3M Scotch-Weld Pipe Sealant Anaerobic Adhesive PS67
Brand Scotch-weld Application Type Adhesive, Pipe Sealant 1 Part or 2 Part 1-Part Material Form Paste Substrate Pure aluminum, Copper, Metal, Stainless Steel, Nickel, Iron, Bronze, Brass, Manganese, Monel, Kovar, Silver, Cadmium, Zinc, Magnesium, Chemical black oxide, Gold, Galvanized steel, Magnetite Steel, Plated parts, Anodized Aluminum, Commercial aluminum Industry Air compressors, Hydraulic pipes and fittings, Pneumatic pipes and fittings, Hydraulic systems, Pneumatic systems Manufacturer 3M Chemistry Dimethacrylate, Anaerobic Cure Method Anaerobic Cure Time (min) Fast, 1,440 Viscosity (cPs) 150,000 to 400,000 Color Off-White Torque (psi) Low to medium, 30 (in.lb), 40 (in.lb) Pressure Resistance Withstand Pressure High Temperature Resistance (°C) 204, High temperature Low Temperature Resistance (°C) -54
Technical Data for 3M Scotch-Weld Pipe Sealant Anaerobic Adhesive PS67
1 Part or 2 Part
- Electronics - Air compressors
- Hydraulic - Hydraulic pipes and fittings, Hydraulic systems
- Pneumatic - Pneumatic systems, Pneumatic pipes and fittings
- Other - Pressure vessels
- Acrylic - Dimethacrylate
- Other - Anaerobic
Cure Time (min) Fast, 1,440 Test Method Viscosity (cPs) 150,000 to 400,000 Test Method Fixture or Handling Strength Time (min) 25 Test Method
Torque (psi) Low to medium, 30 (in.lb), 40 (in.lb) Pressure Resistance Withstand Pressure
High Temperature Resistance (°C) 204, High temperature Low Temperature Resistance (°C) -54
Shelf Life Details Storage: Store product in cool, dry area out of direct sunlight., 3MTM Scotch-WeldTM Pipe Sealant Anaerobic Adhesives have a shelf life of 12 months when stored at 60o to 80oF (16o to 27o C) in the original unopened container. Shelf Life Temperature (°F) 60 to 80 Shelf Life (mon) 12
Not Good For
Don't Use For Piping systems that contain pure oxygen or oxygen-rich environment, chlorine, or strong oxidizing substances. Don't Use With Most plastics due to potential cracking of plastic parts.
Best Practices for 3M Scotch-Weld Pipe Sealant Anaerobic Adhesive PS67
Ensure parts are clean, dry and free from oil, grease and dirt. For best results, clean and dry parts with solvent or a 3M™ Scotch-Weld™ Anaerobic Activator. (Activator can also be used on inactive surfaces or to accelerate the cure on active surfaces.)
Note: Use of a 3M™ Scotch-Weld™ Activator with 3M™ Scotch-Weld™ Pipe Sealant Anaerobic Adhesives may reduce bond strength depending on substrates and gap. Testing is recommended to evaluate the effect.
If not sure of surface type, always use activator.
Apply sealant onto the second and third threads (not the first thread) of the male fitting so as to avoid introducing uncured sealant into the system. (However, should uncured sealant get into the piping system, it will not cure or cause blockage and can be flushed out.)
Avoid touching the metal surfaces with the bottle tip since the metal ions may react with the adhesive upon contact and eventually may clog the bottle tip.
Spread adhesive evenly around the male fitting.
Assemble parts and tighten as required.
Allow assemblies to set for sufficient time so that handling strength or full cure will occur before further processing or testing.
Comparable Materials for 3M Scotch-Weld Pipe Sealant Anaerobic Adhesive PS67
Spec Engine® Results
Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of MaterialsRead Article
Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:Read Article
Cure Time Test Methods
|Cure Time||Test Method|
|1,440 min||Full Cure|
Fixture or Handling Strength Time Test Methods
|Fixture or Handling Strength Time||Fixture-Handling Strength Test Method|
|25 min||The following technical information and data should be considered representative or typical only and should not be used for specification purpose|
Viscosity Test Methods
|150,000 to 400,000 cPs||Brookfield Viscometer spindle T-E at 2.5 rpm, Uncured, The following technical information and data should be considered representative or typical only and should not be used for specification purpose|