Elantas (Altana) TU-801

Elantas (Altana) TU-801 Datasheet
  • Description for Elantas (Altana) TU-801

    A new two-component, liquid casting system - free from MbOCA, TDI, MDA, and Hg catalyst - that produces flexible elastomers of exceptional toughness, high elongation, high tensile and tear strength.

    *See Terms of Use Below

    Brand Cytec
    Application Type Casting, Gaskets
    1 Part or 2 Part 2 Part
    Material Form Liquid
    Industry Industrial wheels
    Manufacturer Elantas (Altana)
    Chemistry MbOCA Free
    Cure Method Resin/Hardener
    Cure Temperature (°C) 80, 20 to 25, 80, 25
    Cure Time (min) 120, 1,440, 960, 10,080 to 30,240
    Viscosity (cPs) Low, 3,500
    Color Light Amber, Clear
    Arc Resistance (sec) Arc Resistance
    Chemical Resistance Good chemical resistance
    Relative Solvent Resistance Chemical Resistance: Good solvent resistance
    Durability Exceptional toughness
    Key Specifications UL94 V-2 (1/8’’ thick)
  • Technical Data for Elantas (Altana) TU-801

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 1 Part or 2 Part - 2 Part
    • Material Form
      • Liquid
    • Industry
      • Industrial Wheels
      • Other - Vibration, shock and sound dampening pads, Metal forming pads, Flexible molds, Washers, Bushings, Diaphrams
    • Chemistry
      • Other - MbOCA Free
    • Application Method
      • Dispenser - automatic metering, mixing equipment, dispensing equipment
    • Cure Method
      • 2-Part Cure - Resin/Hardener
    • Color
      • Clear / Transparent - Clear
      • Red - Light Amber
    • Key Specifications
      • UL (Underwriters Laboratory), ULC (Underwriters Laboratories of Canada), NFPA (National Fire Protection Association) - UL94 V-2 (1/8’’ thick)
    • Brand
      • Cytec
    Specifications
    Cure Specs
    Cure Temperature (°C) 80, 20 to 25, 80, 25 Test Method
    Cure Time (min) 120, 1,440, 960, 10,080 to 30,240 Test Method
    Viscosity (cPs) Low, 3,500 Test Method
    Linear Shrinkage (%) 0.93, Undetectable Test Method
    Work / Pot Time (min) Adequate, 20 to 30 Test Method
    Mix Ratio Convienient (by volume), 100:53 (by volume), 100:51 (by weight)
    Bond Strength
    Tear Strength (piw) High, 360 (pli) Test Method
    Tensile Strength (psi) High, 3,500 Test Method
    Material Resistance
    Arc Resistance (sec) Arc Resistance
    Abrasion Resistance excellent abrasion resistance
    Chemical Resistance Good chemical resistance
    Relative Solvent Resistance Chemical Resistance: Good solvent resistance
    UV Resistance UV Resistance Test Method
    Conductivity
    Dissipation Factor 0.07400, 0.02700, 0.07800 Test Method
    Dielectric Strength (V/mil) 519 (vpm) Test Method
    Dielectric Constant 5.31, 5.13, 4.18 Test Method
    Volume Resistivity (O) 1.2e12 (ohm-cm) Test Method
    Surface Resistivity (O) 6.2e13 (ohms) Test Method
    Hardness
    Durability Exceptional toughness
    Shore A Hardness 80 Test Method
    Elongation (%) High, 700 Test Method
    Flexibility Flexible
    Modulus (psi) 500, 600, 800 Test Method
    Business Information
    Shelf Life Details CONATHANE TU-401 Part A and TU-801 Part B have a storage life of at least 18 months from date of shipment when stored in their original unopened containers at 20ºC-30ºC (68ºF-86ºF)., CONATHANE TU-401 Part A and TU-801 Part B have a storage life of at least 18 months from date of shipment when stored in their original unopened containers at 20ºC-30ºC (68ºF-86ºF).
    Shelf Life Temperature (°F) 68 to 86, 68 to 86
    Shelf Life Type From date of manufacture., From date of manufacture.
    Shelf Life (mon) 18 Part A, 18 Part B
  • Best Practices for Elantas (Altana) TU-801

    *See Terms of Use Below

    1. Surface Preparation

      When curing CONATHANE TU-801 at 80C(176°F) or above, the recommended primer is CONAP® AD-1147 or AD-1147-C.

