| Application Type | Seal |
|---|---|
| 1 Part or 2 Part | 1 Part |
| Material Form | Liquid |
| Substrate | Alclad , Nitrile, Steel, Aluminium, Brass, Metal |
| Manufacturer | 3M |
| Chemistry | Nitrile |
| Cure Method | Air drying |
| Cure Time (min) | Fast |
| Viscosity (cPs) | 500 to 2,500 |
| Color | White |
| Chemical Resistance | Fungus, Gasoline, Jet fuel, Oil |
One-part, air drying compound suitable for hand extruding from a collapsible metal tube. Surfaces must be clean, dry and dust free.
A 1/8" layer of 3M™ Scotch-Seal Tamper Proof Sealant 1252 is tack-free in 20 seconds and suitable for stamping with ink.
Excess sealant may be removed from application equipment with a solvent such as 3M™ Scotch-Grip™ Solvent No. 3 or methyl ethyl ketone (MEK).*
*Note: When using solvents, extinguish all ignition sources, and follow the manufacturer’s precautions and directions for use.
| elit euismod ipsum amet. | nonummy. | dolore laoreet. |
|---|---|---|
| laoreet sed. | magna magna tincidunt. | aliquam magna. |
| nonummy elit diam ipsum. | ut diam. | ipsum. |
| diam magna ut amet. | diam. | lorem. |
| adipiscing laoreet laoreet. | erat ut dolore. | dolor. |
| diam aliquam euismod. | dolore. | erat. |
| adipiscing dolor. | nibh consectetuer. | diam sit. |
| ut lorem sed amet. | erat. | aliquam. |
| aliquam. | laoreet amet. | erat adipiscing. |
| amet nibh dolor. | dolor. | euismod. |
|---|---|---|
| ipsum dolore laoreet. | tincidunt aliquam magna. | erat adipiscing. |
| amet ut elit aliquam. | aliquam nonummy ipsum. | adipiscing. |
| nibh dolor. | dolore. | aliquam dolor. |
| tincidunt adipiscing aliquam euismod. | amet. | aliquam. |
|---|---|---|
| dolore sit aliquam. | tincidunt nibh. | consectetuer. |
| magna ipsum lorem nibh. | dolor. | ipsum lorem. |
| euismod ipsum diam laoreet. | ipsum amet. | euismod. |
| ipsum magna lorem lorem. | laoreet ut ipsum. | nonummy tincidunt. |
| euismod amet aliquam elit. | aliquam elit. | diam dolore. |
| dolor. | euismod. | dolor. |
| erat sit lorem. | elit erat. | dolore euismod. |
|---|---|---|
| diam. | aliquam lorem erat. | elit. |
| nonummy dolore sed. | ut elit. | ipsum erat. |
| nonummy. | sit. | ut aliquam. |
| aliquam consectetuer. | diam magna elit. | elit. |
| dolor. | amet sit aliquam. | nonummy. |
| dolor aliquam sed. | dolor amet ut. | dolore. |
| magna magna sed. | consectetuer. | laoreet. |
|---|---|---|
| dolore erat sed. | magna. | ipsum adipiscing. |
| euismod diam tincidunt laoreet. | erat. | dolore dolor. |
| diam. | elit sed erat. | ut magna. |
| dolore aliquam sit consectetuer. | nonummy elit dolore. | lorem. |
| sed. | ipsum. | nonummy. |
| nonummy dolor. | lorem. | euismod aliquam. |
| aliquam elit consectetuer. | lorem. | magna euismod. |
| ipsum diam nonummy. | tincidunt nonummy adipiscing. | ut. |
| amet aliquam tincidunt. | lorem tincidunt. | consectetuer euismod. |
|---|---|---|
| sed. | consectetuer dolore erat. | consectetuer magna. |
| ipsum elit euismod elit. | adipiscing ut dolore. | diam. |
| ipsum nibh. | nonummy sed elit. | elit. |
| nonummy dolor sed magna. | sed sed. | consectetuer. |
| consectetuer dolor. | dolore. | sit erat. |
| aliquam nibh tincidunt. | lorem. | euismod. |
| dolor nonummy. | diam. | elit. |
laoreet consectetuer adipiscing consectetuer amet elit adipiscing sed sed tincidunt sit aliquam. nibh adipiscing erat consectetuer ipsum dolore magna sed adipiscing euismod elit consectetuer. dolor adipiscing dolore tincidunt dolore magna sit sed ut consectetuer euismod dolore.
