Elantas (Altana) Conathane UC-41 Datasheet Elantas (Altana) Conathane UC-41

Information provided by Gluespec
  • Description for Elantas (Altana) Conathane UC-41

    An unfilled, two-component, room temperature curing, 100%-solids urethane casting system, excellent handling properties, high impact resistance, excellent machinability.

    *See Terms of Use Below

    Brand Conathane, Cytec
    Application Type Bond, Casting
    1 Part or 2 Part 2-Part
    Material Form Liquid
    Manufacturer Elantas (Altana)
    Chemistry Urethane
    Cure Method 2-Part Cure, Elevated temperature curing, Room temperature curing
    Demolding Time (min) 240, 60
    Cure Temperature (°C) 25, 80, 20 to 25 Room temperature
    Cure Time (min) 10,080, 960
    Viscosity (cPs) Low, 500
    Color Natural White, Opaque White
    High Temperature Resistance (°C) 60
    Heat Deflection (°C) 60, 88
    Volume Resistivity (O) 1.2e14 (ohm-cm)
    Durability Tough
  • Technical Data for Elantas (Altana) Conathane UC-41

    • Application Type
    • 1 Part or 2 Part
      • 2-Part
    • Material Form
      • Liquid
    • Industry
      • Industrial
      • Other - Used in prototyping work requiring a “thermoplastic” feel and appearance
    • Chemistry
    • Application Method
      • Dispenser - processed by hand or by machine
      • Other - Meter-mix Vacuum Potting / Casting, Meter-mix Bench Potting / Casting, Hand-mix Bench Potting / Casting
    • Cure Method
      • Room Temperature / Air Dry - Room temperature curing
      • Heat - Elevated temperature curing
      • 2-Part Cure
    • Color
      • White - Natural White, Opaque White
    • Brand
      • Conathane
      • Cytec
    Cure Specs
    Demolding Time (min) 240, 60
    Cure Temperature (°C) 25, 80, 20 to 25 Room temperature
    Cure Time (min) 10,080, 960
    Viscosity (cPs) Low, 500 Test Method
    Fixture or Handling Strength Time (min) Excellent handling properties
    Linear Shrinkage (%) Low, <0.10, 0.50 Test Method
    Work / Pot Time (min) 4.00 Test Method
    Mix Ratio 100:50 (by volume), 100:50 (by weight), Convenient (2:1)
    Bond Strength
    Impact Strength (psi) 0.34 (ft-lb), 0.35 (ft-lb), 2.3 (in), 2.8 (in) Test Method
    Flexural Strength (psi) 5,900, 7,900 Test Method
    Tensile Strength (psi) 5,500, 7,500 Test Method
    Material Resistance
    Dimensional Stability (%) Dimensionally stable
    High Temperature Resistance (°C) 60
    Impact Resistance High
    Heat Deflection (°C) 60, 88 Test Method
    Unfilled Unfilled
    Dissipation Factor 0.00500 Test Method
    Dielectric Strength (V/mil) Test Method
    Dielectric Constant 3.80 Test Method
    Volume Resistivity (O) 1.2e14 (ohm-cm) Test Method
    Durability Tough
    Shore D Hardness 80, High, 80 Test Method
    Elongation (%) 6, 7 Test Method
    Modulus (psi) 174,200, 207,800 Test Method
    Other Properties
    Machinability Excellent
    Glass Transition Temp (Tg) (°C) 63, 93 Test Method
    Specific Gravity 1.100, 1.100 Test Method
    % Solids (%) 100
    Business Information
    Shelf Life Details Both Part A and Part B components are moisture sensitive. Avoid the use of paper cups and wooden sticks. Unless the contents are used within one day, we recommend flushing with dry nitrogen or CONAP® Dri-Purge each time the containers are closed., CONATHANE® UC-41, Part A and Part B, have a shelf life of 18 months from date of manufacture when stored in their original, unopened containers at 65°-85°F., Store at 20 - 30°C / 68 - 86°F in a dry controlled environment out of direct sunlight. This material should be suitable for use stored under these conditions in the original sealed containers for twelve (12) months from the date of shipment.
    Shelf Life Temperature (°F) 149 to 185, 68 to 86
    Shelf Life Type From date of manufacture, From the date of shipment
    Shelf Life (mon) 12, 18, 12
  • Best Practices for Elantas (Altana) Conathane UC-41

    *See Terms of Use Below

    1. Application

      CONATHANE® UC-41 may be processed by hand or by machine.