      It is important that all dirt, grease, and oil be removed from surfaces prior to applying the primers.

    2. Application

      Pour mixed material into molds or fixtures in a manner to avoid trapping air bubbles or pockets, and cure as recommended. Porous molds should be properly sealed prior to using. Contact Cytec's customer service department or your local Regional Sales Manager for assistance.

      If parts are to be demolded, a quality CONAP® mold release should be applied prior to pouring.

    3. Mixing

      CONATHANE® TU-801 can be processed by batch mixing or by the use of automatic metering, mixing and dispensing equipment. Specific recommendations can be made by the customer service department of Cytec or by your local Regional Sales Manager. The following procedure is recommended for batch processing: Containers used for weighing or mixing should be metal, glass or plastic. Mixing rods should be plastic or glass also. Avoid paper containers and wooden sticks!

      Use a separate container for mixing with enough space (usually 2 to 3 times the volume of material being mixed) to allow for expansion during degassing. If void free castings are not necessary, the degassing step may be eliminated.

      Weigh the correct proportions of the two components together. MIX THOROUGHLY, and degas, if desired, at 28-29 inches of mercury to remove entrapped air caused by mixing.

    4. Clean-Up

      Equipment may be cleaned with Methyl Ethyl Ketone or other hydrocarbon solvents.

  • Comparable Materials for Elantas (Altana) TU-801

    *See Terms of Use Below

    Spec Engine® Results

Questions about this material?

Get personal assistance with your specific application needs.

Your Profile Edit
  1. 89198c31-2f03-4f46-8ff9-e5e572fb686b
  2. 89198c31-2f03-4f46-8ff9-e5e572fb686b

Popular Articles

Testing the effectiveness of surface treatments

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

Who do you read or follow for engineering news and entertainment?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
80°C Cytec
20 to 25°C Cytec
80°C
25°C
Cure Time Test Methods
Cure Time Test Method
120 min Cytec
1,440 min Cytec
960 min
10,080 to 30,240 min
Linear Shrinkage Test Methods
Linear Shrinkage Test Method Temp
0.93 % Cytec 80°C
Undetectable Cytec 25°C
Viscosity Test Methods
Viscosity Temperature
Low
3,500 cPs 25°C
Work / Pot Time Test Methods
Work / Pot Time Temperature
Adequate
20 to 30 min 25°C
Tensile Strength Test Methods
Tensile Strength Test Method
High
3,500 psi ASTM D412
Tear Strength Test Methods
Tear Strength Test Method
High
360 (pli) Graves, ASTM D624
UV Resistance Test Methods
UV Resistance Test Method
UV Resistance ASTM G-53
Dielectric Constant Test Methods
Dielectric Constant Temperature Test Method
5.31 25°C ASTM D150, 100 Hz
5.13 25°C ASTM D150, 1 KHz
4.18 25°C ASTM D150, 1 MHz
Dielectric Strength Test Methods
Dielectric Strength Test Method
519 (vpm) ASTM D149
Dissipation Factor Test Methods
Dissipation Factor Temperature Test Method
0.07400 25°C ASTM D150, 100 Hz
0.02700 25°C ASTM D150, 1 KHz
0.07800 25°C ASTM D150, 1 MHz
Volume Resistivity Test Methods
Volume Resistivity Test Method
1.2e12 (ohm-cm) ASTM D257
Surface Resistivity Test Methods
Surface Resistivity Test Method
6.2e13 (ohms) ASTM D257
Modulus Test Methods
Modulus Test Method
500 psi 100% Modulus, ASTM D412
600 psi 200% Modulus, ASTM D412
800 psi 300% Modulus, ASTM D412
Elongation Test Methods
Elongation Test Method
High
700 % ASTM D412
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method
80 ASTM D2240