Description for Henkel Armstrong A-5 w/ E Activator
Formulated from epoxy resins and unique, inert filler materials. The A-5 contains metallic aluminum powder imparting a silver color. It is particularly useful where a solder-like appearance is <br/>desired.Brand Armstrong Application Type Adhesive 1 Part or 2 Part 2 Part Material Form Liquid Substrate Steel Manufacturer Henkel Chemistry Epoxy Cure Method Activator Cure Temperature (°C) Elevated Temperature, 93 Cure Time (min) 60 Viscosity (cPs) 140, 130 (poise) Color Silver Density (g/cm³) 0.38 lbs/cubic in
Popular Articles
Electrically Conductive Adhesives
Read ArticleInfographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation
Read ArticleEpoxies in the Medical Device Industry
Read ArticleTesting the effectiveness of surface treatments
Read ArticleSponsored Articles
Unique Advantages of Contact Adhesives
Read ArticleUsing LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials
Read ArticleSylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:
Read ArticleCase Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive
Read ArticleFeatured Ads

Viscosity Test Methods
Viscosity | Temperature |
---|---|
140 cPs | 25°C |
130 (poise) | 25°C |
Work / Pot Time Test Methods
Work / Pot Time | Temperature |
---|---|
120 to 180 min | 25°C |
Shear Strength Test Methods
Shear Strength | Substrate | Chemical | Test Time | Test Temperature | Test Humidity |
---|---|---|---|---|---|
2,470 psi | 25°C | ||||
2,260 psi | 82°C | ||||
2,240 psi | -51°C | ||||
2,830 psi | Amonia, 28% | 604,800 sec | |||
3,000 psi | Distilled Water | 604,800 sec | |||
2,730 psi | Salt Water 10% | 604,800 sec | |||
2,980 psi | Acetone | 604,800 sec | |||
2,180 psi | Glacial Acetic Acid | 604,800 sec | |||
3,000 psi | Toluene | 604,800 sec | |||
2,680 psi | Ethylenedichloride | 604,800 sec | |||
2,100 psi | Ethyl Acetate | 604,800 sec | |||
2,500 psi | Hexane | 604,800 sec | |||
1,830 psi | Steel to Steel | 604,800 sec | 100 % |