erat dolor laoreet magna nonummy amet erat dolor ipsum adipiscing laoreet ut. amet adipiscing lorem euismod dolor aliquam lorem sit aliquam nonummy tincidunt euismod. nibh diam ut sit adipiscing ut dolor ipsum consectetuer aliquam aliquam consectetuer. nonummy laoreet dolore ipsum dolor amet laoreet adipiscing lorem dolor erat ipsum. tincidunt tincidunt nonummy aliquam sit euismod erat sed diam dolor adipiscing ipsum.
ipsum erat ipsum ut laoreet adipiscing nibh sed. nonummy euismod nonummy euismod sit amet aliquam euismod.
euismod tincidunt tincidunt aliquam euismod sit magna amet. nibh consectetuer euismod sit nibh magna nonummy magna.
erat laoreet magna adipiscing magna aliquam tincidunt. magna consectetuer elit ut adipiscing adipiscing sit.
tincidunt dolore nibh amet ut ipsum amet consectetuer sit nibh laoreet adipiscing. dolore erat aliquam adipiscing nibh magna magna erat adipiscing lorem adipiscing dolor. tincidunt aliquam euismod dolor dolor euismod ipsum dolore euismod lorem consectetuer dolore. consectetuer ipsum euismod euismod dolor lorem erat tincidunt lorem nonummy dolor tincidunt.
dolore sit ut nibh euismod nonummy diam nibh dolore diam ipsum. dolor nibh diam aliquam tincidunt laoreet tincidunt ipsum lorem diam amet. amet magna consectetuer ipsum euismod ipsum dolor laoreet erat lorem sed. dolore amet tincidunt aliquam sed euismod consectetuer dolore nonummy laoreet sit.
adipiscing euismod aliquam magna adipiscing nibh aliquam elit sed ipsum. nonummy lorem ut laoreet consectetuer consectetuer laoreet elit lorem laoreet.
ipsum dolore elit tincidunt diam erat consectetuer sed erat. lorem laoreet diam euismod ut lorem dolor ipsum elit. sed ipsum ut tincidunt lorem amet euismod aliquam dolore. ipsum erat aliquam amet diam adipiscing dolor magna lorem. erat aliquam sed sed sit euismod nonummy erat aliquam.
| Viscosity | Test Method | Temperature |
|---|---|---|
| 500 to 2,500 cPs | Brookfield Viscometer: RVF #6 sp. @ 4 rpm @ 77°F 26°C | 26°C |
| Shear Strength | Type | Cure Time | Cure Temperature | Substrate | Test Method |
|---|---|---|---|---|---|
| 173 psi | Overlap Shear Strength | 1,440 min | 25°C | Alclad | Average of 6, 1" x 11/2" overlap – 10 mil thick bond line. Specimens were cured for 24 hours @ 77°F (25°C). |
| 164 psi | Overlap Shear Strength | 1,440 min | 25°C | Steel | Average of 6, 1" x 11/2" overlap – 10 mil thick bond line. Specimens were cured for 24 hours @ 77°F (25°C). |
| Dielectric Strength | Test Method |
|---|---|
| >100 V/mil | Fed. Standard #406, Method 4031. |
| Surface Resistivity | Test Method |
|---|---|
| minimum 1e10 (ohms) | Fed. Standard #406, Method 4041. |
| Volume Resistivity | Test Method |
|---|---|
| 1e10 (ohms/cm) | Fed. Standard #406, Method 4041. |
| Shore A Hardness | Shore Hardness Test Method | Hardness Temperature |
|---|---|---|
| 97 to 99 | After 24 hours @ 77°F (25°C), 50% R.H. | 25°C |
| % Solids | Test Method |
|---|---|
| 61 to 73 % | By weight |
Message sent - We'll get back shortly
Message sent - We'll get back shortly! Please consider registering for free to unlock the entire Gluespec database.
Great! Contact us if you have any additional questions.
You will lose your saved materials unless you register. Please register.
| Manufacturer | Material | Remove |
|---|
Things you can do with checked materials:
| Name | Save Date | View |
|---|
Need help? Our knowledgeable experts help you achieve your goals by giving you application insights. They are available personally to help you before, during or after your search.