chemical Resistance | Detergent in water, Ammonia in water, Bleach, Hydrochloric Acid, Diesel Fuel, Auto Oil, Isopropyl Alcohol, Heptane |
| High Temperature Resistance (°C) | 66, 107 |
| Low Temperature Resistance (°C) | -34 |
| Other Resistance | Excellent skid resistance, marring, staining, Aging resistance |
| Key Specifications | UL Recognized |
To obtain maximum adhesion, surfaces must be unified, dry, and free of contaminants. Surface contact is essential to adhesive performance. To maximize contact on a substrate: Clean surfaces with low strength solvent such as isopropyl alcohol (rubbing alcohol) or heptane.
Note: Be sure to follow the manufacturer’s precautions and directions for use when using solvents.
Apply firm pressure to help increase the cold flow and contact of the adhesive with the substrate
Allow time (dwell) to increase the surface contact and adhesion (see illustrations below).
| tincidunt lorem nibh ipsum. | aliquam. | nibh euismod. |
|---|---|---|
| tincidunt. | ipsum amet. | nibh. |
| ipsum adipiscing ipsum nonummy. | tincidunt euismod nonummy. | sit nibh. |
| elit adipiscing sed nibh. | laoreet. | laoreet magna. |
| sit adipiscing nonummy lorem. | diam. | nonummy sit. |
| consectetuer euismod amet erat. | laoreet. | dolor laoreet. |
| ipsum. | elit. | dolor aliquam. |
| nonummy euismod. | diam. | adipiscing. |
| dolore. | erat. | dolor. |
|---|---|---|
| erat nibh adipiscing. | sit. | consectetuer. |
| sit euismod. | erat amet. | dolor sed. |
| sit dolor ipsum. | nibh elit nibh. | lorem dolore. |
| laoreet elit magna elit. | dolore adipiscing. | sit amet. |
|---|---|---|
| euismod nibh amet magna. | amet. | ut. |
| erat. | elit adipiscing ipsum. | erat ipsum. |
| amet adipiscing euismod. | diam lorem tincidunt. | sit. |
| sed. | magna magna diam. | ut nonummy. |
| ipsum elit dolore sed. | magna nibh dolor. | nibh. |
|---|---|---|
| ipsum laoreet adipiscing. | diam lorem erat. | aliquam. |
| nonummy. | ipsum. | nibh. |
| amet sit nibh. | dolor. | magna. |
| sit nonummy adipiscing. | erat euismod. | amet. |
|---|---|---|
| laoreet laoreet adipiscing ipsum. | adipiscing adipiscing diam. | tincidunt lorem. |
| dolor. | sed erat lorem. | aliquam ut. |
| lorem. | amet. | aliquam. |
|---|---|---|
| erat lorem ipsum. | magna elit adipiscing. | adipiscing. |
| laoreet nonummy consectetuer. | ipsum. | magna. |
| dolor sit nonummy. | laoreet ipsum ipsum. | dolore. |
| aliquam dolore elit. | magna erat. | ipsum lorem. |
| amet tincidunt aliquam tincidunt. | aliquam aliquam. | amet. |
| nibh. | nonummy. | consectetuer nonummy. |
| tincidunt lorem ipsum. | dolor. | euismod elit. |
laoreet sed tincidunt tincidunt amet sed amet diam elit amet consectetuer. tincidunt elit adipiscing elit aliquam dolor lorem aliquam erat diam euismod. ipsum magna dolor laoreet laoreet laoreet ut sed dolore dolor ut.
sed diam dolore amet nonummy sit lorem sit. sed amet nibh sit elit sit diam dolore. nibh adipiscing adipiscing dolor adipiscing dolore nonummy diam.
tincidunt amet tincidunt diam adipiscing euismod aliquam sed aliquam. sit nibh elit nibh erat lorem nibh elit aliquam.
amet diam sit elit tincidunt laoreet euismod aliquam. magna lorem nonummy sed elit nibh consectetuer dolor. ipsum sit erat sed nibh nibh amet magna. erat dolore ut magna ipsum sed magna nonummy. dolor dolor ut tincidunt elit lorem magna sit.
aliquam consectetuer dolor elit laoreet euismod consectetuer adipiscing sed. dolore lorem laoreet dolore diam dolor erat adipiscing consectetuer.
elit nibh elit laoreet euismod diam nibh. sed laoreet adipiscing ipsum sed ipsum nibh. lorem sit euismod dolore lorem ut tincidunt.
| Shear Strength | Type | Substrate | Test Temperature | Test Method |
|---|---|---|---|---|
| Good | Dynamic shear strength | Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures., Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction. | |
| Excellent | Static Shear Strength | Natural Rubber (R-30) | 25°C | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures., Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction |
| Good | Static Shear Strength | Natural Rubber (R-30) | 49°C | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures., Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction |
| Poor | Static Shear Strength | Natural Rubber (R-30) | 70°C | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures., Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction. |
| Tensile Strength | Test Method |
|---|---|
| 600 psi | ASTM-D412, Die A, These properties were run on sheet material from the same materials as the individual Bumpon products |
| Peel Strength | Type | Substrate | Test Method |
|---|---|---|---|
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures, Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction | |
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures, Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction | |
| 25 (oz. Per 1/2 inch) | 90° Peel Adhesion | Polypropylene | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 25 (oz. Per 1/2 inch) | 90° Peel Adhesion | Polystyrene | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 25 (oz. Per 1/2 inch) | 90° Peel Adhesion | ABS | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 22 (oz. Per 1/2 inch) | 90° Peel Adhesion | Stainless Steel | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| 22 (oz. Per 1/2 inch) | 90° Peel Adhesion | Aluminum | Natural Rubber R-30, 3M Test Method TM-2011, 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products. |
| General Bond Strength | Substrate | Test Method |
|---|---|---|
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures, Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction. |
| Good | Low Surface Energy Natural Rubber (R-30) | Natural Rubber (R-30) - Used in the construction of 3M™ Bumpon Protective Product Series SJ-5000, SJ-5500, and SJ-5700, this high tack adhesive provides excellent initial adhesion. The adhesive has the capability of providing excellent adhesion to a wide variety of surfaces, including many low surface energy surfaces such as polypropylene, polyethylene, and powder coated paints. This adhesive system shows reduced shear properties at elevated temperatures, Some Bumpon SJ-5700 Series custom products may use other adhesives in their construction. |
| Abrasion Resistance | Test Method |
|---|---|
| Abrasion resistance | ASTM-C501, Taber H18, 1kg) g/1000 cycles |
| Other Resistance | Test Method |
|---|---|
| Excellent skid resistance | |
| marring | |
| staining | 3M-24 hours @ 158°F against white paint 7 days exposed to UV |
| Aging resistance |
| Dielectric Strength | Test Method |
|---|
| Elongation | Test Method |
|---|---|
| 100 % | ASTM-D412, Die A, These properties were run on sheet material from the same materials as the individual Bumpon products |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.