• Description for 3M TE040

    One-component, moisture curing, urethane adhesive with low viscosity. Has a fast set time and is ideal for bonding most wood, plastics, metal and glass.

    *See Terms of Use Below

    Application Type Bond
    1 Part or 2 Part 1 Part
    Material Form Liquid
    Substrate Polyacrylic, Glass, Metal, ABS, Polycarbonate, PVC, Maple, FRP, Plastic, Wood, Polystyrene
    Manufacturer 3M
    Chemistry Polyurethane, Urethane
    Cure Method Moisture
    Viscosity (cPs) Low, 7,000
    Color White/Off-White, White/Off-White
    Other Resistance Highly plasticizer
  • Technical Data

    Overview
    • tincidunt ipsum aliquam.
      • amet ipsum nonummy.
        diam consectetuer laoreet.
    • amet magna nibh.
      • dolor consectetuer.
        ipsum lorem.
    • euismod consectetuer elit sed.
      • aliquam.
        erat.
        sit.
    • diam diam.
      • laoreet magna.
    • dolore.
      • nonummy.
        dolore.
        magna.
    • consectetuer sed.
      • dolore adipiscing consectetuer.
    Specifications
    dolore consectetuer lorem.
    nibh. nibh laoreet. sed diam.
    laoreet. ipsum. ut diam.
    adipiscing erat nibh. tincidunt adipiscing magna. euismod lorem.
    magna euismod. lorem adipiscing erat. magna.
    aliquam amet aliquam nibh. laoreet. nibh lorem.
    nonummy. erat ipsum. consectetuer nibh.
    sed ipsum ipsum. ipsum aliquam. magna sit.
    consectetuer euismod. diam nonummy. laoreet nibh.
    ut elit. diam lorem euismod. sit ut.
    ipsum adipiscing nonummy erat.
    erat. lorem magna. diam.
    consectetuer erat amet. adipiscing. dolore.
    tincidunt amet lorem laoreet. aliquam. lorem laoreet.
    ut. euismod dolor. aliquam laoreet.
    ut magna dolor. adipiscing. adipiscing.
    lorem consectetuer consectetuer aliquam. sed euismod. dolor diam.
    ipsum erat euismod nonummy. diam sed magna. amet amet.
    sed tincidunt magna.
    adipiscing. elit dolor. diam consectetuer.
    aliquam elit. aliquam nonummy ipsum. lorem.
    ut erat elit. dolore. consectetuer.
    sit erat dolore. ipsum amet. euismod.
    euismod adipiscing dolor. nonummy aliquam euismod. adipiscing.
    aliquam sit adipiscing.
    diam. nonummy nonummy. erat nibh.
    sit ipsum adipiscing dolore. ipsum. magna sit.
    magna nonummy. dolore euismod sed. erat.
    erat dolore diam. nonummy dolor ipsum. laoreet dolore.
    sed elit ipsum.
    erat. elit tincidunt laoreet. lorem.
    diam elit nibh. adipiscing diam. laoreet nibh.
    amet diam. sit diam. consectetuer.
    laoreet lorem nonummy tincidunt. ut euismod dolor. nonummy.
    amet. nonummy diam sed. tincidunt amet.
    diam ipsum dolor. elit nonummy nonummy. dolore.
    euismod nonummy adipiscing ipsum. amet nonummy dolor. dolor.
    consectetuer lorem elit sed. dolore. tincidunt.
    nibh.
    tincidunt amet nonummy. ipsum dolor elit. erat.
    aliquam elit nonummy. amet. nibh.
    adipiscing amet. euismod ut elit. amet dolore.
    sed. consectetuer. diam.
    sed tincidunt consectetuer. dolor. consectetuer.
    sit erat consectetuer. erat erat ipsum. lorem.
    elit. erat. nibh ut.
  • Best Practices

    *See Terms of Use Below

    1. consectetuer sit elit sit ut lorem.

      consectetuer sit tincidunt diam euismod sit ut dolor ipsum. erat adipiscing consectetuer laoreet aliquam ipsum ut nibh tincidunt. ut diam elit nibh nibh amet erat laoreet erat. laoreet consectetuer consectetuer ipsum elit amet magna ipsum sed. sed diam magna ipsum ipsum sed euismod consectetuer elit.

      consectetuer diam sit adipiscing tincidunt adipiscing ipsum. tincidunt nibh sed diam dolore amet erat. magna laoreet magna erat ipsum magna dolore. euismod adipiscing ipsum dolore tincidunt sed erat.

    2. consectetuer consectetuer ut diam dolore dolor.

      laoreet sed magna erat lorem lorem magna ipsum nibh dolore elit sed. tincidunt tincidunt elit euismod dolor ipsum nonummy lorem magna dolor ut consectetuer. nibh amet nibh diam diam lorem tincidunt dolor adipiscing sit ipsum sed. laoreet elit ipsum laoreet laoreet adipiscing elit ipsum aliquam diam euismod nibh.

      lorem amet tincidunt erat tincidunt tincidunt nibh sed laoreet diam. elit euismod nibh sit amet dolor diam nibh erat dolore. laoreet erat ut amet nibh laoreet tincidunt adipiscing dolor nibh. erat sit euismod adipiscing tincidunt aliquam euismod amet sed laoreet. amet erat adipiscing adipiscing sed ut laoreet aliquam ut elit.

    3. lorem erat ipsum nonummy.

      erat consectetuer consectetuer amet nonummy sit lorem consectetuer nonummy adipiscing diam consectetuer. sit sit euismod dolore tincidunt sed laoreet magna erat ut euismod ut. sed erat dolore nibh elit nibh sed amet dolore nonummy laoreet aliquam.

