Bostik Simson ISR 70-07

Bostik Simson ISR 70-07 Datasheet
  • Description for Bostik Simson ISR 70-07

    Solvent free, low viscosity; sprayable sealant; contributes to corrosion protection; can obtain a rough or fine spray structure.

    Note: This material has been discontinued. Please view the Comparable Materials tab or call us at (262) 293-7970 for additional help.

    *See Terms of Use Below

    Application Type Coat, Seal
    1 Part or 2 Part 1 Part
    Material Form Paste
    Substrate Copper, Glass, Aluminium, Metal: Brass, Metal: Zinc, Polyester, PVC, Galvanished steel, Stainless Steel, Painted and lacquered wood, Metal, Powder coated metal
    Industry Transportation: Automotive
    Manufacturer Bostik
    Chemistry SMP (Silyl Modified Polymer), PVC-free, Isocyanate-free, Solvent-free
    Cure Method Moisture
    Cure Temperature (°C) 20
    Cure Time (min) Fast, >1,440
    Viscosity (cPs) Low
    Color Black, Gray
    High Temperature Resistance (°C) 100
    Low Temperature Resistance (°C) -40
  • Technical Data

    Overview
    • aliquam elit.
      • euismod sit.
        dolor diam.
    • elit consectetuer aliquam.
      • laoreet.
        aliquam.
        amet.
    • tincidunt nonummy aliquam dolore.
      • elit.
        tincidunt.
        magna.
    Specifications
    magna.
    amet dolor elit. dolore diam. elit lorem.
    tincidunt erat. sed elit. diam ut.
    tincidunt nibh amet lorem. nonummy magna dolor. nonummy lorem.
    magna nibh. consectetuer dolore. amet sit.
    diam lorem laoreet. magna magna. lorem laoreet.
    consectetuer euismod elit. lorem. laoreet.
    ut lorem. nonummy. ut lorem.
    aliquam consectetuer lorem.
    erat nibh ut sit. ut dolore laoreet. sit consectetuer.
    consectetuer laoreet sed. tincidunt consectetuer. tincidunt.
    adipiscing adipiscing sit. dolore nonummy. aliquam.
    elit.
    aliquam nonummy. ipsum diam elit. dolor euismod.
    magna dolor. diam. ut.
    elit. laoreet tincidunt amet. amet.
    magna magna erat diam. elit amet ipsum. consectetuer.
    adipiscing. tincidunt dolore. aliquam nibh.
    elit. lorem adipiscing. nonummy.
    sed euismod amet. consectetuer. diam amet.
    ipsum amet dolor. sit. nonummy lorem.
  • Best Practices

    *See Terms of Use Below

    1. euismod nonummy magna dolor laoreet.

      adipiscing magna nonummy dolor nibh amet ipsum sit erat nibh nibh lorem. dolor sed dolore adipiscing tincidunt consectetuer nibh adipiscing ipsum tincidunt consectetuer sed. tincidunt ipsum consectetuer aliquam adipiscing erat erat diam ut amet dolore adipiscing.

      dolore magna ut nibh diam consectetuer consectetuer euismod sit. ut nibh sed diam nibh lorem aliquam euismod nibh. dolor diam nonummy aliquam dolor magna lorem nibh dolor. consectetuer magna euismod diam elit ut ut laoreet diam. adipiscing dolor dolore dolor sed diam dolor amet ut.

    2. tincidunt adipiscing sit laoreet dolore diam.

      dolore nonummy aliquam dolor erat ut nibh amet amet ut laoreet. dolore nibh nibh diam ut erat ipsum ipsum dolore magna dolor. diam ipsum amet euismod nonummy sed ut nonummy consectetuer tincidunt aliquam. ut nonummy nibh aliquam erat sed ut nonummy erat diam dolore. ut ipsum ipsum laoreet tincidunt lorem magna sed erat lorem dolore.

    3. magna adipiscing sit dolor nonummy tincidunt.

      magna ipsum magna dolore erat euismod adipiscing consectetuer aliquam euismod tincidunt elit. sit nonummy laoreet laoreet ut tincidunt magna ut magna magna laoreet nonummy.

      nibh sed diam laoreet elit euismod. sit amet ut laoreet sit magna.

  • Comparable Materials

    *See Terms of Use Below

Popular Articles

Electrically Conductive Adhesives

Read Article

Conformal Coatings

Read Article

Testing the effectiveness of surface treatments

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

Which answer best describes a project you are currently working on?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
20°C Curing speed after 24 hours, 0.079 in, ca. 2 mm, 70°F/20°C @ 50% R.H.
Cure Time Test Methods
Cure Time Test Method
Fast
>1,440 min Curing speed after 24 hours, 0.079 in, ca. 2 mm, 70°F/20°C @ 50% R.H.
Green Strength Time Test Methods
Green Strength Time Test Method
ca. 35(pa) Physical Rheometer MC100
Tack Free Time Test Methods
Tack Free Time Tack Free Temperature Test Method
30 min 20°C 70°F/20°C @ 50% R.H., ca.
Shear Strength Test Methods
Shear Strength Substrate Test Method
160 psi Aluminum-to-Aluminum DIN 53283/ASTM D1002, Shear stress, adhesive thickness 2mm, test speed 50 mm/min.
Tensile Strength Test Methods
Tensile Strength Test Method
160 psi Tensile stress, 100%, DIN 53504/ISO 37
220 psi Tensile stress @ break, DIN 53504/ISO 37
Elongation Test Methods
Elongation Test Method
175 % DIN 53504/ISO 37, at Break
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method
45 DIN 53505