Description for Bostik Simson MSR Fast Tack
High green strength; solventless; UV resistant; good adhesion without primer; fast curing; pintable.Application Type Bond, Seal 1 Part or 2 Part 1-Part Material Form Liquid Substrate Copper, Glass, Metal, Polyester, PVC, Lacquered wood, Stainless Steel, Brass, Zinc, Galvanized steel, Galvanized steel Industry Marine, Window Manufacturer Bostik Chemistry SMP (Silyl Modified Polymer) Cure Method Moisture Application Temperature (°F) 41 to 95 Cure Temperature (°C) 20 Cure Time (min) Fast, 1,440 Color Black, White High Temperature Resistance (°C) 100 Low Temperature Resistance (°C) -40 -
Technical Data for Bostik Simson MSR Fast Tack
Overview
-
1 Part or 2 Part
- 1-Part
-
Material Form
- Liquid
-
Substrate
- Glass
- Metal
- Copper
- Brass
- Zinc
- Galvanized - Galvanized steel
- Polyvinyl chloride (PVC) - PVC
- Wood - Lacquered wood
- Polyester
- Stainless Steel
- Galvanized Steel
-
Industry
- Marine
- Industrial - Portholes, Push Borders, Screens, Sheet, Wall ceiling
- Construction - Deck fittings, Deck hatches, Deck/Hull connection, Floor
- Construction Window - Window
-
Chemistry
- Silyl Modified Polymer (SMP) / MS Polymer - SMP (Silyl Modified Polymer)
-
Application Method
- Dispenser - Air-pressure mastic gun
- Brush - Hand
-
Cure Method
- Moisture / Condensation Cure - Moisture
-
Color
- Black
- White
Specifications
Cure Specs
Application Temperature (°F) 41 to 95 Cure Temperature (°C) 20 Test Method Cure Time (min) Fast, 1,440 Test Method Open Time Temperature (°C) 20 Tack Free Time (min) 10, Fast Test Method Open Time (min) <15 Bond Strength
General Bond Strength (psi) Good Shear Strength (psi) ca. 2.3 MPa Test Method Green Strength (psi) High, ca. 1700(pa) Test Method Tensile Strength (psi) ca. 2.2 MPa, ca. 2.9 MPa Test Method Material Resistance
UV Resistance Excellent, Very Good Environmental Resistance Excellent High Temperature Resistance (°C) 100 Low Temperature Resistance (°C) -40 Hardness
Shore A Hardness 65 Test Method Elongation (%) 225 Test Method Flexibility Permanently elastic Other Properties
Specific Gravity ca. 1.4 (g/ml) Business Information
Shelf Life Details MSR Fast Tack can be stored for 18 months in a closed (unopened) container in a dry place at temperatures between +5°C and +30°C. (cartridges 18 months). Shelf Life (mon) 18 -
Best Practices for Bostik Simson MSR Fast Tack
-
Application
MSR Fast Tack can be extruded easily with a hand- or air-pressure gun between temperatures of 5°C and 35°C.Because of the high green strength clamping can be significantly reduced and in some cases even be completely eliminated. The substrates have to be assembled within 15 minutes (at 20°C/50% R.H.) after the application of MSR Fast Tack. In general, an adhesive thickness of 2 mm is recommended.
-
Clean-Up
Remove uncured residues of MSR Fast Tack or cleaning tools can be done with a clean, colourless cloth, wetted with Simson SMP Remover or Simson Cleaner E. It is recommended to make a trial first to check possible harmful effects of these cleaners on the substrate.
-
-
Comparable Materials for Bostik Simson MSR Fast Tack
Spec Engine® Results
Popular Articles
Testing the effectiveness of surface treatments
Read ArticleInfographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation
Read ArticleWhat Are the Differences Between Adhesives and Sealants?
Read ArticleAnaerobic Adhesives
Read ArticleSponsored Articles
Unique Advantages of Contact Adhesives
Read ArticleUsing LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials
Read ArticleSylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:
Read ArticleCase Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive
Read ArticleFeatured Ads

Cure Temperature Test Methods
Cure Temperature | Cure Time Test Method |
---|---|
20°C | Curing speed after 24 hrs., ca. 3 mm, 20°C/50%R.H. |
Cure Time Test Methods
Cure Time | Test Method |
---|---|
Fast | |
1,440 min | Curing speed after 24 hrs., ca. 3 mm, 20°C/50%R.H. |
Tack Free Time Test Methods
Tack Free Time | Tack Free Temperature | Test Method |
---|---|---|
10 min | 20°C | 20°C/50% R.H. |
Fast |
Green Strength Test Methods
Green Strength | Test Method |
---|---|
High | |
ca. 1700(pa) | Physical Rheometer MC100 |
Tensile Strength Test Methods
Tensile Strength | Test Method |
---|---|
ca. 2.2 MPa | Tensile Stress 100%, ca., DIN 53504/ISO 37 |
ca. 2.9 MPa | Tensile stress@ Break, ca., DIN 53504/ISO 37 |
Shear Strength Test Methods
Shear Strength | Substrate | Test Method |
---|---|---|
ca. 2.3 MPa | Alu to Alu | DIN 53283/ASTM D1002, ca., shear stress, adh. thickness 2mm, test speed 50 mm/min. |
Elongation Test Methods
Elongation | Test Method |
---|---|
225 % | DIN 53504/ISO 37, at Break, ca |
Shore A Hardness Test Methods
Shore A Hardness | Shore Hardness Test Method |
---|---|
65 | DIN 53505, ca. |