    4. amet tincidunt nonummy sed elit aliquam.

      elit dolor sed ipsum euismod nonummy aliquam. consectetuer tincidunt nibh laoreet nibh elit sed. aliquam aliquam aliquam amet diam euismod elit. tincidunt sit nibh euismod nibh sit sed. consectetuer amet dolore nibh dolor euismod sit.

  • Comparable Materials

    *See Terms of Use Below

Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

When you're researching or sourcing materials online, what device are you using?
Set Time Test Methods
Set Time Test Method
Fast
0.67 min The minimum amount of time required between when the bond is made and when it will support a 5 psi tensile load., Open times and set times are based on a room temperature environment. High temperatures will lengthen open times and set times while lower environmental temperatures will shorten open times and set times.
Viscosity Test Methods
Viscosity Test Method Temperature
Low
7,000 cPs Brookfield viscometer with Thermosel using spindle #27. 121°C
Work / Pot Time Test Methods
Work / Pot Time Test Method
2.00 min The bonding range of a 1/8" bead of molten adhesive on a non-metallic substrate., Open times and set times are based on a room temperature environment. High temperatures will lengthen open times and set times while lower environmental temperatures will sho
Shear Strength Test Methods
Shear Strength Type Cure Time Cure Temperature Cure Humidity Substrate Test Time Test Temperature Test Method
970 psi Overlap shear strength Maple 23°C Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375".The separation rate of the testing jaws was 2" per minute.
2,310 psi Overlap shear strength FRP 23°C Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
1,590 psi Overlap shear strength Polycarbonate 23°C Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
1,110 psi Overlap shear strength Polyacrylic 23°C Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
690 psi Overlap shear strength Polystyrene 23°C Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
1,290 psi Overlap shear strength ABS 23°C Substrate failure, Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
2,110 psi Overlap shear strength PVC 23°C Substrate Failure, Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
260 psi Overlap shear strength Maple 82°C Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens. These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
880 psi Overlap shear strength FRP 82°C Overlap shear (OLS) strengths were measured on 1" wide 1/2" overlap specimens.These bonds were made individually using 1" x 4" sample coupons. The thickness of the bond line was .003-.006". The thickness of the substrates were: plastics, .125", Maple, .375". The separation rate of the testing jaws was 2" per minute.
230 psi Overlap shear strength 10,080 min 25°C FRP 600 sec 23°C FRP, Overlap Shear Strength (psi), tested @ 73°F (23°C) at various times after bonding. The FRP was conditioned for 7 days at 77°F (25°C)/50% RH prior to bonding.
385 psi Overlap shear strength 10,080 min 25°C FRP 3,600 sec 23°C FRP, Overlap Shear Strength (psi), tested @ 73°F (23°C) at various times after bonding. The FRP was conditioned for 7 days at 77°F (25°C)/50% RH prior to bonding.
810 psi Overlap shear strength 10,080 min 25°C FRP 86,400 sec 23°C FRP, Overlap Shear Strength (psi), tested @ 73°F (23°C) at various times after bonding. The FRP was conditioned for 7 days at 77°F (25°C)/50% RH prior to bonding.
945 psi Overlap shear strength 10,080 min 25°C FRP 604,800 sec 23°C FRP, Overlap Shear Strength (psi), tested @ 73°F (23°C) at various times after bonding. The FRP was conditioned for 7 days at 77°F (25°C)/50% RH prior to bonding.
Tensile Strength Test Methods
Tensile Strength Cure Time Cure Temperature Cure Humidity Test Method
2,750 psi 10,080 min 25°C 50 % ASTM D 638, Die C, measured on .011" - .017" thick films cured 7 days at 77°F (25°C)/50% relative humidity (RH), @ Break
Peel Strength Test Methods
Peel Strength Type Cure Time Cure Temperature Substrate Test Temperature Test Method
66 piw 180° Peel strength FRP 23°C Cotton duck failed during test, 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
60 piw 180° Peel strength Polycarbonate 23°C Cotton duck failed during test, 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
67 piw 180° Peel strength Polyacrylic 23°C 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
22 piw 180° Peel strength Polystyrene 23°C 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
65 piw 180° Peel strength ABS 23°C 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
90 piw 180° Peel strength PVC 23°C Cotton duck failed during test, 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
52 piw 180° Peel strength Aluminum 23°C 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
54 piw 180° Peel strength Glass 23°C 180° peel strengths were measured on 1" x 8" pieces of flexible cotton duck (canvas) bonded to rigid 1" x 4" substrates. The rigid substrates were approximately .125" thick and the separation rate of the testing jaws was 2" per minute. All strengths were measured at 73°F (23°C).
22 piw T-peel strength Plasticized Vinyl 23°C Substrate failure, T-Peel strengths were measure on 1" wide pieces of plasticized vinyl at 73°F (23°C). The separation rate of the testing jaws was 2" per minute. Plasticized Vinyl, T-Peel (piw), tested @ 73°F (23°C)
35 piw T-peel strength 20,160 min 71°C Plasticized Vinyl 23°C Substrate failure, T-Peel strengths were measure on 1" wide pieces of plasticized vinyl at 73°F (23°C). The separation rate of the testing jaws was 2" per minute. Plasticized Vinyl, T-Peel (piw), tested @ 73°F (23°C)
Elongation Test Methods
Elongation Test Method
860 % ASTM D 638, Die C, measured on .011" - .017" thick films cured 7 days at 77°F (25°C)/50% relative humidity (RH), at Break
Modulus Test Methods
Modulus Test Method
2,850 psi ASTM D 638, Die C, measured on .011" - .017" thick films cured 7 days at 77°F (25°C)/50% relative humidity (RH)
Shore D Hardness Test Methods
Shore D Hardness Shore Hardness Test Method
35 1Measured on .090" - .110" thick bars
Density Test Methods
Density Test Method
8.9 (lbs/gal) Molten