      CONATHANE® UC-41 has very good adhesion to most substrates and generally will not require the use of a primer. If adhesion improvement is necessary, contact Cytec Industries Inc. for specific recommendations. If the cast part is to be demolded after cure, apply a CONAP® mold release agent prior to casting. Castings can generally be demolded in 4 hours at room temperature

    2. Mixing

      Mix individual components thoroughly before use.

      Mix the UC-41 Part A and UC-41 Part B in the ratio specified above until homogeneous. Components may be preheated up to 60°C if reduced viscosity is required. If hand mixing, degas at >27 in. Hg vacuum before use.

    3. Deairing/Degassing

      If stirring is done carefully degassing of the mixed material may not be necessary. If air entrapment is excessive, degas the mixture for 1 to 1 2 minutes at 1-5 mm of vacuum.

    4. Curing

      Cure 7 days at 25°C / 77°F – or – 16 hours at 80°C / 176°F

      Demold time of 4 hours at 25°C / 77°F – or – 1 hours at 80°C / 176°F

      The cure schedules are based on time after the unit reaches the specified temperature and are recommendations only. The user is responsible for determining the optimum cure conditions for their application.

  • Comparable Materials for Elantas (Altana) Conathane UC-41

    *See Terms of Use Below

    Spec Engine® Results

Popular Articles

Testing the effectiveness of surface treatments

Read Article

An Overview of Fluid Dispensing Systems & How They’re Used

Read Article

Characteristics of MMAs

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for Elantas (Altana) Conathane UC-41

Gluespec Poll

When you're researching or sourcing materials online, what device are you using?
Linear Shrinkage Test Methods
Linear Shrinkage Test Method Temp
<0.10 % ASTM D2566, Cured 25°C
0.50 % ASTM D2566, Cured 80°C
Viscosity Test Methods
Viscosity Test Method Temperature
500 cPs Initial, Mixed Materials 25°C
Work / Pot Time Test Methods
Work / Pot Time Test Method Temperature
4.00 min 200 g, Mixed Materials 25°C
Flexural Strength Test Methods
Flexural Strength Cure Time Cure Temperature Test Method
5,900 psi 10,080 min 25°C 25°C, ASTM D790, Cured
7,900 psi 960 min 80°C 25°C , ASTM D790, Cured
Impact Strength Test Methods
Impact Strength Cure Time Cure Temperature Test Method
0.34 (ft-lb) 10,080 min 25°C Notched, ASTM D256, Cured
0.35 (ft-lb) 960 min 80°C Notched, ASTM D256, Cured
2.3 (in) 0.12 min 25°C Unotched, ASTM D256, Cured
2.8 (in) 960 min 80°C Unotched, ASTM D256, Cured
Tensile Strength Test Methods
Tensile Strength Cure Time Cure Temperature Test Method
5,500 psi 10,080 min 25°C 25°C, ASTM D412, Cured
7,500 psi 960 min 80°C 25°C, ASTM D412, Cured
Heat Deflection Test Methods
Heat Deflection Test Method
60°C Heat Distortion Temperature, 66 psi, Cured @ 25°C, ASTM D638
88°C Heat Distortion Temperature, 66 psi, Cured @ 80°C, ASTM D638
Dielectric Constant Test Methods
Dielectric Constant Temperature Test Method
3.80 25°C 1 kHz @, ASTM D15
Dielectric Strength Test Methods
Dielectric Strength Test Method
Dissipation Factor Test Methods
Dissipation Factor Temperature Test Method
0.00500 25°C 1 kHz @, ASTM D150
Volume Resistivity Test Methods
Volume Resistivity Temp (°C) Test Method
1.2e14 (ohm-cm) 25°C ASTM D257
Elongation Test Methods
Elongation Test Method
6 % Cured @ 25°C, Ultimate, ASTM D638
7 % Cured @ 80°C, Ultimate, ASTM D638
Modulus Test Methods
Modulus Temperature Test Method
174,200 psi 25°C Cured @ 25°C, Flexural, ASTM D790
207,800 psi 25°C Cured @ 80°C, Flexural, ASTM D790
Shore D Hardness Test Methods
Shore D Hardness Shore Hardness Test Method
80 Cured @ 25°C, ASTM D2240
80 Cured @ 80°C, ASTM D2240
Glass Transition Temp (Tg) Test Methods
Glass Transition Temp (Tg) Glass Transition Temperature (Tg) Test Method
63°C Cured @ Room Temperature
93°C Cured 16 hours @ 80°C
Specific Gravity Test Methods
Specific Gravity Temperature Test Method
1.100 25°C Cured @ 25°C, ASTM D792
1.100 25°C Cured @ 80°C, ASTM D792