Bostik 1100 Fast Set Urethane Adhesive/Sealant

Bostik 1100 Fast Set Urethane Adhesive/Sealant Datasheet
BUY ONLINE

  • Description for Bostik 1100 Fast Set Urethane Adhesive/Sealant

    One part urethane sealant that cures by reaction with atmospheric moisture to form a tough, flexible seal.

    *See Terms of Use Below

    Application Type Sealing, Bonding, Beading
    1 Part or 2 Part 1 Part
    Material Form Paste
    Substrate FRP, Metal, Most plastics, Wood
    Industry Bus, Emergency vehicle, Truck trailer, Railcar, RV, Transportation, Truck trailer, Horse trailer
    Manufacturer Bostik
    Chemistry Polyurethane, Urethane
    Cure Method Atmospheric moisture
    Cure Temperature (°C) 25, 25
    Cure Time (min) 2,160 to 4,320, 20,160
    Viscosity (cPs) Non-sag, Tenacious
    Color White, Grey, Black
    Ozone Resistance Excellent ozone resistance
    Aging Resistance Good aging resistance
    High Temperature Resistance (°C) 82, Good Heat resistance
    Low Temperature Resistance (°C) -40
    Durability Tough
    Key Specifications ASTM (American Standard Test Method): ASTM C920 Standard Specifications, CAN/CGSB (Canadian General Standards Board): Canadian Standard CAN/CGSB-19.13, TT (U.S. Federal Specification): TT-S-00230C (COM-NBS)

  • Technical Data for Bostik 1100 Fast Set Urethane Adhesive/Sealant

    *See Terms of Use Below

    Overview
    • Application Type
    • 1 Part or 2 Part
      • 1 Part or 2 Part - 1 Part
    • Material Form
      • Paste
    • Substrate
    • Industry
      • Transportation
      • Bus
      • Trailer - Horse trailer, Truck trailer
      • Rail - Railcar
      • Recreational Vehicles - RV
      • Trucks - Truck trailer
      • Automotive - Emergency vehicle
      • Industrial - HVAC, General industry
      • Other - Container construction
    • Chemistry
    • Cure Method
      • Moisture - Atmospheric moisture
    • Color
      • Black
      • Gray - Grey
      • White
    • Key Specifications
      • ASTM (American Standard Test Method): C920 - ASTM C920 Standard Specifications
      • CAN/CGSB (Canadian General Standards Board): 19.13 - Canadian Standard CAN/CGSB-19.13
      • TT (U.S. Federal Specification): S-00230C - TT-S-00230C (COM-NBS)
    Specifications
    Cure Specs
    Cure Temperature (°C) 25, 25 Test Method
    Cure Time (min) 2,160 to 4,320, 20,160 Test Method
    Viscosity (cPs) Non-sag, Tenacious
    Set Time (min) Fast
    Tack Free Time (min) 90 Test Method
    Work / Pot Time (min) 70 Test Method
    Bond Strength
    Peel Strength (piw) >25 Test Method
    Tear Strength (piw) Tear Resistant
    Tensile Strength (psi) 240 Test Method
    Material Resistance
    Ozone Resistance Excellent ozone resistance
    Aging Resistance Good aging resistance
    Abrasion Resistance Abrasion Resistant
    UV Resistance Good
    High Temperature Resistance (°C) 82, Good Heat resistance Test Method
    Low Temperature Resistance (°C) -40 Test Method
    Hardness
    Durability Tough
    Shore A Hardness 40 to 45 Test Method
    Elongation (%) 850 Test Method
    Flexibility Flexible
    Modulus (psi) 65 Test Method
    Business Information
    Shelf Life Details When stored at or below 80°F (27°C), Bostik 1100FS polyurethane sealant has a shelf life of nine months from date of manufacture.
    Shelf Life Temperature (°F) <81
    Shelf Life Type From date of manufacture.
    Shelf Life (mon) 9
    Not Good For
    Don't Use With glazing, plastic materials with high plasticizer content or corrosion/crack sensitive plastics.

  • Best Practices for Bostik 1100 Fast Set Urethane Adhesive/Sealant

    *See Terms of Use Below

    1. Clean-Up

      Uncured Bostik 1100 Fast Set may be easily removed from hands and tools with Bostik® Hand & Tool Towels. Excess sealant should be drywiped from all surfaces and tools while still uncured. Cured sealant can be removed with a sharp blade. NOTE: Cured sealant is usually very difficult to remove without altering or damaging the surface to which the sealant was applied.

  • Comparable Materials for Bostik 1100 Fast Set Urethane Adhesive/Sealant

    *See Terms of Use Below

    Spec Engine® Results

    • Bostik
      920 Urethane(Bostik)

      Outstanding weather resistance; strong flexible bonds.

    • Schnee-Morehead (ITW)
      7100(Schnee-Morehead (ITW))

      A one component gun-grade, non-sag, moisture cure polyurethane sealant. This is high performance product is designed with outstanding UV resistance and long term durability with a proven record in tough climates around the world.

    • Bostik
      CC-900(Bostik)

      One-component, architectural grade sealant capable of dynamic joint movement; properties remain stable in severe weather and temperature changes.

    • Compare All
  Download Technical Data Sheet   Save This Material Saved Items

Questions about this material?

Bostik - 1100 Fast Set Urethane Adhesive/Sealant

Get personal assistance with your specific application needs.

Your Profile Edit
Submit

Popular Articles

What Are the Differences Between Adhesives and Sealants?

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Testing the effectiveness of surface treatments

Read Article

Anaerobic Adhesives

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

What level of expertise do you have in specialty chemicals like adhesives, sealants, conformal coatings, etc.?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
25°C Uncured
25°C after 14 days cure at 77°F and 50% RH
Cure Time Test Methods
Cure Time Test Method
2,160 to 4,320 min Uncured
20,160 min after 14 days cure at 77°F and 50% RH
Tack Free Time Test Methods
Tack Free Time Test Method
90 min Uncured
Work / Pot Time Test Methods
Work / Pot Time Test Method
70 min Tool/Work Life, uncured
Tensile Strength Test Methods
Tensile Strength Cure Time Cure Temperature Cure Humidity Test Method
240 psi 20,160 min 25°C 50 % Cured, after 14 days cure at 77°F and 50% RH
Peel Strength Test Methods
Peel Strength Cure Time Cure Temperature Cure Humidity Test Method
>25 piw 20,160 min 25°C 50 % Cured, after 14 days cure at 77°F and 50% RH
High Temperature Resistance Test Methods
High Temperature Resistance Test Method
82°C Cured
Good Heat resistance
Low Temperature Resistance Test Methods
Low Temperature Resistance Test Method
-40°C Cured
Elongation Test Methods
Elongation Test Method
850 % Cured, after 14 days cure at 77°F and 50% RH
Modulus Test Methods
Modulus Test Method
65 psi Cured, @ 100% Elongation, after 14 days cure at 77°F and 50% RH
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method Hardness Temperature
40 to 45 Cured, After 14 days cure at 77°F and 50% RH 25°C
;