Bostik Liquid Rivet 1152 FS Urethane Adhesive/Sealant

Bostik Liquid Rivet 1152 FS Urethane Adhesive/Sealant Datasheet
  • Description for Bostik Liquid Rivet 1152 FS Urethane Adhesive/Sealant

    One part, polyurethane, moisture cure, high thixotropy and cured strength. Very high green strength and initial tack.

    *See Terms of Use Below

    Application Type Bond, Seal
    1 Part or 2 Part 1 Part
    Material Form Liquid
    Substrate Aluminum, Stainless Steel, Plywood, FRP
    Industry Vehicle frames
    Manufacturer Bostik
    Chemistry Polyurethane, Urethane
    Cure Method Moisture
    Cure Temperature (°C) 25
    Cure Time (min) 1,440, >20,160
    Color Black, White
    High Temperature Resistance (°C) 190
    Low Temperature Resistance (°C) -40
  • Technical Data for Bostik Liquid Rivet 1152 FS Urethane Adhesive/Sealant

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 1 Part or 2 Part - 1 Part
    • Material Form
      • Liquid
    • Substrate
    • Industry
      • Other Transportation - Side panels
      • Automotive - Vehicle frames
      • Industrial - Corner posts, Roof panels, Sandwich panels, Sub-floors, Tubular frame
      • Construction - Aluminum roof bows, Composite roof panels, Floor, Walls
    • Chemistry
    • Cure Method
      • Moisture / Condensation Cure - Moisture
    • Color
      • Black
      • White
    Specifications
    Cure Specs
    Cure Temperature (°C) 25 Test Method
    Cure Time (min) 1,440, >20,160 Test Method
    Tack Free Time (min) 30 to 45
    Open Time (min) 50
    Thixotropic Exremely High Thixotropy
    Bond Strength
    General Bond Strength (psi) Initial
    Shear Strength (psi) 250, 240, 200, 175 Test Method
    Green Strength (psi) High
    Tensile Strength (psi) 300 Test Method
    Material Resistance
    High Temperature Resistance (°C) 190
    Low Temperature Resistance (°C) -40
    Moisture/Humidity Resistance Moisture/humidity resistance
    Hardness
    Shore A Hardness 55 Test Method
    Elongation (%) 300 Test Method
    Flexibility Excellent elastic
    Modulus (psi) 200 Test Method
    Other Properties
    % Solids (%) Very high solid
    Business Information
    Shelf Life Details Six months from date of manufacture when stored below 80°F (27°C).
    Shelf Life Temperature (°F) <81
    Shelf Life Type From date of manufacture
    Shelf Life (mon) 6
  • Best Practices for Bostik Liquid Rivet 1152 FS Urethane Adhesive/Sealant

    *See Terms of Use Below

    1. Surface Preparation

      Substrates should be free of all loose contamination, greases, oils, etc. Use Isopropyl alcohol or other approved solvent for substrate pretreatment.

      Temperatures of substrate must be above 40°F.Recommended substrate and product application temperatures are between 55°F and 100°F.

    2. Application

      Sausage Package—Cut metallic end-clip and place sausage into a pneumatic caulking dispenser. Apply appropriate pressure to install Liquid Rivet 1152 FS so as to assure full contact (surface wetting) to promote sealing and adhesion performance. Tool and finish applied Liquid Rivet 1152 FS immediately to promote best mechanical adhesion and cure appearance. Use water or soapy water solution for tooling compound.

      Cartridge—Cut tip to desired shape and diameter. Puncture inner seal before extruding! Apply appropriate pressure to install Liquid Rivet 1152 FS so as to assure full contact (surface wetting) to promote sealing and adhesion performance. Tool and finish applied Liquid Rivet 1152 FS immediately to promote best mechanical adhesion and cure appearance. Use water or soapy water solution for tooling compound.

    3. Clean-Up

      Uncured Liquid Rivet 1152 FS can be easily removed from hands, tools and substrates using Bostik® Hand & Tool Towels.

  • Comparable Materials for Bostik Liquid Rivet 1152 FS Urethane Adhesive/Sealant

    *See Terms of Use Below

    Spec Engine® Results

    Closest Results from this Manufacturer

Questions about this material?

Get personal assistance with your specific application needs.

Your Profile Edit
  1. 0fbcde97-60b6-4516-beb0-999cfe2751fb
  2. 0fbcde97-60b6-4516-beb0-999cfe2751fb

Popular Articles

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Anaerobic Adhesives

Read Article

Testing the effectiveness of surface treatments

Read Article

What Are the Differences Between Adhesives and Sealants?

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

Who do you read or follow for engineering news and entertainment?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
25°C after 14 days cure at 77°F and 50% RH
Cure Time Test Methods
Cure Time Test Method
1,440 min 1/8 in bead
>20,160 min after 14 days cure at 77°F and 50% RH
Shear Strength Test Methods
Shear Strength Type Cure Time Cure Temperature Cure Humidity Substrate Test Method
250 psi Lap shear strength 20,160 min 25°C 50 % Plywood 0.062in gap, 1-in overlap, speed 2 inches/min, psi to break
240 psi Lap shear strength 20,160 min 25°C 50 % FRP 0.062in gap, 1-in overlap, speed 2 inches/min, psi to break
200 psi Lap shear strength 20,160 min 25°C 50 % Painted Aluminum 0.062in gap, 1-in overlap, speed 2 inches/min, psi to break
175 psi Lap shear strength 20,160 min 25°C 50 % Stainless Steel 0.062in gap, 1-in overlap, speed 2 inches/min, psi to break
Tensile Strength Test Methods
Tensile Strength Cure Time Cure Temperature Cure Humidity
300 psi >20,160 min 25°C 50 %
Elongation Test Methods
Elongation Test Method
300 % after 14 days cure at 77°F and 50% RH, at Break
Modulus Test Methods
Modulus Temperature Test Method
200 25°C @ 25% Elongation, after 14 days cure at 77°F and 50% RH
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method Hardness Temperature
55 after 14 days cure at 77°F and 50% RH 25°C