3M Bumpon Protective Product SJ5616

3M Bumpon Protective Product SJ5616 Datasheet
  • Description for 3M Bumpon Protective Product SJ5616

    A resilient clear polyurethane rollstock products utilizing an aggressive acrylic-based, pressure sensitive adhesive, high strength acrylic adhesive that provides excellent shear properties at elevated temperatures.

    *See Terms of Use Below

    Brand Bumpon
    Application Type Bumpon
    Material Form Rollstock
    Substrate Aluminum, Polystyrene, Glass, Many metal surfaces, Many high surface energy plastics, polycarbonate, Polypropylene, Stainless Steel, Wood, Formica, ABS
    Industry Die cut shapes for use as spacers on cabinet doors, Die cut shapes for use as skid-resistant feet hand held devices, Die cut shapes for use as skid-resistant feet desktop electronic devices, Die cut shapes for use as skid-resistant feet desk top equipment, Door kick pads
    Manufacturer 3M
    Chemistry Acrylic, Polyurethane, Acrylic-based
    Cure Method Pressure Sensitive
    Color Clear, Transparent
    Relative Solvent Resistance Chemical Resistance: 5% Detergent in water, Chemical Resistance: 25% Detergent in water, Chemical Resistance: 5% Bleach in water, Chemical Resistance: Gasoline (10% ethanol), Chemical Resistance: Motor Oil (10W30), Chemical Resistance: Isopropyl Alcohol, Chemical Resistance: Solvent Resistance
    Non-Yellowing UV Resistance: Excellent resistance to yellowing
    High Temperature Resistance (°C) 66, 107
    Low Temperature Resistance (°C) -34
    Other Resistance Good resistance to staining, Good resistance to marring, Excellent cushioning properties
    Shore M Hardness 73 to 78
    Density (g/cm³) 70 (lb./ft.2)
    Key Specifications UL (Underwriters Laboratory), ULC (Underwriters Laboratories of Canada), NFPA (National Fire Protection Association): Flammability Listing Classification UL94HB
  • Technical Data for 3M Bumpon Protective Product SJ5616

    Overview
    • Application Type
      • Bumpons - Bumpon
    • Material Form
      • Rollstock
    • Substrate
    • Industry
      • Electronics - Die cut shapes for use as skid-resistant feet desk top equipment
      • Telecom / Datacom - Die cut shapes for use as skid-resistant feet hand held devices
      • Storage & Graphics - Die cut shapes for use as skid-resistant feet desktop electronic devices
      • Industrial
      • Appliances
      • Construction Door - Die cut shapes for use as spacers on cabinet doors, Door kick pads
      • Other - Die cut shapes for cushioning glass from metal frames, Die cut shapes for use as skid-resistant feet on small appliances, Die cut shapes for use as cushions and pads on glass, Strips or pads for use as skid-resistant surfaces on glass, Antichafe protection, Corner protection strips, Spacer or stop to prevent surface damage, Anti-rattle spacer to fill gaps, Die cut shapes for use as spacers on cabinet lids, Die cut shapes for use as cushions, Die cut shapes for use as spacers on cabinet drawers, Die cut shapes for cushioning glass from wood frames, Die cut shapes for glass table tops, Die cut shapes for use as cushions and pads on clear plastic shelves, Strips or pads for use as skid-resistant surfaces on clear plastic shelves, Reduce vibration, Dampen noise
    • Chemistry
    • Application Method
      • Contact
      • Other - Easy application
    • Cure Method
      • Pressure Sensitive (min) - Pressure Sensitive
    • Color
      • Clear / Transparent - Clear, Transparent
    • Key Specifications
      • UL (Underwriters Laboratory), ULC (Underwriters Laboratories of Canada), NFPA (National Fire Protection Association): UL 94 HB - Flammability Listing Classification UL94HB
    • Brand
      • Bumpon
    Specifications
    Cure Specs
    Application Temperature (°F) 39 to 126
    Bond Strength
    General Bond Strength (psi) High
    Peel Strength (piw) 6 (oz. per 1 inch), 22 (oz. per 1 inch), 45 (oz. per 1 inch), 45 (oz. per 1 inch), 45 (oz. per 1 inch), 45 (oz. per 1 inch) Test Method
    Shear Strength (psi) 1000 (gram), 1000 (gram), 1000 (gram), 1000 (gram), Excellent Test Method
    Tensile Strength (psi) > 580 (lb./in.2) Test Method
    Tape Properties
    Total Thickness (mil) 1/16 (inches)
    Single Sided Single Sided
    Material Resistance
    Abrasion Resistance Excellent, < 0.13 (gm/1000 cycles) Test Method
    Environmental Resistance Long aging resiliency
    High Temperature Resistance (°C) 66, 107 Test Method
    Low Temperature Resistance (°C) -34 Test Method
    Other Resistance Good resistance to staining, Good resistance to marring, Excellent cushioning properties Test Method
    Hardness
    Shore A Hardness 70 Test Method
    Shore M Hardness 73 to 78 Test Method
    Elongation (%) 100 Test Method
    Flexibility Resilient
    Other Properties
    Density (g/cm³) 70 (lb./ft.2) Test Method
    Business Information
    Shelf Life Details The shelf life of 3M™ Bumpon™ Protective Products SJ5600 Series is 18 months from the date of manufacture when stored in the original packaging materials and stored at 16-27°C (60-80°F) and 50% relative humidity., To obtain best performance, use this product within 18 months from date of manufacture.
    Shelf Life Temperature (°F) 61 to 81
    Shelf Life Type From date of manufacture
    Shelf Life (mon) 18
    Not Good For
    Don't Use With Low surface energy plastics, Polypropylene, Polyethylene, Other various surfaces, Powdercoat painted
  • Best Practices for 3M Bumpon Protective Product SJ5616

    *See Terms of Use Below

    1. Surface Preparation

      To obtain maximum adhesion, surfaces must be unified, dry, and free of contaminants. Surface contact is fundamental to adhesive performance. To maximize contact on a substrate: Clean surfaces with low strength solvents such as isopropyl alcohol (rubbing alcohol) or heptane.

