Dow Silastic 9280/75E Datasheet Dow Silastic 9280/75E

Information provided by Gluespec
  • Description for Dow Silastic 9280/75E

    Good clarity; easily pigmented; formulated to meet BgVV, XV and FDA regulations.

    *See Terms of Use Below

    Brand Silastic
    Application Type Mold-Making
    1 Part or 2 Part 2-Part
    Material Form Liquid
    Manufacturer Dow
    Chemistry Silicone rubber
    Cure Method Part A/Part B
    Cure Temperature (°C) 120, 200, 200
    Cure Time (min) 10, 240, 0.13 to 0.23
    Viscosity (cPs) 520 (Pa.s)
    Volume Resistivity (O) 4.8e15 (ohms/cm)
    Key Specifications FDA (U.S. Food & Drug Administration) and/or CFIA (Canadian Food Inspection Agency): FDA 21 CFR 177.2600
  • Technical Data for Dow Silastic 9280/75E

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 2-Part
    • Material Form
      • Liquid
    • Chemistry
    • Application Method
      • Dispenser - Meter mix equipment
    • Cure Method
      • 2-Part Cure - Part A/Part B
    • Key Specifications
      • FDA (U.S. Food & Drug Administration) and/or CFIA (Canadian Food Inspection Agency) : 177.2600 - FDA 21 CFR 177.2600
    • Brand
      • Silastic
    Specifications
    Cure Specs
    Cure Temperature (°C) 120, 200, 200 Test Method
    Cure Time (min) 10, 240, 0.13 to 0.23 Test Method
    Viscosity (cPs) 520 (Pa.s) Test Method
    Work / Pot Time (min) 4,320 Test Method
    Mix Ratio 1:1 (by volume)
    Bond Strength
    Tear Strength (piw) 20 (kN/m), 10 (kN/m) Test Method
    Tensile Strength (psi) 9.0 (Mpa), 9.0 (Mpa) Test Method
    Conductivity
    Volume Resistivity (O) 4.8e15 (ohms/cm) Test Method
    Hardness
    Shore A Hardness 74, 77 Test Method
    Elongation (%) 400, 380 Test Method
    Other Properties
    Specific Gravity 1.160 Test Method
    Flash Point (°F) 212.0
    % Solids (%) 100
    Business Information
    Shelf Life Details When stored at or below 32°C (90°F) in original unopened containers, this product has a usable life of 15 months from the date of production.
    Shelf Life Type from the date of production
    Shelf Life (mon) 15
  • Best Practices for Dow Silastic 9280/75E

    *See Terms of Use Below

    1. Mixing

      The A & B components are supplied strained and de-aired to be used as lot matched kits.

      Mix Parts A & B in a 1:1 ratio. Meter Mix equipment which pumps, meters and mixes the two components without the incorporation of air is strongly recommended for production.

    2. Deairing/Degassing

      If air bubbles are entrapped during mixing the moisture must be thoroughly degassed under vacuum.

    3. Curing

      SILASTIC 9280/75E cures rapidly at elevated temperatures. A 2mm cross-section requires 8-14 seconds at 200°C (392°F). The cure time depends on the thickness and the cure temperature used. Cure can be inhibited by contact with certain materials such as amines, sulphur and tin complexes.

    4. Clean-Up

      The uncured silicone can readily be removed by most hydrocarbon solvents. Polar solvents, such as ketones and alcohols, are not suitable.

  • Comparable Materials for Dow Silastic 9280/75E

    *See Terms of Use Below

    Spec Engine® Results

Popular Articles

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Electrically Conductive Adhesives

Read Article

6 objects held together by adhesives you probably can't live without

Read Article

Testing the effectiveness of surface treatments

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for Dow Silastic 9280/75E

Gluespec Poll

What level of expertise do you have in specialty chemicals like adhesives, sealants, conformal coatings, etc.?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
120°C Press cure
200°C Post cure
200°C
Cure Time Test Methods
Cure Time Test Method
10 min Press cure
240 min Post cure
0.13 to 0.23 min
Viscosity Test Methods
Viscosity Test Method
520 (Pa.s) Y=10.0s-1, Viscosity measured on the Carrimed CSL Viscometer.
Work / Pot Time Test Methods
Work / Pot Time Temperature
4,320 min 25°C
Tensile Strength Test Methods
Tensile Strength Test Method
9.0 (Mpa) ASTM DIN 53504
9.0 (Mpa) ASTM DIN 53504
Tear Strength Test Methods
Tear Strength Test Method
20 (kN/m) ASTM D624B
10 (kN/m)
Volume Resistivity Test Methods
Volume Resistivity Test Method
4.8e15 (ohms/cm) ASTM D257
Elongation Test Methods
Elongation Test Method
400 % DIN 53504
380 % DIN 53504
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method
74 Hardness/Durometer Test Method
77 DIN 53505
Specific Gravity Test Methods
Specific Gravity Test Method
1.160 DIN 53479