Elantas (Altana) 1817 Datasheet Elantas (Altana) 1817

Information provided by Gluespec
  • Description for Elantas (Altana) 1817

    A liquid two-component polyurethane casting system formulated to produce 90 Shore A elastomers. It does not contain MbOCA or heavy metal catalysts.

    *See Terms of Use Below

    Brand Cytec
    Application Type Casting, Gaskets
    1 Part or 2 Part 2-Part
    Material Form Liquid
    Substrate Metal
    Industry Bushings
    Manufacturer Elantas (Altana)
    Chemistry polyurethane
    Cure Method Resin/Hardener
    Cure Temperature (°C) 25, 80
    Cure Time (min) 10,080 to 14,400, 960
    Viscosity (cPs) 3,500
    Color Light Amber
    Volume Resistivity (O) 7.3e15 (ohm-cm), 1.2e10 (ohm-cm)
  • Technical Data for Elantas (Altana) 1817

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 2-Part
    • Material Form
      • Liquid
    • Substrate
    • Industry
      • Industrial - Industrial wheels
      • Bushing - Bushings
      • Other - Cast-in-place linings for metal polishing and finishing equipment, Sound dampening pads, Metal forming pads, Flexible molds, Drop hammer faces, Washers, Diaphragms, Vibration dampening pads, Shock dampening pads
    • Chemistry
    • Application Method
      • Dispenser - automatic metering, mixing, dispensing equipment
    • Cure Method
      • 2-Part Cure - Resin/Hardener
    • Color
      • Red - Light Amber
    • Brand
      • Cytec
    Specifications
    Cure Specs
    Cure Temperature (°C) 25, 80
    Cure Time (min) 10,080 to 14,400, 960
    Viscosity (cPs) 3,500 Test Method
    Linear Shrinkage (%) 1.18 Test Method
    Work / Pot Time (min) 15 to 20 Test Method
    Mix Ratio 100:20 (by volume), 100:18 (by weight)
    Bond Strength
    Tear Strength (piw) 525 (pli), 135 (pli) Test Method
    Tensile Strength (psi) 3,500 Test Method
    Conductivity
    Dissipation Factor 0.02400, 0.34800, 0.02400, 0.04800, 0.05700, 0.02100 Test Method
    Dielectric Strength (V/mil) 534 (vpm) Test Method
    Dielectric Constant 5.38, 4.43, 5.18, 4.24, 4.32, 3.89 Test Method
    Volume Resistivity (O) 7.3e15 (ohm-cm), 1.2e10 (ohm-cm) Test Method
    Surface Resistivity (O) 2.0e16 (ohms), 4.2e11 (ohms) Test Method
    Hardness
    Shore A Hardness 90 Test Method
    Elongation (%) 600 Test Method
    Flexibility Flexible
    Modulus (psi) 1,250, 1,500, 1,750 Test Method
    Business Information
    Shelf Life Details CONATHAN® TU-8090 has a shelf life of 18 months from date of manufacture when stored in the original unopened containers at 70°- 85°F. Containers should be flushed with dry nitrogen or CONAP® Dri-Purge each time they are opened unless the contents are used within one day.
    Shelf Life Type From date of manufacture
    Shelf Life (mon) 18
  • Best Practices for Elantas (Altana) 1817

    *See Terms of Use Below

    1. Surface Preparation

      It is important that all dirt, rust, grease, and oil be removed from surfaces prior to applying the primer. Request Surface Preparation Guide, Bulletin AC-107, for recommendations.

    2. Mixing

      CONATHANE TU-8090 can be processed by batch mixing or by the use of automatic metering, mixing, and dispensing equipment. Specific recommendations can be made by the technical service department of Cytec Industries Inc. or by your regional sales manager. The following procedure is recommended for batch processing: Containers used for weighing or mixing should be metal, glass, or plastic. Mixing rods should also be metal, plastic, or glass. Avoid paper containers and wooden sticks.

      Use a separate container for mixing, with enough space to allow for expansion during degassing (usually two to three times the volume of material being mixed) if voidfree castings are desired. In many applications the degassing step may be eliminated.

      Weigh the correct proportions of the two components together, mix thoroughly, and degas at 28-29 inches of mercury vacuum to remove air entrapped during mixing.

      Pour mixed material into molds or fixtures in a manner to avoid trapping air bubbles or pockets, and cure as recommended. Porous molds should be properly sealed prior to using. Contact Cytec's customer service department, or your local regional sales manager, for assistance.

      If parts are to be demolded, a quality CONAP® mold release should be applied prior to pouring.

    3. Clean-Up

      Equipment may be cleaned with methylene chloride or acetone.

  • Comparable Materials for Elantas (Altana) 1817

    *See Terms of Use Below

    Spec Engine® Results

Popular Articles

Testing the effectiveness of surface treatments

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Characteristics of MMAs

Read Article

The effectiveness of adhesives in the wind power industry

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Top Catalog Pages for Elantas (Altana) 1817

Gluespec Poll

When you're researching or sourcing materials online, what device are you using?
Linear Shrinkage Test Methods
Linear Shrinkage Test Method Temp
1.18 % ASTM D2566 80°C
Viscosity Test Methods
Viscosity Temperature
3,500 cPs 25°C
Work / Pot Time Test Methods
Work / Pot Time Temperature
15 to 20 min 25°C
Tensile Strength Test Methods
Tensile Strength Test Method
3,500 psi ASTM D412
Tear Strength Test Methods
Tear Strength Test Method
525 (pli) ASTM D-624, Graves
135 (pli) ASTM D470, Split
Dielectric Constant Test Methods
Dielectric Constant Temperature Test Method
5.38 25°C Dielectric constant, 100 Hz
4.43 130°C Dielectric constant, 100 Hz
5.18 25°C Dielectric constant, 1 KHz
4.24 130°C Dielectric constant, 1 KHz
4.32 25°C Dielectric constant, 1 MHz
3.89 130°C Dielectric constant, 1 MHz
Dielectric Strength Test Methods
Dielectric Strength Temperature
534 (vpm) 25°C
Dissipation Factor Test Methods
Dissipation Factor Temperature Test Method
0.02400 25°C Dissipation Factor, 100 Hz
0.34800 130°C Dissipation Factor, 100 Hz
0.02400 25°C Dissipation Factor, 1 KHz
0.04800 130°C Dissipation Factor, 1 KHz
0.05700 25°C Dissipation Factor, 1 MHz
0.02100 130°C Dissipation Factor, 1 MHz
Volume Resistivity Test Methods
Volume Resistivity Temp (°C)
7.3e15 (ohm-cm) 25°C
1.2e10 (ohm-cm) 130°C
Surface Resistivity Test Methods
Surface Resistivity Temperature
2.0e16 (ohms) 25°C
4.2e11 (ohms) 130°C
Elongation Test Methods
Elongation Test Method
600 % ASTM D412
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method
90 ASTM D2240
Modulus Test Methods
Modulus Test Method
1,250 psi ASTM D412, 100% Modulus,
1,500 psi ASTM D412, 200% Modulus,
1,750 psi ASTM D412, 300% Modulus