Bostik 920 FS Urethane

Bostik 920 FS Urethane Datasheet
BUY ONLINE

  • Description for Bostik 920 FS Urethane

    Outstanding weather resistance; strong flexible bonds.

    *See Terms of Use Below

    Application Type Bond, Seal
    1 Part or 2 Part 1 Part
    Material Form Paste
    Substrate Aluminum, FRP, Metal, Plastics, Woods
    Industry Marine, Sealing window, Sealing door
    Manufacturer Bostik
    Chemistry Urethane
    Cure Method Moisture
    Cure Temperature (°C) 25, 25
    Cure Time (min) Fast, 2,160 to 4,320, 20,160
    Ozone Resistance Excellent Ozone resistance
    High Temperature Resistance (°C) 82
    Low Temperature Resistance (°C) -40
    Durability Tough

  • Technical Data for Bostik 920 FS Urethane

    *See Terms of Use Below

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 1 Part or 2 Part - 1 Part
    • Material Form
      • Paste
    • Substrate
    • Industry
      • Other Transportation - Hull seams
      • Marine
      • Industrial - Keel joints, Under moldings
      • Construction - Deck
      • Construction Window - Sealing window
      • Construction Door - Sealing door
    • Chemistry
    • Application Method
      • Dispenser - Gun
    • Cure Method
      • Moisture / Condensation Cure - Moisture
    Specifications
    Cure Specs
    Cure Temperature (°C) 25, 25 Test Method
    Cure Time (min) Fast, 2,160 to 4,320, 20,160 Test Method
    Set Time (min) Fast
    Tack Free Time (min) 90
    Work / Pot Time (min) 70
    Bond Strength
    Peel Strength (piw) >25 Test Method
    Tensile Strength (psi) 267 Test Method
    Material Resistance
    Ozone Resistance Excellent Ozone resistance
    UV Resistance Good
    Environmental Resistance Outstanding weather resistance
    High Temperature Resistance (°C) 82
    Low Temperature Resistance (°C) -40
    Hardness
    Durability Tough
    Shore A Hardness 37 Test Method
    Elongation (%) 850 Test Method
    Flexibility Permanent elastomeric, Strong Flexible
    Modulus (psi) 65 Test Method
    Business Information
    Shelf Life Details When stored at or below 80°F (27°C), Bostik Marine 920 FS polyurethane sealant has a shelf life of nine months from date of manufacture.
    Shelf Life Temperature (°F) <81
    Shelf Life Type From date of manufacture
    Shelf Life (mon) 9

  • Best Practices for Bostik 920 FS Urethane

    *See Terms of Use Below

    1. Clean-Up

      Use Bostik® Hand & Tool Towels to clean excess sealant from all surfaces and tools while still uncured. Cured sealant can be removed with a sharp blade. NOTE: Cured sealant is usually very difficult to remove without altering or damaging the surface to which the sealant was applied.

  • Comparable Materials for Bostik 920 FS Urethane

    *See Terms of Use Below

    Spec Engine® Results

  Download Technical Data Sheet   Save This Material Saved Items

Questions about this material?

Bostik - 920 FS Urethane

Get personal assistance with your specific application needs.

Your Profile Edit
Submit

Popular Articles

Anaerobic Adhesives

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

What Are the Differences Between Adhesives and Sealants?

Read Article

Testing the effectiveness of surface treatments

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

Which answer best describes a project you are currently working on?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
25°C 77°F AND 50% RH
25°C AFTER 14 DAYS CURE AT 77°F AND 50% RH
Cure Time Test Methods
Cure Time Test Method
Fast
2,160 to 4,320 min 77°F AND 50% RH
20,160 min AFTER 14 DAYS CURE AT 77°F AND 50% RH
Peel Strength Test Methods
Peel Strength Cure Time Cure Temperature Cure Humidity Test Method
>25 piw 20,160 min 25°C 50 % AFTER 14 DAYS CURE AT 77°F AND 50% RH
Tensile Strength Test Methods
Tensile Strength Cure Time Cure Temperature Cure Humidity Substrate Test Method
267 psi 20,160 min 25°C 50 % Aluminum to Aluminum AFTER 14 DAYS CURE AT 77°F AND 50% RH
Elongation Test Methods
Elongation Test Method
850 % After 14 days cure at 77°F and 50% RH
Modulus Test Methods
Modulus Test Method
65 psi @ 100% Elongation, After 14 days cure at 77°F and 50% RH
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method Hardness Temperature
37 After 14 days cure at 77°F and 50% RH 25°C