    2. Application

      Apply firm pressure to increase the cold flow and contact of the adhesive with the substrate.

    3. Curing

      Allow time (dwell) to increase the surface contact and adhesion.

    4. Testing

      Note: Product selection is ultimately the user’s responsibility. Users should conduct their own tests under actual use and storage conditions to determine whether the product is fit for a particular purpose and method of application.

  • Comparable Materials for 3M Bumpon Protective Product SJ5616

    *See Terms of Use Below

    Spec Engine® Results

Questions about this material?

Get personal assistance with your specific application needs.

Your Profile Edit
  1. 1e575223-c7c5-4571-8a7b-78a52a82608a
  2. 1e575223-c7c5-4571-8a7b-78a52a82608a

Popular Articles

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

What Projects Require Custom Adhesive Formulations and Why?

Read Article

Characteristics of MMAs

Read Article

Testing the effectiveness of surface treatments

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

Which answer best describes a project you are currently working on?
Shear Strength Test Methods
Shear Strength Type Substrate Test Time Test Temperature Test Method
1000 (gram) Static Shear Adhesive Stainless steel >600,000 sec 24°C One in. overlap shear test; tested in accordance with the ASTM-D-3654-M (1000 gram) method; testing completed on stainless steel test panels using 3M™ Bumpon™ Protective Product SJ5616.
1000 (gram) Static Shear Adhesive Stainless steel >600,000 sec 49°C One in. overlap shear test; tested in accordance with the ASTM-D-3654-M (1000 gram) method; testing completed on stainless steel test panels using 3M™ Bumpon™ Protective Product SJ5616.
1000 (gram) Static Shear Adhesive Stainless steel >600,000 sec 70°C One in. overlap shear test; tested in accordance with the ASTM-D-3654-M (1000 gram) method; testing completed on stainless steel test panels using 3M™ Bumpon™ Protective Product SJ5616.
1000 (gram) Static Shear Adhesive Stainless steel >600,000 sec 82°C One in. overlap shear test; tested in accordance with the ASTM-D-3654-M (1000 gram) method; testing completed on stainless steel test panels using 3M™ Bumpon™ Protective Product SJ5616.
Excellent At elevated temperatures
Tensile Strength Test Methods
Tensile Strength Test Method
> 580 (lb./in.2) ASTM-D-412, Die A
Peel Strength Test Methods
Peel Strength Type Substrate Test Time Test Method
6 (oz. per 1 inch) 90° Peel Adhesion Polypropylene 4,320 min 3M Test Method TM-2065; 72 hour dwell, 1 inch wide samples pulled at 12 in. per minute. Testing completed using Bumpon Protective Product SJ5616.
22 (oz. per 1 inch) 90° Peel Adhesion Polystyrene 4,320 min 3M Test Method TM-2065; 72 hour dwell, 1 inch wide samples pulled at 12 in. per minute. Testing completed using Bumpon Protective Product SJ5616.
45 (oz. per 1 inch) 90° Peel Adhesion ABS 4,320 min 3M Test Method TM-2065; 72 hour dwell, 1 inch wide samples pulled at 12 in. per minute. Testing completed using Bumpon Protective Product SJ5616.
45 (oz. per 1 inch) 90° Peel Adhesion Stainless Steel 4,320 min 3M Test Method TM-2065; 72 hour dwell, 1 inch wide samples pulled at 12 in. per minute. Testing completed using Bumpon Protective Product SJ5616.
45 (oz. per 1 inch) 90° Peel Adhesion Aluminum 4,320 min 3M Test Method TM-2065; 72 hour dwell, 1 inch wide samples pulled at 12 in. per minute. Testing completed using Bumpon Protective Product SJ5616.
45 (oz. per 1 inch) 90° Peel Adhesion Glass 4,320 min 3M Test Method TM-2065; 72 hour dwell, 1 inch wide samples pulled at 12 in. per minute. Testing completed using Bumpon Protective Product SJ5616.
Abrasion Resistance Test Methods
Abrasion Resistance Test Method
Excellent
< 0.13 (gm/1000 cycles) ASTM-C-501; Taber H, 1 kg
High Temperature Resistance Test Methods
High Temperature Resistance Test Method
66°C Service Temperature
107°C Service Temperature, intermittent exposure
Low Temperature Resistance Test Methods
Low Temperature Resistance Test Method
-34°C Service Temperature
Other Resistance Test Methods
Other Resistance Test Method
Good resistance to staining 3M - 24 hrs. at 158°F against white paint, 7 days, 7 days exposed to UV; Reference test for 24 hours only
Good resistance to marring
Excellent cushioning properties
Elongation Test Methods
Elongation Test Method
100 % ASTM-D-412, Die A, When ASTM method is listed, data was collected in accordance with ASTM test method.
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method
70 ASTM-D-2240, When ASTM method is listed, data was collected in accordance with ASTM test method.
Shore M Hardness Test Methods
Shore M Hardness Shore Hardness Test Method
73 to 78 ASTM-D-2240, When ASTM method is listed, data was collected in accordance with ASTM test method.
Density Test Methods
Density Test Method
70 (lb./ft.2) Approximate