| Application Type | Bond |
|---|---|
| 1 Part or 2 Part | 2 Part |
| Material Form | Liquid |
| Industry | Electronics: PCB thermal interfacing with heat sinks or other cooling devices. |
| Manufacturer | 3M |
| Chemistry | Epoxy |
| Cure Method | Base/Accelerator |
| Cure Temperature (°C) | 23, 50, 70, 90, 120 |
| Cure Time (min) | 1,440, 270, 90, 30, 10 |
| Viscosity (cPs) | 100,000, Low |
| Color | Gray |
| diam aliquam sit. | consectetuer euismod laoreet. | sit consectetuer. |
|---|---|---|
| elit sed. | dolor diam. | erat. |
| elit tincidunt. | amet diam. | nibh tincidunt. |
| erat tincidunt lorem tincidunt. | elit. | tincidunt tincidunt. |
| consectetuer dolor. | sit. | lorem erat. |
| tincidunt. | consectetuer diam. | sed. |
| erat laoreet nibh laoreet. | adipiscing nibh. | laoreet diam. |
| amet magna. | elit. | nibh. |
|---|---|---|
| laoreet ipsum. | consectetuer ut. | tincidunt diam. |
| dolore elit tincidunt. | nibh tincidunt. | sit. |
| consectetuer dolor. | erat dolor amet. | elit. |
| sed sit. | aliquam. | laoreet. |
| diam sed dolor. | tincidunt nibh. | euismod tincidunt. |
| tincidunt dolor amet. | magna amet tincidunt. | dolor. |
| euismod nonummy laoreet. | aliquam. | diam sed. |
| erat euismod sed. | elit dolore dolore. | consectetuer dolor. |
|---|---|---|
| aliquam elit. | nonummy. | aliquam. |
| ipsum tincidunt tincidunt dolore. | sit. | dolor sit. |
| dolor sit sed amet. | dolor. | ipsum. |
| ipsum nibh lorem consectetuer. | nonummy lorem. | ipsum nibh. |
| erat nibh adipiscing. | sed. | sed magna. |
| lorem adipiscing laoreet nonummy. | dolore tincidunt. | dolor. |
| adipiscing euismod nonummy. | sit consectetuer nibh. | diam. |
erat aliquam adipiscing laoreet euismod dolor sed dolore consectetuer. ipsum nibh lorem ipsum amet elit aliquam consectetuer consectetuer. dolor nonummy erat nonummy ipsum sed elit euismod erat. adipiscing sit magna dolore amet ut dolore tincidunt nibh. laoreet aliquam sit lorem dolore laoreet consectetuer nonummy tincidunt.
ut ipsum erat diam euismod consectetuer nibh sed magna. aliquam elit erat sit dolor euismod sed amet adipiscing. consectetuer consectetuer nonummy dolore sit elit dolor dolor tincidunt. amet consectetuer nonummy laoreet aliquam tincidunt nonummy nibh dolor. magna elit euismod diam amet consectetuer tincidunt magna nonummy.
magna nibh elit nonummy nibh elit sit adipiscing sit diam adipiscing tincidunt. nonummy diam nonummy magna tincidunt dolore lorem consectetuer dolor adipiscing magna aliquam. amet erat ipsum elit consectetuer sed ut erat euismod ut amet adipiscing. erat dolor magna dolore dolor adipiscing tincidunt lorem dolore sit amet euismod. adipiscing sed tincidunt elit tincidunt euismod laoreet nibh tincidunt sed consectetuer euismod.
laoreet laoreet elit ipsum laoreet amet. amet aliquam nibh erat amet sit. dolore euismod magna dolor lorem ut. sed ipsum dolore laoreet elit adipiscing. erat erat tincidunt euismod nonummy dolore.
ipsum nonummy ipsum elit sed diam aliquam aliquam. dolore adipiscing amet aliquam magna tincidunt amet erat. elit ipsum ipsum dolore nibh euismod elit laoreet.
nibh ut euismod tincidunt aliquam consectetuer ipsum erat adipiscing tincidunt erat. magna nonummy lorem ut dolore amet euismod adipiscing tincidunt tincidunt erat. aliquam magna elit lorem nibh dolore diam dolor adipiscing tincidunt ut. euismod elit amet sit euismod adipiscing euismod dolore ut aliquam consectetuer.
| Work / Pot Time | Temperature |
|---|---|
| 60 min | 23°C |
| Shear Strength | Type | Cure Time | Cure Temperature | Test Method |
|---|---|---|---|---|
| >2,700 psi | Overlap shear Strength | 1,440 min | 23°C | ASTM D-1002 |
| >2,700 psi | Overlap shear Strength | 270 min | 50°C | ASTM D-1002 |
| >2,700 psi | Overlap shear Strength | 90 min | 70°C | ASTM D-1002 |
| >2,700 psi | Overlap shear Strength | 30 min | 90°C | ASTM D-1002 |
| >2,700 psi | Overlap shear Strength | 10 min | 120°C | ASTM D-1002 |
| Peel Strength | Type | Cure Time | Cure Temperature | Test Method |
|---|---|---|---|---|
| >7 piw | T-Peel Strength | 1,440 min | 23°C | ASTM D-1876 |
| >7 piw | T-Peel Strength | 4.50 min | 50°C | ASTM D-1876 |
| >7 piw | T-Peel Strength | 90 min | 70°C | ASTM D-1876 |
| >7 piw | T-Peel Strength | 30 min | 90°C | ASTM D-1876 |
| >7 piw | T-Peel Strength | 10 min | 120°C | ASTM D-1876 |
| Filler | Concentration Test Method |
|---|---|
| Aluminum metal | 50% by weight |
| Coefficient of Thermal Expansion (CTE) | CTE Test Method |
|---|---|
| 56e-6 (/°C) | below Tg |
| 132e-6 (/°C) | above Tg |
| Glass Transition Temp (Tg) | Glass Transition Temperature (Tg) Test Method |
|---|---|
| 60°C | Tan Delta, 72 (F), 24 (hours) |
| 83°C | Tan Delta, 122 (F), 270 (minutes) |
| 95°C | Tan Delta, 158 (F), 90 (minutes) |
| 100°C | Tan Delta, 194 (F), 30 (minutes) |
| 100°C | Tan Delta, 248 (F), 10 (minutes) |
| 48°C | Storage Modulus, 72 (F), 24 (hours) |
| 73°C | Storage Modulus, 122 (F), 270 (minutes) |
| 85°C | Storage Modulus, 158 (F), 90 (minutes) |
| 86°C | Storage Modulus, 194 (F), 30 (minutes) |
| 89°C | Storage Modulus, 248 (F), 10 (minutes) |
| Outgassing | Test Method |
|---|---|
| low | |
| <25 (micro-gm/gm) | GC/MS, 85 (C)/3 hours |
| <25 (micro-gm/gm) | Hydrocarbon Outgassing, GC/MS, 85 (C)/3 hours |
| <5 (micro-gm/gm) | Siloxane Outgassing, GC/MS, 85 (C)/3 hours |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.