Dow SE 1701 LTV

CONTACT REP

Description for Dow SE 1701 LTV

Noncorrosive; self-priming; high strength.

Application Type	Bond, Seal, Gaskets
1 Part or 2 Part	2-Part
Material Form	Liquid, Silicone elastomer
Substrate	Ceramics, Glass, Reactive metals, Plastics, Resins
Industry	Electronic components, Circuit boards, Flyback transformer, Connectors, Smart Meters, ECUs, E-Mobility Solutions, Smart Home Devices, Electronic modules, Electronic part, Key pad of PC
Manufacturer	Dow
Chemistry	Silicone elastomer
Cure Method	Part A/Part B, Heat
Cure Temperature (°C)	Faster or lower, 20 to 25, >100 (C), 150
Cure Time (min)	Rapid, 30
Viscosity (cPs)	80,000, Flowable
Color	White
High Temperature Resistance (°C)	200
Low Temperature Resistance (°C)	-45, -55
Volume Resistivity (O)	1E+15 (ohms/cm)

Best Practices for Dow SE 1701 LTV

Register for FREE to view more details

Why register?

View Technical Details
View Test Methods
View Key Specifications
View Similar Materials
Save your Project Searches

See what Gluespec offers

Sign up now Already registered? Sign in!

Email: *

Password: *

Confirm Password: *

Do you prefer to see data in °F or °C?

First Name: *

Last Name: *

Phone: *

Company Name: *

Address: *

Postal Code: *

Country: *

Job Function: *

Industry: *

Describe: *

I agree to the terms of use *

*: Required

Technical Data for Dow SE 1701 LTV

*See Terms of Use Below

Overview

Application Type
- Gasketing - Gaskets
- Adhesive - Bond
- Sealant - Seal
1 Part or 2 Part
- 2-Part
Material Form
- Elastomer - Silicone elastomer
- Liquid
Substrate
- Ceramic - Ceramics
- Glass
- Metal - Reactive metals
- Plastic - Plastics, Resins
- Other - Laminates
Industry
- Smart Meters
- Smart Home Devices
- Electronic Control Unit - ECUs
- E-Mobility Solutions
- Electronics - Electronic components, Electronic modules, Electronic part, Key pad of PC
- Printed Circuit Board (PCB) - Circuit boards
- Transformers - Flyback transformer
- Connectors
- Power Supplies - Power modules
- Industrial - Ceramic condensers, Condensers, Housing seals, Lid
Chemistry
- Silicone - Silicone elastomer
Cure Method
- Heat
- 2-Part Cure - Part A/Part B
Color
- White

Specifications

Cure Specs

Cure Temperature (°C)	Faster or lower, 20 to 25, >100 (C), 150
Cure Time (min)	Rapid, 30
Viscosity (cPs)	80,000, Flowable
Tack Free Time (min)	Fast
Work / Pot Time (min)	Long, 360	Test Method
Mix Ratio	10:1 (by volume)

Bond Strength

General Bond Strength (psi)	High
Shear Strength (psi)	820	Test Method
Tensile Strength (psi)	1,000

Material Resistance

Environmental Resistance	Environmental resistance
High Temperature Resistance (°C)	200
Low Temperature Resistance (°C)	-45, -55
Moisture/Humidity Resistance	Moisture/humidity resistance

Conductivity

Dissipation Factor	0.00300	Test Method
Dielectric Strength (V/mil)	Good, Durable, 725
Dielectric Constant	3.00	Test Method
Volume Resistivity (O)	1E+15 (ohms/cm)

Hardness

Shore A Hardness	64
Elongation (%)	2
Flexibility	Flexible

Business Information

Shelf Life Details	Shelf life is indicated by the “Use Before” date found on the product label. For best results, Dow Corning RTV adhesives should be stored at or below 25°C (77°F). Special precautions must be taken to prevent moisture from contacting these materials. Containers should be kept tightly closed with head or air space minimized. Partially filled containers should be purged with dry air or other gases, such as nitrogen.
Shelf Life Type	from date of manufacture
Shelf Life (mon)	14

Not Good For

Don't Use With	Plastic, rubber

Best Practices for Dow SE 1701 LTV

*See Terms of Use Below
1. Surface Preparation
  
  All surfaces should be thoroughly cleaned and/or degreased with Dow Corning® brand OS Fluids, naphtha, mineral spirits, methyl ethyl ketone (MEK) or other suitable solvent. Solvents such as acetone or isopropyl alcohol (IPA) do not tend to remove oils well, and any oils remaining on the surface may interfere with adhesion. Light surface abrasion is recommended whenever possible, because it promotes good cleaning and increases the surface area for bonding. A final surface wipe with acetone or IPA is also useful. Some cleaning techniques may provide better results than others
  
  users should determine the best techniques for their particular applications.
2. Mixing
  
  Upon standing, some filler may settle to the bottom of the liquid containers after several weeks. To ensure a uniform product mix, the material in each container should be thoroughly mixed prior to use. Two-part materials should be mixed in the proper ratio (1:1 or 10:1) either by weight or volume. The presence of light colored streaks or marbling indicates inadequate mixing.
3. Deairing/Degassing
  
  Automated airless dispense equipment can be used to reduce or avoid the need to de-air. If de-airing is required to reduce voids in the cured elastomer, consider a vacuum de-air schedule of >28 inches Hg for 10 minutes or until bubbling subsides.
Comparable Materials for Dow SE 1701 LTV

*See Terms of Use Below

Spec Engine^® Results
- Sylgard 577 Primerless Silicone Adhesive Kit(Dow)
  A Gray, flowable adhesive with high tensile strength and good flame resistance, MIL-PRF-23586F tested.
- Dowsil Q5-8401 Adhesive(Dow)
  • Flowable • 1:1 mix ratio • Heat cure • High tensile strength • 2-part • Dark gray • Heat cure •
- Compare All