Description for Bostik 2100 SPS
One part adhesive/sealant; fast cure, superior adhesion to porous and non-porous surfaces and is non yellowing.Application Type Bond, Maintenance, Seal, Repair 1 Part or 2 Part 1-Part Material Form Paste Substrate Porous substrates Industry Transportation, Utility trailers, Light rail units, Buses, Truck trailer, RV, Truck trailer, Utility trailers, Trailer vans Manufacturer Bostik Chemistry Porous and non-porous Cure Method Moisture Cure Temperature (°C) 25 Cure Time (min) 1,440, Fast Viscosity (cPs) Non-sag Ozone Resistance Very good ozone resistance Aging Resistance Good aging resistance High Temperature Resistance (°C) 99, Good Heat resistance Low Temperature Resistance (°C) -40 -
Technical Data for Bostik 2100 SPS
Overview
-
Application Type
- Adhesive - Bond
- Repair & Maintenance - Maintenance, Repair
- Sealant - Seal
-
1 Part or 2 Part
- 1-Part
-
Material Form
- Paste
-
Substrate
- Porous Substrates
-
Industry
- Transportation
- Other Transportation - Roofs, Sidewalls
- Utility - Utility trailers
- Rail - Light rail units
- Bus - Buses
- Trucks - Truck trailer
- Recreational Vehicles - RV
- Trailer - Trailer vans, Truck trailer, Utility trailers
- Construction
-
Chemistry
- Other - Porous and non-porous
-
Cure Method
- Moisture / Condensation Cure - Moisture
Specifications
Cure Specs
Cure Temperature (°C) 25 Test Method Cure Time (min) 1,440, Fast Test Method Viscosity (cPs) Non-sag Work / Pot Time (min) 45, 60 Thixotropic Slump Bond Strength
General Bond Strength (psi) Superior Peel Strength (piw) >20 Test Method Tensile Strength (psi) 175 Test Method Material Resistance
Ozone Resistance Very good ozone resistance Aging Resistance Good aging resistance UV Resistance Very Good High Temperature Resistance (°C) 99, Good Heat resistance Low Temperature Resistance (°C) -40 Hardness
Shore A Hardness 30 Test Method Elongation (%) >400 Test Method Modulus (psi) 75 Test Method Business Information
Shelf Life Details When stored at or below 80°F (27°C), Bostik® 2100 SPS has a shelf life of twelve months from the date of shipment from Bostik's warehouse facilities. Shelf Life Temperature (°F) <81 Shelf Life Type From date of shipment Shelf Life (mon) 12 Not Good For
Don't Use For not recommended to be subjected to traffic. -
-
Best Practices for Bostik 2100 SPS
-
Application
Bostik® 2100 SPS is not recommended to be subjected to traffic.
Bostik® 2100 SPS is not intended to be used as a glazing sealant.
-
Curing
Bostik® 2100 SPS requires atmospheric air and moisture to properly cure.
-
Clean-Up
Uncured Bostik® 2100 SPS may be easily removed from hands and tools with Bostik® Hand & Tool Towels. Cured 2100 SPS must be removed by mechanical means such as scrapers.
-
-
Comparable Materials for Bostik 2100 SPS
Spec Engine® Results
Closest Results from this Manufacturer
Popular Articles
Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation
Read ArticleAnaerobic Adhesives
Read ArticleWhat Are the Differences Between Adhesives and Sealants?
Read ArticleTesting the effectiveness of surface treatments
Read ArticleSponsored Articles
Unique Advantages of Contact Adhesives
Read ArticleUsing LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials
Read ArticleSylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:
Read ArticleCase Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive
Read ArticleFeatured Ads

Cure Temperature Test Methods
Cure Temperature | Cure Time Test Method |
---|---|
25°C | 0.25 in. @77°F |
Cure Time Test Methods
Cure Time | Test Method |
---|---|
1,440 min | 0.25 in. @77°F |
Fast |
Peel Strength Test Methods
Peel Strength | Cure Time | Cure Temperature | Cure Humidity | Test Method |
---|---|---|---|---|
>20 piw | 20,160 min | 25°C | 50 % | after 14 days cure at 77°F and 50% RH |
Tensile Strength Test Methods
Tensile Strength | Cure Time | Cure Temperature | Cure Humidity | Test Method |
---|---|---|---|---|
175 psi | 20,160 min | 25°C | 50 % | after 14 days cure at 77°F and 50% RH |
Elongation Test Methods
Elongation | Test Method |
---|---|
>400 % | after 14 days cure at 77°F and 50% RH, at break |
Modulus Test Methods
Modulus | Test Method |
---|---|
75 psi | @ 100% Elongation, after 14 days cure at 77°F and 50% RH |
Shore A Hardness Test Methods
Shore A Hardness | Shore Hardness Test Method | Hardness Temperature |
---|---|---|
30 | After 14 days cure at 77°F and 50% RH | 25°C |