Dow HV 1860/023

CONTACT REP

Description for Dow HV 1860/023

Suitable for bonding high temperature peroxide cured silicone rubbers; remains active over several hours after application.

*See Terms of Use Below

Application Type	Primer
1 Part or 2 Part	1-Part
Material Form	Liquid
Substrate	Silicone rubber
Manufacturer	Dow
Chemistry	Heptane, Siloxane
Cure Method	Air dry, Solvent
Cure Temperature (°C)	20 to 25
Cure Time (min)	15 to 90
Viscosity (cPs)	Low, 0.6 (mPa.s)

Best Practices for Dow HV 1860/023

Register for FREE to view more details

Why register?

View Technical Details
View Test Methods
View Key Specifications
View Similar Materials
Save your Project Searches

See what Gluespec offers

Sign up now Already registered? Sign in!

Email: *

Password: *

Confirm Password: *

Do you prefer to see data in °F or °C?

First Name: *

Last Name: *

Phone: *

Company Name: *

Address: *

Postal Code: *

Country: *

Job Function: *

Industry: *

Describe: *

I agree to the terms of use *

*: Required

Technical Data for Dow HV 1860/023

*See Terms of Use Below

Overview

Application Type
- Primer
1 Part or 2 Part
- 1-Part
Material Form
- Liquid
Substrate
- Silicone Rubber
Chemistry
- Solvent-Based - Heptane
- Other - Siloxane
Application Method
- Brush
- Spray
- Dip
Cure Method
- Room Temperature / Air Dry - Air dry
- Solvent

Specifications

Cure Specs

Cure Temperature (°C)	20 to 25
Cure Time (min)	15 to 90
Viscosity (cPs)	Low, 0.6 (mPa.s)	Test Method

Other Properties

Specific Gravity	0.720	Test Method
Flash Point (°F)	24.8	Test Method
% Solids (%)	7

Business Information

Shelf Life Details	When stored at or below 25°C (77°F) in the original unopened containers, this product has a usable life of 450 days from the date of production., This material should be stored in a warehouse suitable for flammable materials., Containers should be kept tightly sealed when not in use. The primer hydrolyzes upon contact with air moisture, and prolonged exposure will reduce or destroy its effectiveness., Once hydrolyzed, indicated by a milky appearance, the material cannot be reclaimed, and will contaminate any unreacted primer.
Shelf Life Type	from the date of production
Shelf Life (mon)	15

Best Practices for Dow HV 1860/023

*See Terms of Use Below
1. Surface Preparation
  
  Thoroughly clean and degrease the surface using a scouring pad, or a coarse lint-free cloth. Rinse all cleaning agents off the surface with acetone, MEK or isopropanol. Allow the surface to dry.
  
  Alternatively, aqueous degreasing with steam or hot water can be used to effectively prepare surfaces. Rinse with demineralised water and allow to dry thoroughly. Ensure no residues are left on the surface.
2. Application
  
  Apply a thin coating of DOW CORNING HV 1860/023 Primer by dipping, brushing or spraying. In most cases a thin primer film will give the best adhesion. Film thickness can be roughly estimated by appearance, the thicker the film the stronger the white tint. If cracks appear in the chalked film, the coating DOW CORNING HV 1860/023 can be diluted with solvent to achieve lighter coats by dipping or spraying. See typical properties for appropriate solvents. All solvents must be water-free.
3. Curing
  
  At normal temperature and humidity conditions (50% R.H. and room temperature) the primer should be allowed to air dry for 15 to 90 minutes. Low humidity will mean longer drying times. Primer which is allowed to overcure will result in poor adhesion, under normal conditions this should be no longer than 6 hours.
Comparable Materials for Dow HV 1860/023

*See Terms of Use Below

Spec Engine^® Results
- 3901(3M)
  A primer for film and liquid adhesives for improved metal and glass adhesion or improved resistance to environmental exposure with epoxy and urethane adhesives. Protects cleaned surfaces until bonding can be completed. Imparts improved corrosion protection to metal.
- Cho-Shield 1091 Primer(Parker Chomerics)
  An air-drying liquid coating for enhancing the adhesion of Cho-Shield 2000 series electrically conductive coating and Cho-Bond 2165 to chemically treated aluminum, and most composite surfaces.
- Chemlok 459M Primer(Parker Lord)
  Primer, designed for promoting adhesion to thermoplastic elastomers (TPE), thermoplastic polyolefins (TPO) and EPDM.
- Compare All
Closest Results from this Manufacturer
- Dowsil PR-1204 RTV Prime Coat(Dow)
  Enhances bonding/adhesion of RTV and heat cure silicones to many metals, ceramics, glass and masonry.
- Dowsil PR-4040 Prime Coat(Dow)
  Primer, used to increase design flexibility, reduce total costs or increase performance reliability of electronic systems.
- Silastic DY 39-123 Rubber(Dow)
  A primer specially designed for silicone rubber to adhere to substrates such as metals, glass fibers and synthetic fibers.
- Compare All