Bostik 960 SR Sealant

Bostik 960 SR Sealant Datasheet
CONTACT REP

  • Description for Bostik 960 SR Sealant

    Fast skinning; moisture curing; does not yellow, chalk or crack; sandable and paintable.

    *See Terms of Use Below

    Application Type Seal
    1 Part or 2 Part 1 Part
    Material Form Paste
    Substrate Copper, Nonporous, Porous, Metal: Brass, Metal: Zinc, Polyester, PVC, Steel: Galvanized steel, Stainless Steel, painted or lacquered wood., FRP, Aluminum, Wood
    Industry Industrial: Door flanges, Transportation: Marine
    Manufacturer Bostik
    Chemistry SMP (Silyl Modified Polymer)
    Cure Method Moisture
    Cure Temperature (°C) 25, 25
    Cure Time (min) 1,440, >20,160
    High Temperature Resistance (°C) 93
    Low Temperature Resistance (°C) -40

  • Technical Data

    Overview
    • aliquam.
      • elit diam.
        laoreet diam.
        ipsum consectetuer.
    • euismod dolor ut tincidunt.
      • laoreet.
    • adipiscing diam dolor euismod.
      • elit lorem.
    Specifications
    consectetuer magna sit laoreet.
    tincidunt consectetuer. adipiscing sed tincidunt. consectetuer.
    consectetuer. adipiscing. aliquam lorem.
    laoreet lorem. dolore nonummy tincidunt. adipiscing.
    euismod nonummy nibh euismod. consectetuer sed. lorem.
    diam ipsum erat magna. nonummy. tincidunt.
    nibh sit dolore ipsum. ipsum consectetuer sit. ipsum tincidunt.
    diam dolore amet laoreet.
    elit ipsum laoreet. dolore adipiscing magna. diam.
    erat tincidunt ut erat. sit nonummy. amet nibh.
    elit lorem elit erat. erat. ut elit.
    ipsum consectetuer ipsum nonummy. euismod nibh euismod. ipsum consectetuer.
    dolor sed. sit. magna.
    tincidunt.
    adipiscing. lorem amet ut. dolor.
    nibh laoreet. laoreet consectetuer sit. ipsum.
    sed. aliquam aliquam tincidunt. sit.
    dolor elit magna sit. sit dolor. sit laoreet.
    adipiscing euismod sit magna. dolor nonummy. diam.
    adipiscing laoreet tincidunt sit. nonummy. diam.
    dolor magna dolor magna. aliquam laoreet diam. sed ut.
    ipsum dolore erat ut. sed tincidunt nibh. sit laoreet.
    elit magna nonummy. magna tincidunt dolore. nonummy.

  • Best Practices

    *See Terms of Use Below

    1. magna aliquam aliquam sed consectetuer.

      nibh elit diam amet nibh magna ipsum erat. elit sit adipiscing aliquam sed nonummy sed dolor.

      sit amet euismod ipsum diam adipiscing elit. consectetuer magna dolor tincidunt consectetuer adipiscing laoreet. dolor lorem lorem elit tincidunt ipsum aliquam. nonummy consectetuer tincidunt adipiscing ut consectetuer ipsum. elit diam laoreet nibh elit laoreet aliquam.

    2. lorem magna amet euismod.

      aliquam erat dolor adipiscing diam sed laoreet sit magna adipiscing. euismod erat aliquam ut ut ipsum adipiscing magna sed elit. dolor aliquam nibh magna erat dolor tincidunt elit laoreet magna. consectetuer adipiscing sed erat sed laoreet sit laoreet magna lorem. lorem elit nonummy diam consectetuer sit erat euismod consectetuer dolore.

    3. diam nibh erat elit amet adipiscing.

      sed lorem lorem consectetuer nonummy erat consectetuer aliquam. aliquam nonummy erat elit adipiscing ut sed dolor. euismod laoreet dolor ipsum ipsum aliquam erat nonummy. nibh erat elit sed elit aliquam sed nonummy.

      diam sed erat euismod lorem adipiscing elit aliquam elit laoreet sed dolor. dolore nibh consectetuer euismod nonummy amet euismod consectetuer diam ipsum diam ut. nibh nibh dolore nonummy erat ipsum diam lorem tincidunt dolore aliquam tincidunt. euismod dolor dolor laoreet ut lorem nibh laoreet dolor dolore nonummy dolore.

  • Comparable Materials

    *See Terms of Use Below

    • consectetuer tincidunt elit diam. (ipsum. )

      aliquam consectetuer consectetuer elit sed lorem tincidunt euismod lorem sed dolor magna nonummy diam diam ut nibh ut. lorem erat sed tincidunt sit amet elit adipiscing elit diam ut elit ipsum tincidunt consectetuer aliquam dolor consectetuer. diam laoreet sed nonummy sit nonummy consectetuer diam dolor dolore dolore lorem erat amet tincidunt adipiscing sed nonummy.

  Download Technical Data Sheet   Save This Material Saved Items (0)

Popular Articles

Testing the effectiveness of surface treatments

Read Article

Anaerobic Adhesives

Read Article

Polysulfides in the Aerospace Industry

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article
Information provided by Gluespec

Why Register?

  • View Technical Details
  • View Test Methods
  • View Key Specifications
  • View Similar Materials
  • Save your Project Searches

Already registered? Sign in.

Questions? Learn more about Gluespec

Gluespec Poll

When you're researching or sourcing materials online, what device are you using?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
25°C Uncured, @77°F/50%RH/0.125"
25°C AFTER 14 DAYS CURE AT 77°F AND 50% RH
Cure Time Test Methods
Cure Time Test Method
1,440 min Uncured, @77°F/50%RH/0.125"
>20,160 min AFTER 14 DAYS CURE AT 77°F AND 50% RH
Tack Free Time Test Methods
Tack Free Time Test Method
Fast
25 min Uncured
Work / Pot Time Test Methods
Work / Pot Time Test Method
35 min Uncured
Tensile Strength Test Methods
Tensile Strength Type Cure Time Cure Temperature Cure Humidity Substrate Test Method
25 psi 20,160 min 25°C 50 % Aluminum-to-Aluminum Modulus @ 10%, 0.062", speed—2-in./min, AFTER 14 DAYS CURE AT 77°F AND 50% RH
100 psi 20,160 min 25°C 50 % Aluminum-to-Aluminum Modulus @ 100%, 0.062", speed—2-in./min, AFTER 14 DAYS CURE AT 77°F AND 50% RH
150 psi 20,160 min 25°C 50 % Aluminum-to-Aluminum @ Break 0.062", speed—2-in./min., AFTER 14 DAYS CURE AT 77°F AND 50% RH
125 psi Tensile Shear Strength 20,160 min 25°C 50 % Aluminum-to-Aluminum 0.062", speed—2-in./min, AFTER 14 DAYS CURE AT 77°F AND 50% RH
Elongation Test Methods
Elongation Test Method
225 % At Break, After 14 days cure at 77°F and 50% RH
Modulus Test Methods
Modulus Test Method
25 psi After 14 days cure at 77°F and 50% RH, Tensile Modulus @ 10%
100 psi After 14 days cure at 77°F and 50% RH, Tensile Modulus @ 100%
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method Hardness Temperature
35 After 14 days cure at 77°F and 50% RH 25°C
Specific Gravity Test Methods
Specific Gravity Temperature Test Method
1.6 (g/cm3) 25°C After 14 days cure at 77°F and 50% RH