Elantas (Altana) RN-1558

CONTACT REP

Description for Elantas (Altana) RN-1558

Liquid isocyanate terminated prepolymers that yield an elastomer with good tear and tensile strengths, good abrasion resistance, exceptional elongation, and good low temperature properties.

*See Terms of Use Below

Brand	Cytec
Application Type	Bond
1 Part or 2 Part	2-Part
Material Form	Liquid
Substrate	Glass, Metal, Plastic
Industry	Gears, Industrial truck tires, Bushings
Manufacturer	Elantas (Altana)
Chemistry	isocyanate terminated prepolymers
Cure Method	2 Parts
Cure Temperature (°C)	100, 100
Cure Time (min)	480, 360
Viscosity (cPs)	6,000, 300
Color	Light Amber

Best Practices for Elantas (Altana) RN-1558

Register for FREE to view more details

Why register?

View Technical Details
View Test Methods
View Key Specifications
View Similar Materials
Save your Project Searches

See what Gluespec offers

Sign up now Already registered? Sign in!

Email: *

Password: *

Confirm Password: *

Do you prefer to see data in °F or °C?

First Name: *

Last Name: *

Phone: *

Company Name: *

Address: *

Postal Code: *

Country: *

Job Function: *

Industry: *

Describe: *

I agree to the terms of use *

*: Required

Technical Data for Elantas (Altana) RN-1558

*See Terms of Use Below

Overview

Application Type
- Adhesive - Bond
1 Part or 2 Part
- 2-Part
Material Form
- Liquid
Substrate
- Glass
- Metal
- Plastic
Industry
- Trucks - Industrial truck tires
- Industrial
- Gears
- Bushing - Bushings
- Other - Rolls, Metal forming dies, Seals, Abrasion resistant belts, Casters, Impellers
Chemistry
- Other - isocyanate terminated prepolymers
Application Method
- Dispenser - automatic metering, mixing equipment
Cure Method
- 2-Part Cure - 2 Parts
Color
- Red - Light Amber
Brand
- Cytec

Specifications

Cure Specs

Cure Temperature (°C)	100, 100
Cure Time (min)	480, 360
Viscosity (cPs)	6,000, 300	Test Method
Work / Pot Time (min)	4.00 to 11

Bond Strength

Tear Strength (piw)	Good, 260 (pli), 250 (pli)
Tensile Strength (psi)	Good, 1,600, 400, 550, 2,000, 550, 700	Test Method

Material Resistance

Abrasion Resistance	good abrasion resistance

Hardness

Shore A Hardness	70, 70, 80
Shore D Hardness	55, 20
Elongation (%)	Exceptional elongation, 1,100, 900

Other Properties

Specific Gravity	1.040	Test Method

Best Practices for Elantas (Altana) RN-1558

*See Terms of Use Below
1. Mixing
  
  Pour mixed system into molds, preheated to 80-100°C that have been coated with CONAP® MR-5002 or equivalent, mold releases.
  
  Automatic metering and mixing equipment can be used with these systems
2. Deairing/Degassing
  
  Heat pre-weighed amounts of CONATHANE® prepolymer to 80-100°C and degas at 1-5 mm of vacuum for at least 5 minutes, or until excessive bubbling stops. Containers should be unlined metal, plastic, or glass, and should be large enough to allow for foaming during degassing.
  
  When adding MbOCA to CONATHANE®, the MbOCA must be melted at 120°C prior to mixing. After adding curative, mix thoroughly and degas at 1-5 mm for 1 to 2 minutes.
Comparable Materials for Elantas (Altana) RN-1558

*See Terms of Use Below

Spec Engine^® Results
- RTV8111 w/ RTV9891(Momentive)
  Momentive RTV8111 w/ RTV9891 is a 2-Part Two-part cure Silicone Rubber Liquid used to Adhere Copper
- Epo-Tek 310M-2(Epoxy Technology)
  A two component, optically clear, flexible epoxy adhesive designed for optical applications within semiconductor, fiber optic industries.
- Epo-Tek 310M-1(Epoxy Technology)
  A two component, optically clear epoxy adhesive designed for optical, semiconductor and medical applications.
- Compare All
Closest Results from this Manufacturer
- FP-1302(Elantas (Altana))
  A two-component, room temperature curing flexible polyurethane elastomer system.
- RN-1559(Elantas (Altana))
  Liquid isocyanate terminated prepolymers that yield an elastomer with good tear and tensile strengths, good abrasion resistance, exceptional elongation, and good low temperature properties.