Description for Bostik Simson ISR 70-01
Multi-purpose permanent elastic sealant; good aging properties; withstands strong movement.Application Type Seal 1 Part or 2 Part 1-Part Material Form Paste Substrate Copper, Glass, Aluminium, Polyester, PVC, Galvanised steel, Painted and lacquered wood, Stainless Steel, Brass, Zinc, Powder coated metal Industry Caravan, Train, Bus, Truck Manufacturer Bostik Chemistry SMP (Silyl Modified Polymer), PVC-free, Isocyanate-free, Solvent-free Cure Method Moisture Application Temperature (°F) 41 to 95 Cure Temperature (°C) 20 Cure Time (min) Fast, >1,440 Color Black, Grey, White High Temperature Resistance (°C) 100 Low Temperature Resistance (°C) -40 -
Technical Data for Bostik Simson ISR 70-01
Overview
-
Application Type
- Sealant - Seal
-
1 Part or 2 Part
- 1-Part
-
Material Form
- Paste
-
Substrate
- Glass
- Metal - Aluminium, Powder coated metal
- Copper
- Steel - Galvanised steel
- Brass
- Zinc
- Polyvinyl chloride (PVC) - PVC
- Wood - Painted and lacquered wood
- Polyester
- Stainless Steel
-
Industry
- Rail - Train
- Bus
- Trucks - Truck
- Automotive - Caravan
- Industrial - Air conditioning equipment, Sound reducing applications, Vibration reducing applications
- Construction
- Packaging - Aluminium containers
-
Chemistry
- Solvent-Free - PVC-free, Isocyanate-free
- Silyl Modified Polymer (SMP) / MS Polymer - SMP (Silyl Modified Polymer)
-
Application Method
- Dispenser - Air-pressure gun
- Brush - Hand
-
Cure Method
- Moisture / Condensation Cure - Moisture
-
Color
- Black
- Gray - Grey
- White
Specifications
Cure Specs
Application Temperature (°F) 41 to 95 Cure Temperature (°C) 20 Test Method Cure Time (min) Fast, >1,440 Test Method Tack Free Time (min) 30 Test Method Bond Strength
Shear Strength (psi) 260 Test Method Green Strength (psi) ca.300(pa) Test Method Tensile Strength (psi) 130, 245 Test Method Material Resistance
UV Resistance Excellent, Very Good High Temperature Resistance (°C) 100 Low Temperature Resistance (°C) -40 Moisture/Humidity Resistance Moisture/humidity resistance Hardness
Shore A Hardness 26 Test Method Elongation (%) 300 Test Method Flexibility Permanently elastic Other Properties
Specific Gravity ca. 1.4 (g/ml) Business Information
Shelf Life Details ISR 70-01 can be stored for 12 months in a closed (unopened) container in a dry place at temp.between +5°C to +30°C (cartridges 18 months) Shelf Life Temperature (°F) 41 to 86 Shelf Life (mon) 12 -
-
Best Practices for Bostik Simson ISR 70-01
-
Surface Preparation
In general ISR 70-01 adheres well without primer on clean, dry, dust- and grease free substrates of aluminum, stainless steel, galvanised steel, zinc, copper, brass powder coated metal, most lacquered metal surfaces, glass, PVC, polyester (GRP), painted and lacquered wood, etc.
Primer M is a so called 'wash primer' and degreases and prepares the surface of the substrate in one step. On plain, untreated wooden surfaces and other porous substrates Simson Primer P is recommended. for more details concerning Primer M and Primer P consult the specific technical information data sheet.
-
Application
ISR 70-01 can easily be extruded with a hand- or air pressure gun at temperatures between +5C and 35C.
-
Clean-Up
Cleaning tools or removing uncured residue of Simson ISR 70-01 can be done with a clean, colorless cloth, wetted with Isopropyl alcohol. It is recommended to make a trial first to check possible attack of the substrate by Isopropyl alcohol.
-
-
Comparable Materials for Bostik Simson ISR 70-01
Spec Engine® Results
Popular Articles
Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation
Read ArticleAnaerobic Adhesives
Read ArticlePolysulfides in the Aerospace Industry
Read ArticleTesting the effectiveness of surface treatments
Read ArticleSponsored Articles
Unique Advantages of Contact Adhesives
Read ArticleUsing LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials
Read ArticleSylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:
Read ArticleCase Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive
Read ArticleFeatured Ads

Cure Temperature Test Methods
Cure Temperature | Cure Time Test Method |
---|---|
20°C | Cure rate after 24 hours, 0.125 in., ca. 3 mm, 70°F/20°C @ 50% R.H. |
Cure Time Test Methods
Cure Time | Test Method |
---|---|
Fast | |
>1,440 min | Cure rate after 24 hours, 0.125 in., ca. 3 mm, 70°F/20°C @ 50% R.H. |
Tack Free Time Test Methods
Tack Free Time | Tack Free Temperature | Test Method |
---|---|---|
30 min | 20°C | 70°F/20°C @ 50% R.H., ca. |
Green Strength Test Methods
Green Strength | Test Method |
---|---|
ca.300(pa) | Physica Rheometer MC100 |
Tensile Strength Test Methods
Tensile Strength | Test Method |
---|---|
130 psi | Tensile stress 100%) DIN 53504/ISO 37 |
245 psi | Tensile stress At break DIN 53504/ISO 37 |
Shear Strength Test Methods
Shear Strength | Substrate | Test Method |
---|---|---|
260 psi | Aluminum-to-Aluminum | DIN 53283/ASTM D1002, adhesive thickness 2mm, test speed 50 mm/min. |
Elongation Test Methods
Elongation | Test Method |
---|---|
300 % | DIN 53504/ISO 37, at Break, ca. |
Shore A Hardness Test Methods
Shore A Hardness | Shore Hardness Test Method |
---|---|
26 | DIN 53505, ca. |