• Description for Loxeal 59-40

    Loxeal 59-40 is a 1-Part Neutral Free of isocyanates Liquid used to Adhere Non metal materials, Glaze and Glass structures and surfaces

    *See Terms of Use Below

    Application Type Bond, Sealing
    1 Part or 2 Part 1-Part
    Material Form Liquid
    Substrate Glass structures and surfaces, Metal substrates, Glazed metal panels, PVC, Steel, Machined wood, Polystyrene foam, Anodised aluminium, Epoxy, Polystyrene foam
    Manufacturer Loxeal
    Chemistry Free of isocyanates, MS polymers
    Cure Method Neutral, Moisture, Room Temperature
    Application Temperature (°F) 41 to 104
    Cure Temperature (°C) 23
    Odorless Odor Details: Odourless
    Cure Time (min) >1,440
    Color Black, Grey
    High Temperature Resistance (°C) 90
    Low Temperature Resistance (°C) -40
    Durability Tough
  • Technical Data for Loxeal 59-40

    • Application Type
    • 1 Part or 2 Part
      • 1-Part
    • Material Form
      • Liquid
    • Substrate
      • Foam - Polystyrene foam
      • Glass - Glass structures and surfaces
      • Metal - Metal substrates, Glazed metal panels
      • Steel
      • Polyvinyl chloride (PVC) - PVC
      • Polystyrene (PS) - Polystyrene foam
      • Epoxy
      • Wood - Machined wood
      • Anodized Aluminum - Anodised aluminium
      • Other - Non metal materials, Glaze
    • Chemistry
      • Other - Free of isocyanates
      • Silyl Modified Polymer (SMP) / MS Polymer - MS polymers
    • Cure Method
      • Room Temperature / Air Dry - Room Temperature
      • Moisture / Condensation Cure - Moisture
      • Other - Neutral
    • Color
      • Black
      • Gray - Grey
    Cure Specs
    Application Temperature (°F) 41 to 104
    Cure Temperature (°C) 23 Test Method
    Cure Time (min) >1,440 Test Method
    Bond Strength
    Shear Strength (psi) 1.2 - 1.8 (MPa) Test Method
    Material Resistance
    High Temperature Resistance (°C) 90 Test Method
    Low Temperature Resistance (°C) -40 Test Method
    Durability Tough
    Shore A Hardness 40 to 60 Test Method
    Elongation (%) 150 to 350 Test Method
    Modulus (psi) 1.7 (MPa) Test Method
    Business Information
    Shelf Life Details 1 year at +5°C/+25°C in original unopened packaging
    Shelf Life Temperature (°F) 41 to 77
    Shelf Life (mon) 12
    Not Good For
    Don't Use For Expansion joints, For underwater application, Can damage coating
    Don't Use With Bituminous surfaces applications, PTFE, PP, PE, Bituminous surfaces applications, Can damage some plastics, Can damage some elastomers, Some thermoplastics
  • Best Practices for Loxeal 59-40

    *See Terms of Use Below

    1. Surface Preparation

      Clean and degrease parts before bonding with Loxeal Cleaner 10.

    2. Application

      Apply product to fill completely the gap, assemble parts and hold on for curing time.

      For application on non metal materials, contact Loxeal Technical Service.

    3. Removal

      For disassembly, use normal tools and eventually heat pieces at +150/+250°C, remove any residue of cured product mechanically and clean parts with Acetone.

  • Comparable Materials for Loxeal 59-40

    *See Terms of Use Below

    Spec Engine® Results

    Closest Results from this Manufacturer

Popular Articles

Anaerobic Adhesives

Read Article

What Are the Differences Between Adhesives and Sealants?

Read Article

Testing the effectiveness of surface treatments

Read Article

Infographic: ENSURING A STRONG BOND - 6 Basic Methods of Surface Preparation

Read Article

Sponsored Articles

Unique Advantages of Contact Adhesives

Read Article

Using LOCTITE® 454™ is a Valid Option for Engineers Working with a Wide Variety of Materials

Read Article

Sylgard 184 by DOW is the Top Choice for a Transparent, Silicone Encapsulant. Read Why:

Read Article

Case Study: Creating reliable, corrosion-free bonds with LORD® 406 acrylic adhesive

Read Article

Featured Ads

Gluespec Poll

Which answer best describes a project you are currently working on?
Cure Temperature Test Methods
Cure Temperature Cure Time Test Method
23°C 55%RF, 2 mm
Cure Time Test Methods
Cure Time Test Method
>1,440 min 55%RF, 2 mm
Shear Strength Test Methods
Shear Strength Test Method
1.2 - 1.8 (MPa) DIN 53504, On 2 mm
High Temperature Resistance Test Methods
High Temperature Resistance Test Method
90°C On 2 mm
Low Temperature Resistance Test Methods
Low Temperature Resistance Test Method
-40°C On 2 mm
Elongation Test Methods
Elongation Test Method
150 to 350 % At break, DIN 53504, On 2 mm
Modulus Test Methods
Modulus Test Method
1.7 (MPa) 100% (DIN 53504), On 2 mm
Shore A Hardness Test Methods
Shore A Hardness Shore Hardness Test Method
40 to 60 DIN 53505, 2 mm