Dow Q3-6093 RTV Adhesive Kit

CONTACT REP

Description for Dow Q3-6093 RTV Adhesive Kit

Noncorrosive; self-priming; rapid room temperature and deep section cure; good green strength; good room-temperature adhesion to most substrates.

Note: This material has been discontinued. Please view the Comparable Materials tab or call us at (262) 293-7970 for additional help.

*See Terms of Use Below

Application Type	Bond, Seal, Gasket
1 Part or 2 Part	2-Part
Material Form	Pre-Cure: Liquid, Post-Cure: Elastomer
Substrate	Ceramics, Glass, Reactive metals, Plastics, Resins
Industry	Light Emitting Diodes (LEDs)
Manufacturer	Dow
Chemistry	Silicone elastomer
Cure Method	RTV, Part A/Part B
Cure Temperature (°C)	20 to 25, 20 to 25
Cure Time (min)	Rapid, 90
Viscosity (cPs)	Non-flow
Color	Black
High Temperature Resistance (°C)	200
Low Temperature Resistance (°C)	-45, -55
Volume Resistivity (O)	7.3E+14 (ohms/cm)

Best Practices for Dow Q3-6093 RTV Adhesive Kit

Register for FREE to view more details

Why register?

View Technical Details
View Test Methods
View Key Specifications
View Similar Materials
Save your Project Searches

See what Gluespec offers

Sign up now Already registered? Sign in!

Email: *

Password: *

Confirm Password: *

Do you prefer to see data in °F or °C?

First Name: *

Last Name: *

Phone: *

Company Name: *

Address: *

Postal Code: *

Country: *

Job Function: *

Industry: *

Describe: *

I agree to the terms of use *

*: Required

Technical Data for Dow Q3-6093 RTV Adhesive Kit

*See Terms of Use Below

Overview

Application Type
- Gasketing - Gasket
- Adhesive - Bond
- Sealant - Seal
1 Part or 2 Part
- 2-Part
Material Form
- Elastomer - Post-Cure: Elastomer
- Liquid - Pre-Cure: Liquid
Substrate
- Ceramic - Ceramics
- Glass
- Metal - Reactive metals
- Plastic - Plastics, Resins
- Other - Laminates
Industry
- LED (Light-Emitting Diodes) - Light Emitting Diodes (LEDs)
- Industrial - Baseplates, Housings, Lids
Chemistry
- Silicone - Silicone elastomer
Cure Method
- 2-Part Cure - Part A/Part B
- RTV (Room Temperature Vulcanization) - RTV
Color
- Black

Specifications

Cure Specs

Cure Temperature (°C)	20 to 25, 20 to 25
Cure Time (min)	Rapid, 90
Viscosity (cPs)	Non-flow
Tack Free Time (min)	Fast	Test Method
Work / Pot Time (min)	32	Test Method
Mix Ratio	10:1 (by volume)
Green Strength Time (min)	Good

Bond Strength

Shear Strength (psi)	230	Test Method
Green Strength (psi)	Good
Tensile Strength (psi)	250

Material Resistance

Environmental Resistance	Environmental resistance
High Temperature Resistance (°C)	200
Low Temperature Resistance (°C)	-45, -55
Moisture/Humidity Resistance	Moisture/humidity resistance

Conductivity

Dissipation Factor	0.00900, 0.00260	Test Method
Dielectric Strength (V/mil)	Good, 19,685,039, Durable
Dielectric Constant	3.38, 3.26	Test Method
Volume Resistivity (O)	7.3E+14 (ohms/cm)

Hardness

Shore A Hardness	42
Elongation (%)	2
Flexibility	Flexible

Other Properties

Specific Gravity	1.370
Coefficient of Thermal Expansion (CTE)	285 (Linear (micron/m °C or ppm ))

Business Information

Shelf Life Details	Shelf life is indicated by the “Use Before” date found on the product label. For best results, Dow Corning RTV adhesives should be stored at or below 25°C (77°F). Special precautions must be taken to prevent moisture from contacting these materials. Containers should be kept tightly closed with head or air space minimized. Partially filled containers should be purged with dry air or other gases, such as nitrogen.
Shelf Life Temperature (°F)	77
Shelf Life Type	from date of manufacture
Shelf Life (mon)	12

Not Good For

Don't Use With	Plastic, rubber

Best Practices for Dow Q3-6093 RTV Adhesive Kit

*See Terms of Use Below
1. Surface Preparation
  
  All surfaces should be thoroughly cleaned and/or degreased with Dow Corning® brand OS Fluids, naphtha, mineral spirits, methyl ethyl ketone (MEK) or other suitable solvent. Solvents such as acetone or isopropyl alcohol (IPA) do not tend to remove oils well, and any oils remaining on the surface may interfere with adhesion. Light surface abrasion is recommended whenever possible, because it promotes good cleaning and increases the surface area for bonding. A final surface wipe with acetone or IPA is also useful. Some cleaning techniques may provide better results than others
  
  users should determine the best techniques for their particular applications.
2. Mixing
  
  Upon standing, some filler may settle to the bottom of the liquid containers after several weeks. To ensure a uniform product mix, the material in each container should be thoroughly mixed prior to use. Two-part materials should be mixed in the proper ratio (1:1 or 10:1) either by weight or volume. The presence of light colored streaks or marbling indicates inadequate mixing.
3. Deairing/Degassing
  
  Automated airless dispense equipment can be used to reduce or avoid the need to de-air. If de-airing is required to reduce voids in the cured elastomer, consider a vacuum de-air schedule of >28 inches Hg for 10 minutes or until bubbling subsides.
Comparable Materials for Dow Q3-6093 RTV Adhesive Kit

*See Terms of Use Below

Spec Engine^® Results
- AS2500(CHT)
  This is a novel (2 part ) twin pack system, which consists of a 1- Part RTV Industrial Adhesive Silicone Sealant and an accelerator in a 10:1.
- EA-3500(Dow)
  Two-part, room temperature cure adhesive. Good adhesion to various substrates (Al, Glass, PBT).
- Dowsil EA-1236 Adhesive(Dow)
  Two-part, room temperature cure adhesive. It is suitable for sealing lids and housings, parts fixing on circuit board.
- Compare All