Bostik Chem-Calk FCB Textured Datasheet Bostik Chem-Calk FCB Textured

CONTACT REP
Information provided by Gluespec

  • Description for Bostik Chem-Calk FCB Textured

    One-component; superior adhesion to fiber cement boards; outstanding elasticity; good adhesion to most building materials.

    *See Terms of Use Below

    Application Type Seal
    1 Part or 2 Part 1 Part
    Material Form Paste
    Substrate Metals, Vinyls, Hardiplank, Wood, Concrete
    Manufacturer Bostik
    Chemistry Urethane
    Cure Method Moisture
    Cure Temperature (°C) 25, 25
    Cure Time (min) 2,880 to 5,760, 20,160
    Viscosity (cPs) Sag, Slump
    Color Tan, Stone, White
    Ozone Resistance Good Ozone resistance
    High Temperature Resistance (°C) 66
    Low Temperature Resistance (°C) -40
    Key Specifications ASTM (American Standard Test Method): ASTM C920; Elastomeric Joint Sealant as Type S, Grade NS, Class 25, Use NT, A and M, CAN/CGSB (Canadian General Standards Board): Canadian Specification CAN/CGSB 19.13, TT (U.S. Federal Specification): TT-S00230C
  Download Technical Data Sheet   Save This Material   Compare Saved Items

Popular Articles

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

What are the Types of Adhesive Sealants? An In-Depth Q&A

Read Article

Q&A Tutorial on the Adhesive Sealant Selection Process

Read Article

Testing the effectiveness of surface treatments

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Gluespec Poll

Which answer best describes a project you are currently working on?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
25°C Varies w/ Relative
25°C After 14 days cure at 77°F & 50% RH
Cure Time Test Methods
Cure Time Test Method
2,880 to 5,760 min Varies w/ Relative
20,160 min After 14 days cure at 77°F & 50% RH
Tack Free Time Test Methods
Tack Free Time Test Method
240 min ASTM C 679
Work / Pot Time Test Methods
Work / Pot Time Test Method
60 min Bostik Test Method
Tensile Strength Test Methods
Tensile Strength Cure Time Cure Temperature Cure Humidity Test Method
143 psi 20,160 min 25°C 50 % ASTM D 412, After 14 days cure at 77°F & 50% RH
Peel Strength Test Methods
Peel Strength Cure Time Cure Temperature Test Method
>25 piw 20,160 min 25°C ASTM C 794, After 14 days cure at 77°F & 50% RH
UV Resistance Test Methods
UV Resistance Test Method
Good ASTM C 793
Elongation Test Methods
Elongation Test Method
564 % ASTM D 412, at Break, After 14 days cure at 77°F & 50% RH
Modulus Test Methods
Modulus Test Method
79 psi @ 100% Elongation ASTM D 412, After 14 days cure at 77°F & 50% RH
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method Hardness Temperature
38 ASTM D 2240, After 14 days cure at 77°F & 50% RH 25°C